WO2011000897A1 - Co-agglomerated latex polymer dispersions and methods of preparing and using same - Google Patents
Co-agglomerated latex polymer dispersions and methods of preparing and using same Download PDFInfo
- Publication number
- WO2011000897A1 WO2011000897A1 PCT/EP2010/059327 EP2010059327W WO2011000897A1 WO 2011000897 A1 WO2011000897 A1 WO 2011000897A1 EP 2010059327 W EP2010059327 W EP 2010059327W WO 2011000897 A1 WO2011000897 A1 WO 2011000897A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- dispersion
- polymer
- agglomerated
- particles
- aqueous dispersion
- Prior art date
Abstract
Description
Claims