WO2011001240A1 - Graphene device and method of fabricating a graphene device - Google Patents

Graphene device and method of fabricating a graphene device Download PDF

Info

Publication number
WO2011001240A1
WO2011001240A1 PCT/IB2010/001453 IB2010001453W WO2011001240A1 WO 2011001240 A1 WO2011001240 A1 WO 2011001240A1 IB 2010001453 W IB2010001453 W IB 2010001453W WO 2011001240 A1 WO2011001240 A1 WO 2011001240A1
Authority
WO
WIPO (PCT)
Prior art keywords
graphene
electrode
porous
multiplicity
layer
Prior art date
Application number
PCT/IB2010/001453
Other languages
French (fr)
Inventor
Asta Maria Karkkaainen
Samiul Haque
Alan Colli
Pirjo Marjaana Pasanen
Leo Mikko Johannes Karkkainen
Mikko Aleksi Uusitalo
Reijo Kalvero Lehtiniemi
Original Assignee
Nokia Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nokia Corporation filed Critical Nokia Corporation
Priority to CA2766085A priority Critical patent/CA2766085C/en
Priority to CN201080029846.8A priority patent/CN102471069B/en
Priority to RU2012101496/02A priority patent/RU2511127C2/en
Priority to EP10793685.8A priority patent/EP2448863B1/en
Publication of WO2011001240A1 publication Critical patent/WO2011001240A1/en

Abstract

In accordance with an example embodiment of the present invention, a device comprising one or more porous graphene layers, the or each graphene porous layer comprising a multiplicity of pores. The device may form at least part of a flexible and/or stretchable, and or transparent electronic device.

Description

GRAPHENE DEVICE AND METHOD OF FABRICATING A GRAPHENE DEVICE
TECHNICAL FIELD
The present application relates generally to a device comprising graphene, and to a method for fabricating a device comprising graphene.
BACKGROUND
Graphene is a one-atom-thick planar sheet of sp2-bonded carbon atoms that are densely packed in a honeycomb crystal lattice. It can be viewed as an atomic-scale chicken wire made of carbon atoms and their bonds. Graphene exhibits new types of fundamental physical properties not found in other materials. From a device point of view the most interesting are the high charge carrier mobility with ballistic transport, high current density, high thermal conductivity, and the possibility to control the electrical properties. In 2004, single graphene sheets, truly two-dimensional atomic thick carbon crystals, were verifiably isolated by mechanical exfoliation of graphite bulk. It has recently been discovered that graphene sheets may be fabricated. These graphene sheets are good conductors, for example about 20 times that of silicon MOSFETs.
Nanowire networks made for example of carbon nanotubes, or silicon nanowires have been studied for a number of years. However, these networks have rather low conductivity, due to high resistance wire-to-wire connections within the network.
SUMMARY
Various aspects of examples of the invention are set out in the claims.
According to a first aspect of the present invention, a device comprising a porous graphene layer comprising a multiplicity of pores.
The device may comprise a porous graphene layer having a porosity between 1% and 99%. The porous graphene layer may comprise a nanoribbon having a width between 0.1 nm and 20nm. The porous graphene layer may have a porosity such that, and configured such that the porous graphene layer is a semiconductor. The device may comprise a substrate, wherein the porous graphene layer is located on the substrate. The substrate may be configured such that it is flexible or stretchable. The device may comprise a substrate, and the porous graphene layer may cover an area on the substrate between 1 μm and 10cm . The porous graphene layer may comprise a monatomic porous graphene layer. The device may comprise a graphene electrode having a continuous layer of graphene having an area between 1 μm2 and 10cm2.
According to a second aspect of the present invention, a method comprising etching a layer of graphene, and inhibiting said etching using a nanowire mask.
According to a third aspect of the present invention, an electronic device comprising
- a first graphene electrode,
- a second graphene electrode,
- a graphene semiconductor, and
- an electrical power supply,
wherein the graphene semiconductor, first, and second graphene electrodes, are configured such that supply of a current by the electrical power supply, between a first location, in the first graphene electrode, and a second location, in the second graphene electrode, establishes a potential difference between the first location and the second location, and such that the potential difference remains substantially constant with variation of the first or second location.
According to a fourth aspect of the present invention, an electronic device comprising a first graphene electrode, a second graphene electrode, a graphene
semiconductor, and an electrical power supply, the graphene semiconductor, first and second graphene electrodes, each being configured such that supply of a current by the power supply, between a first point, in the first graphene electrode, and a second point, in the second graphene electrode, establishes a potential difference between the points, and such that there is substantially no potential difference across the first graphene electrode, and substantially no potential difference across the second graphene electrode.
According to a fifth aspect of the present invention, a method of applying a potential difference between a first point, in a first graphene electrode, and a second point, in a second graphene electrode comprising:
locating a graphene semiconductor between the two electrodes;
(ii) passing an electrical current through the graphene semiconductor and between the first and second points, such that a potential difference is established between the first and second points, and such that there is substantially no potential difference across the first graphene electrode, and substantially no potential difference across the second graphene electrode. BRIEF DESCRIPTION OF THE DRAWINGS
For a more complete understanding of example embodiments of the present invention, reference is now made to the following descriptions taken in connection with the accompanying drawings in which:
FIGURE 1 shows a process for fabricating a device according to one aspect of the invention;
FIGURE 2 shows a two variants for one of the stages in the figure 1 process; and
FIGURE 3 shows a device according to one aspect of the invention.
DETAILED DESCRIPTON OF THE DRAWINGS
An example embodiment of the present invention and its potential advantages are understood by referring to FIGURES 1 to 3 of the drawings.
Fig. 1 shows a fabrication process in accordance with one aspect of the present invention. An initial step 1 is deposition of a layer of graphene 12 on a substrate 11. One example process for implementing the deposition is described in US20090110627. The graphene deposition process comprises the forming a graphitizing catalyst; heat-treating a gaseous carbon source in the presence of the graphitizing catalyst to form graphene, and cooling the graphene to form a graphene layer 12.
The gaseous carbon source may comprise a compound having molecules containing between 1 and 7 carbon atoms, may comprise a compound selected from: carbon monoxide, ethane, ethylene, ethanol, acetylene, propane, propylene, butane, butadiene, pentane, pentene, cyclopentadiene, hexane, cyclohexane, benzene, toluene, methane, and a combination comprising at least one of the foregoing compounds.
The heat-treating may be performed at a temperature between 300 C to about 2000 C, and for between 0.001 hour to about 1000 hours. The graphitizing catalyst may comprise Ni, Co, Fe, Pt Au, Al, Cr, Cu, Mg, Mn, Mo, Rh, Si, Ta, Ti, W, U, V, Zr, or any combination thereof.. Hydrogen is further supplied with the gaseous carbon source.
The graphene film 12 may be fabricated by chemical vapour deposition described by Alfonso Reina et al in Nano Letters, 9 (1), 30-35 (2009); or by chemical reduction of exfoliated graphite oxide, which is described by Stankovich, S. etc al, in Carbon 2007, 45 (7), 1558-1565. Once the graphene layer 12 has been deposited, a continuous mask 16 may be fabricated by step 2, on the graphene layer 12, by electron beam lithography using a hydrogen silsesquioxane (HSQ) resist as described in "Semiconducting Graphene Ribbon Transistor" by Zhihong Chen et al, IEEE Xplore, p 265 to 266. Alternatively, once the graphene layer 12 has been deposited, a continuous mask 16 may be fabricated by step 2, on the graphene layer 12, using a hydrogen silsesquioxane (HSQ) deposition by a spin-on process. Example of such process is described in US 6,232,662.
Once the continuous mask 16 has been deposited, a nanowire mask 14 is deposited, at step 3a. The nanowire mask comprises nanowires, such as silicon nanowires that may be randomly oriented. Step 3a may comprise fabrication of silicon nanowires on a sacrificial substrate and transfer of silicon nanowires on to the graphene layer 12 by mechanical contact pressure. An example of step 3a is described by Javey, A. et al in Nano Lett. 2007, 7, 773. Alternative methods of nanowire deposition are: spin casting, ink-jet printing, shear force contact printing, or nanowire suspensions as described in "Nanowire lithography on silicon", Alan CoIi et al, Nano Lett, VoI 8, No 5, 2008, p 1358 to 1362.
Once the nanowire mask 14 has been deposited, graphene not under the continuous mask or nanowire mask 14 is removed by etching, at step 4. This can be implemented for example by using oxygen plasma in a reactive ion etching apparatus. One example of etching is described by B. Ozyilmaz et al in Appl. Phys. Lett. 91, 192107 (2007).
Once step 4 is complete, the continuous mask 16 is removed by step 5 that comprises a process of reactive ion etching. Example of the process is described in US 6,211,063. The nanowire mask removed by using hydrogen fluoride solution, e.g. as described in "Single-crystal metallic nanowires and metal/semiconductor nanowire heterostructures" Yue Wu et al, Nature, VoI 430, 1 July 2004, p 61 to 65.
Removal of part of the graphene layer 12 results in the formation of a porous graphene layer 15 having a multiplicity of pores which may correspond to the location of the nanowires in the nanowire mask 14. The porous graphene layer 15 may comprise a number of graphene nanoribbons, each nanoribbon having a smallest dimension, measured in the plane of the substrate, between lnm and 20nm. Some graphene nanoribbons may be interstitial nanoribbons, each interstitial nanoribbon being located between at least two pores formed in graphene layer 15.
In accordance with a further aspect of the invention, the process shown in figure 1 may be repeated, with the exception of step 3, which may be replaced by an alternative step 3b. Steps 3a and 3b are shown in figure 2. Step 3a is the same as step 3 in figure 1. Step 3b differs from the step 3b, in that an electric field is applied in the vicinity of the continuous mask 16 such that an aligned nanowire mask 14b is deposited- The aligned nanowire mask 14b comprises nanowires that are aligned with by the presence of the electric field.
The electrical properties of components comprising one or more graphene ribbons may be altered by changing the width of the ribbon or ribbons. Depending on the width, the component may be a semiconductor or a metallic conductor.
Figure 3 shows a device that may be fabricated by employing the figure 1 process, or by the variant of this process, partly depicted in figure 2. The device 31 comprises a power supply 32, a first graphene electrode 17, and a second graphene electrode 18. The device further comprises a graphene semiconductor 15, which is between, and in electrical contact with, the first and second graphene electrodes 17, 18. It has been shown that when graphene is confined to nanoribbons it changes from semi-metallic to semiconducting material, the graphene semiconductor 15 therefore comprises such nanoribbons. A potential difference is applied between a first point 37, in the first graphene electrode 17, and a second point 38, in the second graphene electrode 18, and an electric current is passed through the graphene semiconductor 15, between the first and second points 37, 38, such that a potential difference is established between the first and second points, and such that there is substantially no potential difference across the first graphene electrode 17, and substantially no potential difference across the second graphene electrode 18. In other words the potential difference remains constant with variation of the first or second location. The graphene electrodes 17, 18, and the graphene semiconductor 15 may have a low coefficient of absorption, and/or be flexible and/or stretchable. The figure 3 device 31 may therefore be at least partly flexible and/or stretchable, and at least partly transmit light through some of its components. A modification of the figure 3 device may comprise a gate electrode, disposed between electrodes 17 and 18, in contact with the semiconductor 15, to which a potential may be applied, such a modification may form part of a field effect transistor.
Without in any way limiting the scope, interpretation, or application of the claims appearing below, a technical effect of one or more of the example embodiments disclosed herein may be fabrication of large surface area graphene layers. Another technical effect of one or more of the example embodiments disclosed herein may be fabrication of transparent electronic devices. Another technical effect of one or more of the example embodiments disclosed herein may be fabrication of flexible and/or stretchable electronic devices. Yet another technical advantage may high charge carrier mobility. Yet other advantages may be at least one of ballistic transport, high current density, high thermal conductivity, and the possibility to control the electrical properties.
If desired, the different functions discussed herein may be performed in a different order and/or concurrently with each other. Furthermore, if desired, one or more of the above-described functions may be optional or may be combined.
Although various aspects of the invention are set out in the independent claims, other aspects of the invention comprise other combinations of features from the described embodiments and/or the dependent claims with the features of the independent claims, and not solely the combinations explicitly set out in the claims.
It is also noted herein that while the above describes example embodiments of the invention, these descriptions should not be viewed in a limiting sense. Rather, there are several variations and modifications which may be made without departing from the scope of the present invention as defined in the appended claims.

Claims

WHAT IS CLAIMED IS
1. A device comprising a porous graphene layer comprising a multiplicity of pores.
2. A device according to claim 1 comprising a multiplicity of porous graphene layers.
3. A device according to claim 1 wherein the porous graphene layer comprises a graphene ribbon.
4. A device according to claim 3 wherein the porous graphene layer comprises a multiplicity of graphene ribbons.
5. A device according to claim 3 wherein the porous graphene layer comprises a multiplicity of graphene ribbons configured to be substantially aligned.
6. A device according to claim 3 wherein the graphene ribbon comprises a graphene nanoribbon.
7. A device according to claim 6 wherein the porous graphene layer comprises a multiplicity of graphene nanoribbons.
8. A device according to claim 1 wherein the device comprises a graphene electrode.
9. A device according to claim 8 wherein the device comprises a multiplicity of graphene electrodes.
10. A device according to claim 8 wherein the graphene electrode comprises a graphene conductor.
11. A device according to claim 8 wherein at least 90% of the graphene electrode surface area is configured to be in contact with an insulator.
12. A device according to claim 8 wherein the graphene electrode comprises a continuous layer of graphene.
13. A device according to claim 9 wherein the porous graphene layer electrically connects two of the graphene electrodes.
14. A device according to claim 9 wherein the porous graphene layer electrically connects each of the graphene electrodes.
15. A method comprising etching a layer of graphene, and inhibiting said etching using a nanowire mask.
16. A method according to claim 15 wherein the method comprises depositing a multiplicity of nanowires on the later of graphene to form said nanowire mask.
17. A method according to claim 15 the nanowire mask comprises silicon, or silicon oxide.
18. A method according to claim 15 wherein the method comprises removing
substantially all the nanowire mask after said etching.
19. An electronic device comprising
- a first graphene electrode,
- a second graphene electrode,
- a graphene semiconductor, and
- an electrical power supply, wherein the graphene semiconductor, first, and second graphene electrodes, are configured such that supply of a current by the electrical power supply, between a first location, in the first graphene electrode, and a second location, in the second graphene electrode, establishes a potential difference between the first location and the second location, and such that the potential difference remains substantially constant with variation of the first or second location.
20. An electronic device according to claim 19 wherein the graphene semiconductor comprises a graphene nanoribbon wherein the nanoribbon has a width between 0.1 nm and 20nm.
PCT/IB2010/001453 2009-06-30 2010-06-15 Graphene device and method of fabricating a graphene device WO2011001240A1 (en)