WO2011008955A1 - Polymerization process for olefin-based polymers - Google Patents
Polymerization process for olefin-based polymers Download PDFInfo
- Publication number
- WO2011008955A1 WO2011008955A1 PCT/US2010/042139 US2010042139W WO2011008955A1 WO 2011008955 A1 WO2011008955 A1 WO 2011008955A1 US 2010042139 W US2010042139 W US 2010042139W WO 2011008955 A1 WO2011008955 A1 WO 2011008955A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymer
- solvent
- liquid
- reactor
- polymerization
- Prior art date
Abstract
Description
Claims