WO2010088006A2 - Catalyst with bimodal pore size distribution and the use thereof - Google Patents

Catalyst with bimodal pore size distribution and the use thereof Download PDF

Info

Publication number
WO2010088006A2
WO2010088006A2 PCT/US2010/020070 US2010020070W WO2010088006A2 WO 2010088006 A2 WO2010088006 A2 WO 2010088006A2 US 2010020070 W US2010020070 W US 2010020070W WO 2010088006 A2 WO2010088006 A2 WO 2010088006A2
Authority
WO
WIPO (PCT)
Prior art keywords
catalyst
pore size
support
silver
olefin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2010/020070
Other languages
French (fr)
Other versions
WO2010088006A3 (en
Inventor
Christian Gueckel
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Scientific Design Co Inc
Original Assignee
Scientific Design Co Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=42396270&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=WO2010088006(A2) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Priority to EP10736169.3A priority Critical patent/EP2391448B1/en
Priority to CN201080013849.2A priority patent/CN102365128B/en
Priority to MX2011007946A priority patent/MX2011007946A/en
Priority to JP2011547990A priority patent/JP2012516234A/en
Priority to KR1020117019691A priority patent/KR101711108B1/en
Application filed by Scientific Design Co Inc filed Critical Scientific Design Co Inc
Priority to RU2011135743/04A priority patent/RU2011135743A/en
Priority to BRPI1007448A priority patent/BRPI1007448A2/en
Publication of WO2010088006A2 publication Critical patent/WO2010088006A2/en
Publication of WO2010088006A3 publication Critical patent/WO2010088006A3/en
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

The invention is directed to a catalyst for the epoxidation of an olefin to an olefin oxide, the catalyst comprising a support having at least two pore size distributions, each pore size distribution possessing a different mean pore size and a different pore size of maximum concentration, the catalyst further comprising a catalytically effective amount of silver, a promoting amount of rhenium, and a promoting amount of one or more alkali metals, wherein the at least two pore size distributions are within a pore size range of about 0.01 m to about 50 m. The invention is also directed to a process for the oxidation of an olefin to an olefin oxide using the above-described catalyst.

Description

CATALYST WITH BIMODAL PORE SIZE DISTRIBUTION AND THE USE THEREOF
[0001] The invention pertains, generally, to a catalyst useful for the epoxidation of an olefin to an olefin oxide, and more particularly, to such a catalyst with an improved selectivity by virtue of an improvement in carrier design.
[0002] There is continuing interest in producing improved catalysts for the epoxidation of olefins. Of particular interest are catalysts for the highly selective epoxidation of ethylene. These catalysts typically comprise a porous refractory support such as alpha alumina, which has on its surface a catalytic amount of silver and at least one promoter that helps to increase selectivity in the epoxidation process. The use of alkali metals and transition metals as promoters for silver catalysts is well known for the production of ethylene oxide by the partial oxidation of ethylene in the vapor phase. Examples of catalysts are disclosed in U.S. Patents 4,010,155; 4,012,425; 4,123,385; 4,066,575; 4,039,561 and 4,350,616. Such highly selective catalysts contain, in addition to silver, selectivity-enhancing promoters such as rhenium, molybdenum, tungsten or nitrate-or nitrite-forming compounds, as discussed in U.S. Patents 4,761,394 and 4,766,105. The catalyst may comprise further elements like alkali metals as described in U.S. Patent 3,962,136 and U.S. Patent 4,010,115.
[0003] Over the last two decades, rhenium was described as being effective in improving the selectivity of alkaline metal promoted silver-based catalyst supported by a refractory porous support. Some references in the art are U.S. Patents 4,761,394 and 4,833,261. The further improvement of silver-based catalyst promoted with alkaline metals and rhenium by the use of sulfur, Mo5 W5 Cr was disclosed in U.S. Patents 4,766,105; 4,820,675 and 4,808,738. EP 1 074301 Bl and WO 2002/051547 disclose a catalyst containing aluminum oxide, titanium oxide and/or silicon oxide and at least one element of the first and second main group, an element of the third sub-group and an element of the eighth sub-group with bimodal pore size distribution for the dehydrogenation Of C2-C]6 hydrocarbons.
[0004] Beside the chemical composition of a supported siϊver-based epoxidation catalyst, the physical characteristics of the finished catalyst as well the support have been an integral part of catalyst development. Generally, the silver-based catalyst support shows a characteristic pore volume and pore size distribution. Furthermore, the surface area and the water absorption are well-known characteristics for such catalyst supports. It has now been found that the physical characteristics of the finished catalyst and the impact of the characteristics on the catalyst performance are more complicated than heretofore believed, especially if the catalyst is promoted with rhenium. In addition to the surface area, the pore volume and the pore size distribution, the pattern of the pore size distribution, especially the number and the specific characteristics of different modes, has now been found to have a significant positive impact on the catalyst selectivity.
(0005] It has been unexpectedly found that improved catalysts selectivity can be attained when the silver, rhenium and promoters are deposited onto a solid support having a multimodal (e.g., bimodal) pore distribution.
[00061 In a first aspect, the invention is directed to an olefin epoxidation catalyst comprising a catalyst support (i.e., carrier) having at least two pore size distributions (i.e., at least two modes of pore distributions), each pore size distribution possessing a different mean pore size and a different pore size of maximum concentration. The at least two pore size distributions are preferably within a pore size range of about 0.01 μm to about 50 μm. The catalyst further contains a catalytically effective amount of silver, a promoting amount of rhenium, and a promoting amount of one or more alkali metals.
[0007] In one embodiment, at least one of the pore size distributions of the carrier is within a pore size range of about 0.01 μm to about 5 μm.
[0008] In another embodiment, at least one of the pore size distributions of the carrier is within a pore size range of about 5 μm to about 30 μm.
|OOΘ9] In another embodiment, at least two pore size distributions of the carrier are within a pore size range of about 0.01 μm to about 5 μm.
[00101 In yet another embodiment, at least two pore size distributions of the carrier are within a pore size range of about 5 μm to about 30 μm.
[0011] In still another embodiment, at least one of the pore size distributions is within a pore size range of about 0.01 μm to about 5 μm, and at least one of the pore size distributions is within a pore size range of about 5 μm to about 30 μm. Alternatively, at least one of the pore size distributions possesses a mean pore size within about 0.01 μm to about 5 μm (for example, at or below 5 μm), and at least one of the pore size distributions possesses a mean pore size range within about 5 μm (for example, at or above 5 μm) to about 30 μm.
[0012] In a particular embodiment, the support possesses a bimodal pore size distribution comprised of a first mode of pores and a second mode of pores. Preferably, the first mode of pores has a mean pore diameter ranging from about 0.01 μm to about 5 μm and the second mode of pores has a mean pore diameter ranging from about 5 μm to about 30 μm.
[0013] The invention also provides a process for the oxidation of an olefin to an olefin oxide, the process comprising the vapor phase oxidation of an olefin (e.g., ethylene) with molecular oxygen in a fixed bed, tubular reactor, in the presence of the catalyst described above.
[0014] Fig 1 shows a graph of a monomodal vs. a bimodal pore size distribution.
[0015] The support employed in this invention may be selected from a large number of solid, refractory supports that are porous and provide the preferred pore structure, Alumina is well known to be useful as a catalyst support for the epoxidation of an olefin and is the preferred support. The alumina support may also contain various impurities and additives which mayor may not influence the catalytic epoxidation reaction. In the process of making the preferred alumina support, high-purity aluminum oxide, preferably alpha-alumina, is thoroughly mixed with temporary and permanent binders. The temporary binders, known as burnout materials, are thermally decomposable organic compounds of moderate to high molecular weight which, on decomposition, alter the pore structure of the support. The permanent binders are typically inorganic clay-type materials having fusion temperatures below that of the alumina and impart mechanical strength to the finished support. After thorough dry-mixing, sufficient water and/or other suitable liquid is added to help form the mass into a paste-like substance. Catalyst support particles are then formed from the paste by conventional means such as extrusion. The particles are then dried and are subsequently calcined at an elevated temperature.
[0016] The support may comprise materials such as alpha-alumina, charcoal, pumice, magnesia, zirconia, titania, kieselguhr, fuller's earth, silicon carbide, silica, silicon carbide, clays, artificial zeolites, natural zeolites, silicon dioxide and/or titanium dioxide, ceramics and combination thereof. The preferred support is comprised of alpha-alumina having a very high purity; i.e., at least 95 wt. % pure, or more preferably, at least 98 wt. % alpha- alumina. The remaining components may include inorganic oxides other than alpha- alumina, such as silica, alkali metal oxides (e.g., sodium oxide) and trace amounts of other metal-containing or non-metal-containing additives or impurities.
[0017] The solid support (carrier) employed in the present invention has a multimodal pore size distribution (Le, different pore size ranges, each range possessing a different pore size of maximum concentration). The multimodal pore size distribution is at least bimodal, and can thus be trimodal, tetramodal, or of a higher modality. The multimodal pore size distribution is characterized by the presence of at least two distributions (modes) of pore sizes, each pore size distribution being either overlapping or non-overlapping with another pore size distribution, and each pore size distribution having its own range of pore sizes (pore diameters) and peak concentration (typically expressed as peak pore volume). Each pore size distribution can be characterized by a single mean pore size (mean pore diameter) value. Accordingly, a mean pore size value given for a pore size distribution necessarily corresponds to a range of pore sizes that result in the indicated mean pore size value.
[0018] The carrier can have any suitable distribution of pore diameters. As used herein, the "pore diameter" is used interchangeably with "pore size". Typically, the pore diameters for each range are at least about 0.01 microns (0.01 μm), and more typically, at least about 0.1 μm. In different embodiments, the pore diameters can be at least about 0.2 μm, or 0.3 μms or 0.4 μm, or 0.5 μm, or 0.6 μm, or 0.7 μm, or 0.8 μm, or 0.9 μm, or 1.0 μm, or 1.5 μm, or 2.0 μm. Typically, the pore diameters are no more than about 50 μm, 40 μm, 30 μm, 20 μm, or 10 μm. In particular embodiments, the pore diameters are no more than about 9 μm, or 8 μm, or 7 μm, or 6 μm, or 5 μm, or 4 μm, or 3 μm, or 2.5 μm. Any range derived from the foregoing minimum and maximum exemplary values is also suitable herein. In different embodiments, the suitable pore diameter range for each mode of pores can be independently selected from, for example, 0.01-50 μm, 1-50 μm, 2-50 μm, 5-50 μm, 10-50 μm, 20-50 μm, 30-50 μm, 0.01-40 μm, 1-40 μm, 2-40 μm, 5-40 μm, 10-40 μm, 20-40 μm, 30-40 μm, 0.01- 30 μm, 0.05-30 μm, 0.1-30 μm, 0.5-30 μm, 1-30 μm, 2-30 μm, 3-30 μm, 4-30 μm, 5-30 μm, 10-30 μm, 15-30 μm, 20-30 μm, 0.01-10 μm, 0.05-10 μm, 0.1-10 μm, 0.5-10 μm, 1-10 μm, 2-10 μm, 3-10 μm, 4-10 μm, 5-10 μm, 640 μm, 7-10 μm, 8-10 μm, 9-10 μm, 0.01-8 μm, 0.05-8 μm, 0.1-8 μm, 0.5-8 μm, 1-8 μm, 1.5-8 μm, 2-8 μm, 2.5-8 μm, 3-8 μm, 4-8 μm, 5-8 μm, 6-8 μm, 7-8 μm, 0.01-6 μm, 0.05-6 μm, 0.1-6 μm, 0.5-6 μm, 1-6 μm, 1.5-6 μm, 2-6 μm, 2.5-6 μm, 3-6 μm, 4-6 μm, 5-6 μm, 0.01-5 μm, 0.05-5 μm, 0.1-5 μm, 0.5-5 μm, 1-5 μm, 1.5-5 μm, 2-5 μm, 2.5-5 μm, 3-5 μm, 3.5-5 μm, 4-5 μm, 0.01-4 μm, 0.05-4 μm, 0.1-4 μm, 0.5-4 μm, 1-4 μm, 1.5-4 μm, 2-4 μm, 2.5-4 μra, 3-4 μm, 3.5-4 μm, 0.01-3 μm, 0.05-3 μm, 0.1-3 μm, 0.5-3 μm, 1-3 μm, 1.5-3 μm, 2-3 μm, 2.5-3 μm, 0.01-2 μm, 0.05-2 μm, 0.1-2 μm, 0.5-2 μm, 1-2 μm, and 1.5-2 μm, as long as the range of each mode of pores is different and each range possesses a different pore size of maximum concentration.
[0019] The first mode and second mode of pores possess different mean pore sizes (i.e., different mean pore diameters). Preferably, at least one of the modes of pores has a mean pore diameter within the range of about 0.01 μm to about 5 μm. More preferably, both a first and second mode of pores have a mean pore diameter within the range of about 0.01 μm to about 5 μm as long as the mean pore diameters are different. For example, at least one of the first and second mode of pores can have a mean pore size of about 0.01 μm, 0.02 μm, 0.03 μm, 0.04 μm, 0.05 μm, 0.06 μm, 0.07 μm, 0.08 μm, 0.09 μm, 0.1 μm, 0.2 μm, 0.3 μm, 0.4 μm, 0.5 μm, 0.6 μm, 0.7 μm, 0.8 μm, 0.9 μm, 1.0 μm, 1.1 μm, 1.2 μm, 1.3 μm, 1.4 μm, 1.5 μm, 1.6 μm, 1.7 μm, 1.8 μm5 1.9 μm, 2.0 μm, 2.1 μm, 2.2 μm, 2.3 μm, 2.4 μm, 2.5 μm, 2.6 μm, 2.7 μm, 2.8 μm, 2.9 μm, 3.0 μm, 3.1 μm, 3.2 μm, 3.3 μm, 3.4 μm, 3.5 μm, 3.6 μm, 3.7 μm, 3.8 μm, 3.9 μm, 4.0 μm, 4.1 μm, 4.2 μm, 4.3 μm, 4.4 μm, 4.5 μm, 4.6 μm, 4.7 μm, 4.8 μm, 4.9 μm, or 5.0 μm. Two or more modes of pores can also be independently selected from any of the above mean pore sizes as long as the mean pore sizes for each mode of pores are different. Any range derived from any two values recited above are also contemplated herein.
[0020] In another embodiment, at least one mode of pores is characterized by having a mean pore diameter at or above 5 μm up to about 30 μm. For example, in different embodiments, at least one mode of pores can have a mean pore diameter at or above 5 μm to about 25 mm, or at or above 5 μm to about 20 mm, or at or above 5 μm to about 15 mm, or at or above 5 μm to about 10 mm, or at or about 6 μm to about 30 μm, or at or about 7 μm to about 30 μm, or at or about 8 μm to about 30 μm, or at or about 10 μm to about 30 μm, or at or about 10 μm to about 25 μm, or at or about 10 μm to about 20 μm, or at or about 15 μm to about 30 μm. In one embodiment, one mode of pores has a mean pore diameter within the range of about 0,01 μm to about 5 μm (or any of the specific exemplary values given above within this range, or sub-ranges derived therefrom) while another mode of pores has a mean pore diameter at or above 5 μm up to about 30 μm, or any of the sub-ranges given therein. In another embodiment, at least two modes of pores have a mean pore diameter at or above 5 μm up to about 30 μm.
[0021] In a first embodiment, the first mode of pores comprises at most about 50 % of the total pore volume and the second mode of pores comprises at least about 50 % of the total pore volume. In a second embodiment, the first or second mode of pores comprises at most about 45 % of the total pore volume and the other mode of pores comprises at least about 55 % of the total pore volume. In a third embodiment, the first or second mode of pores comprises at most about 40 % of the total pore volume and the other mode of pores comprises at least about 60 % of the total pore volume. In a fourth embodiment, the first or second mode of pores comprises at most about 35 % of the total pore volume and the other mode of pores comprises at least about 65 % of the total pore volume. In a fifth embodiment, the first or second mode of pores comprises at most about 30 % of the total pore volume and the other mode of pores comprises at least about 70 % of the total pore volume. Numerous other embodiments reflective of different bimodal pore distributions are possible and within the scope of the present invention. Without wishing to be bound by any theory, it is believed that a catalyst with the described bimodal or multimodal pore size distribution possesses a type of pore structure in which reaction chambers are separated by diffusion channels. The pore volume and pore size distribution described herein can be measured by any suitable method, but are more preferably obtained by the conventional mercury porosimeter method as described in, for example, Drake and Ritter, Ind. Eng. Chem. Anal Ed , 17, 787 (1945).
[0022] Preferably, the mean pore diameter of the first mode of pores and the mean pore diameter of the second mode of pores (i.e., the "differential in mean pore diameters") are different by at least about 0.1 μm. In different embodiments, the difference in mean pore sizes can be at least, for example, 0.2 μm, or 0.3 μm, or 0.4 μm, or 0.5 μm, or 0.6 μm, or 0.7 μm, or 0.8 μm, or 0.9 μm, or LO μm, or 1.2 μm, or 1.4 μm, or 1,5 μm, 1.6 μm, or 1.8 μm, or 2.0 μm, or 2.5 μm, or 3 μm, or 4 μm, or 5 μm, or 6 μm, or 7 μm, or 8 μm, or 9 μm, or 10 μm, and up to about 15, 20 or 30 μm.
[0023] In a preferred embodiment, the solid support surface has a bimodal pore size distribution comprised of a first mode and a second mode of pores. Preferably, the first mode of pores has a mean pore diameter ranging from about 0.01 μm to about 5 μm. More preferably, the first mode of pores has a mean diameter ranging from about 0.1 μm to about 4 μm. The second mode of pores possesses a mean pore diameter different from the first mode of pores. Preferably, the second mode of pores has a mean pore diameter ranging from about 5 μm to about 30 μm. More preferably, the second mode of pores has a mean pore diameter ranging from about 5 μm to about 20 μm. In one embodiment, the first mode of pores comprises at most about 50% of the total pore volume. In another embodiment, the first mode of pores comprises at most about 45% of the total pore volume and the second mode of pores comprises at least about 55% of the total pore volume. In another embodiment, the first mode of pores comprises at most about 40% of the total pore volume and the second mode of pores comprises at least about 60% of the total pore volume. It is believed, without limiting the scope of the invention, that a catalyst with the described bimodal pore size distribution provides advantageous pore structure with reaction chambers separated by diffusion channels. The surface acidity of the support, as determined by irreversible ammonia sorption at 1000C, is often less than about 2 niicromoles per gram of support, preferably less than about 1.5 micromoles per gram of support, and more preferably from about 0.05 to 1.0 micromoles per gram of support. Fig. 1 shows a graph of monomodal vs. bimodal pore size distribution.
[0024J The support preferably has a B.E.T. surface area of at most 20 m2/g, more preferably at most 10 m2/g, more preferably at most 5 m2/g, and more preferably at most 1 m2/g. More preferably, the B.E.T. surface area is in the range of 0.4 - 4.0 m2/g, more preferably from about 0.5 to about 1.5 m2/g, and most preferably from about 0.5 m2/g to about 1 m2/g. Preferably, the support comprises alumina with a surface area of less than about 1 m2/g. The B.E.T. surface area described herein can be measured by any suitable method, but is more preferably obtained by the method described in Brunauer, S., et al., J. Am. Chem. Soc, 60, 309-16 (1938). Suitable porosity volumes measured by mercury intrusion techniques are expected to be in the range of from about 0,2 ml/g to about 0.8 ml/g, preferably from about 0.25 ml/g to about 0.60 ml/g. The final support typically has a water absorption values ranging from about 0.2 cc/g to about 0.8 cc/g, preferably from about 0.25 cc/g to about 0.6 cc/g.
[0025] The carrier of the invention can be of any suitable shape or morphology. For example, the carrier can be in the form of particles, chunks, pellets, rings, spheres, three- holes, wagon wheels, cross-partitioned hollow cylinders, and the like, of a size preferably suitable for employment in fixed bed reactors. Typically, carrier particles have equivalent diameters in the range of from about 3 mm to about 12 mm, and more typically in the range of from about 5 mm to about 10 mm, which are usually compatible with the internal diameter of the tubular reactors in which the catalyst is placed. As known in the art, the term "equivalent diameter" is used to express the size of an irregularly-shaped object by expressing the size of the object in terms of the diameter of a sphere having the same volume as the irregularly-shaped object.
[0026] In general, a suitable catalyst support of the present invention can be prepared by mixing the refractory material, such as alumina, water or other suitable liquid, a burnout material or suitable porosity-controlling agent, and a binder. Burnout materials include cellulose, substituted celluloses, e.g. methylcellulose, ethylcellulose, and carboxyethylcellulose, stearates, such as organic stearate esters, e.g. methyl or ethyl stearate, waxes, granulated polyolefins, particularly polyethylene and polypropylene, walnut shell flour, and the like which are decomposable at the firing temperatures used in preparation of the support. The burnout is used to modify the porosity of the support. It is essentially totally removed during the firing to produce the finished support. Supports of the present invention are preferably made with the inclusion of a bonding material such as silica with an alkali metal compound in sufficient amount to substantially prevent the formation of crystalline silica compounds. Appropriate binders include inorganic clay-type materials. A particularly convenient binder material is a mixture of boehmite, an ammonia stabilized silica sol, and a soluble sodium salt.
[0027] A paste is formed by mixing the dry ingredients of the support with water or other suitable liquid, and the paste is usually extruded or molded into the desired shape, and then fired or calcined at a temperature of from about 12000C to about 16000C to form the support. When the particles are formed by extrusion, it may be desirable to also include extrusion aids. The amounts of extrusion aids required would depend on a number of factors that relate to the equipment used. However, these matters are well within the general knowledge of a person skilled in the art of extruding ceramic materials. After firing, the support is preferably washed to remove soluble residues. Washing is most commonly done with water but washing with other solvents or aqueous/non-aqueous solutions can also be beneficial. Suitable supports having a bimodal pre-distribution are available from Saint- Gobain Norpro Co., Noritake Co., and Sued Chemie AG, CeramTec AG.
[0028] In order to produce a catalyst for the oxidation of ethylene to ethylene oxide, a support having the above characteristics is then provided with a catalytically effective amount of silver on its surface. The catalyst is prepared by impregnating the support with a silver compound, complex or salt dissolved in a suitable solvent sufficient to cause deposition of a silver-precursor compound onto the support. Preferably, an aqueous silver solution is used. After impregnation, the excess solution is removed from the impregnated support and the impregnated support is heated to evaporate the solvent and to deposit the silver or silver compound on the support as is known in the art.
[0029] Preferred catalysts prepared in accordance with this invention contain up to about 45% by weight of silver, expressed as metal, based on the total weight of the catalyst including the support. The silver is deposited upon the surface and throughout the pores of a porous refractory support. Silver contents, expressed as metal, of from about 1% to about 40% based on the total weight of the catalyst are preferred, while silver contents of from about 8% to about 35% are more preferred. The amount of silver deposited on the support or present on the support is that amount which is a catalytically effective amount of silver, i.e., an amount which economically catalyzes the reaction of ethylene and oxygen to produce ethylene oxide. As used herein, the term "catalytically effective amount of silver" refers to an amount of silver that provides a measurable conversion of ethylene and oxygen to ethylene oxide. Useful silver-containing compounds which are silver precursors non- exclusively include silver oxalate, silver nitrate, silver oxide, silver carbonate, a silver carboxylate, silver citrate, silver phthalate, silver lactate, silver propionate, silver butyrate and higher fatty acid salts and combinations thereof.
[0030J Also deposited on the support, either prior to, coincidentally with, or subsequent to the deposition of the silver is a promoting amount of a rhenium component, which may be a rhenium-containing compound or a rhenium-containing complex. The rhenium promoter may be present in an amount of from about 0.001 wt.% to about 1 wt.%, preferably from about 0.005 wt. % to about 0.5 wt. %, and more preferably from about 0.01 wt. % to about 0.1 wt. % based on the weight of the total catalyst including the support, expressed as the rhenium metal.
[0031] Also deposited on the support either prior to, coincidentally with, or subsequent to the deposition of the silver and rhenium are promoting amounts of an alkali metal or mixtures of two or more alkali melals, as well as optional promoting amounts of a Group II A alkaline earth metal component or mixtures of two or more Group HA alkaline earth metal components, and/or a transition metal component or mixtures of two or more transition metal components, all of which may be in the form of metal ions, metal compounds, meta! complexes and/or metal salts dissolved in an appropriate solvent. The support may be impregnated at the same time or in separate steps with the various catalyst promoters. The particular combination of silver, support, alkali metal promoters, rhenium component, and optional additional promoters of the instant invention will provide an improvement in one or more catalytic properties over the same combination of silver and support and none, or only one of the promoters.
[0032J As used herein, the term "promoting amount" of a certain component of the catalyst refers to an amount of that component that works effectively to improve the catalytic performance of the catalyst when compared to a catalyst that does not contain that component. The exact concentrations employed, of course, will depend on, among other factors, the desired silver content, the nature of the support, the viscosity of the liquid, and solubility of the particular compound used to deliver the promoter into the impregnating solution. Examples of catalytic properties include, inter alia, operability (resistance to runaway), selectivity, activity, conversion, stability and yield. It is understood by one skilled in the art that one or more of the individual catalytic properties may be enhanced by the "promoting amount" while other catalytic properties may or may not be enhanced or may even be diminished. It is further understood that different catalytic properties may be enhanced at different operating conditions. For example, a catalyst having enhanced selectivity at one set of operating conditions may be operated at a different set of conditions wherein the improvement is exhibited in the activity rather than the selectivity. In the epoxidation process, it may be desirable to intentionally change the operating conditions to take advantage of certain catalytic properties even at the expense of other catalytic properties. The preferred operating conditions will depend upon, among other factors, feedstock costs, energy costs, by-product removal costs and the like.
[0033] Suitable alkali metal promoters may be selected from lithium, sodium, potassium, rubidium, cesium or combinations thereof, with cesium being preferred, and combinations of cesium with other alkali metals being especially preferred. The amount of alkali metal deposited or present on the support is to be a promoting amount. Preferably, the amount will range from about 10 ppm to about 3000 ppm, more preferably from about 15 ppm to about 2000 ppm, and even more preferably from about 20 ppm to about 1500 ppm, and as especially preferred from about 50 ppm to about 1000 ppm by weight of the total catalyst, measured as the metal.
[0034] Suitable alkaline earth metal promoters comprise elements from Group IIA of the Periodic Table of the Elements, which may be beryllium, magnesium, calcium, strontium, and barium or combinations thereof. Suitable transition metal promoters may comprise elements from Groups IVA, VA, VIA, VIIA and VIIIA of the Periodic Table of the Elements, and combinations thereof, Most preferably, the transition metal comprises an element selected from Groups IVA, VA or VIA of the Periodic Table of the Elements. Preferred transition metals that can be present include molybdenum, tungsten, chromium, titanium, hafnium, zirconium, vanadium, tantalum, niobium, or combinations thereof.
[0035] The amount of alkaline earth metal promoter(s) and/or transition metal promoter(s) deposited on the support is a promoting amount. The transition metal promoter may typically be present in an amount of from about 0.1 micromoles per gram to about 10 micromoles per gram, preferably from about 0.2 micromoles per gram to about 5 micromoles per gram, and more preferably from about 0.5 micromoles per gram to about 4 micromoles per gram of total catalyst, expressed as the metal. The catalyst may further comprise a promoting amount of one or more sulfur compounds, one or more phosphorus compounds, one or more boron compounds, one or more halogen-containing compounds, or combinations thereof.
[0036] The silver solution used to impregnate the support may also comprise an optional solvent or a complexing/solubilizing agent such as are known in the art. A wide variety of solvents or complexing/solubilizing agents may be employed to solubilize silver to the desired concentration in the impregnating medium. Useful complexing/solubilizing agents include amines, ammonia, oxalic acid, lactic acid and combinations thereof. Amines include an alkylene diamine having from 1 to 5 carbon atoms. In one preferred embodiment, the solution comprises an aqueous solution of silver oxalate and ethylene diamine. The complexing/solubilizing agent may be present in the impregnating solution in an amount of from about 0.1 to about 5.0 moles per mole of silver, preferably from about 0.2 to about 4.0 moles, and more preferably from about 0.3 to about 3.0 moles for each mole of silver.
[0037] When a solvent is used, it may be an organic solvent or water, and may be polar or substantially or totally non-polar. In general, the solvent should have sufficient solvating power to solubilize the solution components. At the same time, it is preferred that the solvent be chosen to avoid having an undue influence on or interaction with the solvated promoters. Examples of organic solvents include, but are not limited to, alcohols, and in particular, alkanols; glycols, in particular alkyl glycols; ketones; aldehydes; amines; tetrahydrofuran; nitrobenzene; nitrotoluene; giymes, in particular glyrne, diglyme and tetraglyme; and the like. Organic-based solvents which have 1 to about 8 carbon atoms per molecule are preferred. Mixtures of several organic solvents or mixtures of organic solvent(s) with water may be used, provided that such mixed solvents function as desired herein.
[0038] The concentration of silver in the impregnating solution is typically in the range of from about 0.1 % by weight up to the maximum solubility afforded by the particular solvent/so lubilizing agent combination employed. It is generally very suitable to employ solutions containing from 0.5% to about 45% by weight of silver, with concentrations of from 5 to 35% by weight of silver being preferred.
[0039] Impregnation of the selected support is achieved using any of the conventional methods; for example, excess solution impregnation, incipient wetness impregnation, spray coating, etc. Typically, the support material is placed in contact with the silver-containing solution until a sufficient amount of the solution is absorbed by the support. Preferably, the quantity of the silver-containing solution used to impregnate the porous support is no more than is necessary to fill the pores of the support. A single impregnation or a series of impregnations, with or without intermediate drying, may be used, depending, in part, on the concentration of the silver component in the solution. Impregnation procedures are described in U.S. patents 4/761,394, 4,766,105, 4,908,343, 5,057,481, 5, 187, 140, 5,102,848, 5,011,807, 5,099,041 and 5,407,888. Known prior procedures of pre-deposition, co-deposition and post-deposition of the various promoters can be employed.
[0040] After impregnation of the support with the silver-containing compound, i.e. a silver precursor, rhenium component, alkali metal component, and the optional other promoters, the impregnated support is calcined for a time sufficient to convert the silver-containing compound to an active silver species and to remove the volatile components from the impregnated support to result in a catalyst precursor. The calcination may be accomplished by heating the impregnated support, preferably at a gradual rate, to a temperature in the range of from about 2000C to about 600 0C, preferably from about 2000C to about 500 0C, and more preferably from about 2000C to about 450 °C> at a pressure in the range of from 0.5 to 35 bar. In general, the higher the temperature, the shorter the required heating period. A wide range of heating periods have been suggested in the art; e.g., U.S. patent 3,563,914 suggests heating for less than 300 seconds, and U.S. patent 3,702,259 discloses heating from 2 to 8 hours at a temperature of from 100° C to 375°C, usually for duration of from about 0.5 to about 8 hours. However, it is only important that the heating time be correlated with the temperature such that substantially all of the contained silver is converted to the active silver species. Continuous or step-wise heating may be used for this purpose.
[0041 J During calcination, the impregnated support may be exposed to a gas atmosphere comprising an inert gas or a mixture of an inert gas with from about 10 ppm to 21 % by volume of an oxygen-containing oxidizing component. For purposes of this invention, an inert gas is defined as a gas that does not substantially react with the catalyst or catalyst precursor under the conditions chosen for the calcination. Non-limiting examples include nitrogen, argon, krypton, helium, and combinations thereof, with the preferred inert gas being nitrogen. Non-limiting examples of the oxygen-containing oxidizing component include molecular oxygen (O2), CO2, NO, NO2, N2O, N2O3, N2O4, or N2O5, or a substance capable of forming NO, NO2, N2O, N2O3, N2O4, or N2O5 under the calcination conditions, or combinations thereof, and optionally comprising SO3, SO2, trimethyl phosphite, or combinations thereof. Of these, molecular oxygen is a preferred embodiment, and a combination of O2 with NO or NO2 is another preferred embodiment. In one embodiment, the atmosphere comprises from about 10 ppm to about 1% by volume of an oxygen- containing oxidizing component. In another embodiment, the atmosphere comprises from about 50 ppm to about 500 ppm of an oxygen-containing oxidizing component.
[0042) In another embodiment, the impregnated support, which has been calcined as disclosed above, may optionally thereafter be contacted with an atmosphere comprising a combination of oxygen and steam, which atmosphere is substantially absent of an olefin, and preferably, completely absent of an olefin. The atmosphere usually comprises from about 2% to about 15% steam by volume, preferably from about 2% to about 10% steam by volume, and more preferably from about 2% to about 8% steam by volume. The atmosphere usually comprises from about 0.5% to about 30% oxygen by volume, preferably from about 1% to about 21 % oxygen by volume, and more preferably from about 5% to about 21 % oxygen by volume. The balance of the gas atmosphere may be comprised of an inert gas. Non-limiting examples of the inert gas include nitrogen, argon, krypton, helium, and combinations thereof, with the preferred inert gas being nitrogen. The contacting is usually conducted at a temperature of about 2000C or higher. In one embodiment the contacting is conducted at a temperature of from about 2000C to about 35O°C. In another embodiment the contacting is conducted at a temperature of from about 2300C to about 3000C. In another embodiment the contacting is conducted at a temperature of from about 2500C to about 2800C. In another embodiment the contacting is conducted at a temperature of from about 2600C to about 2800C. Usually the contacting is conducted for about 0.15 hour or more. In one embodiment the contacting is conducted for about 0.5 hour to about 200 hours. In another embodiment the contacting is conducted for about 3 hours to about 24 hours. In another embodiment the contacting is conducted for about 5 hours to about 15 hours.
Ethylene oxide production [0043] The epoxidation process may be carried out by continuously contacting an oxygen- containing gas with an olefin, which is preferably ethylene, in the presence of the catalyst produced by the invention. Oxygen may be supplied to the reaction in substantially pure molecular form or in a mixture such as air. Molecular oxygen employed as a reactant may be obtained from conventional sources. Reactant feed mixtures may contain from about 0.5% to about 45% ethylene and from about 3% to about 15% oxygen, with the balance comprising comparatively inert materials including such substances as carbon dioxide, water, inert gases, other hydrocarbons, and one or more reaction modifiers such as organic halides. Non-limiting examples of inert gases include nitrogen, argon, helium and mixtures thereof. Non-limiting examples of the other hydrocarbons include methane, ethane, propane and mixtures thereof. Carbon dioxide and water are byproducts of the epoxidation process as well as common contaminants in the feed gases. Both have adverse effects on the catalyst, so the concentrations of these components are usually kept at a minimum. Non- limiting examples of reaction moderators include organic halides such as Cj to Cg halohydrocarbons. Preferably, the reaction moderator is methyl chloride, ethyl chloride, ethylene dichloride, ethylene dibromide, vinyl chloride or mixtures thereof. Most preferred reaction moderators are ethyl chloride and ethylene dichloride.
[0044] A typical method for the ethylene epoxidation process comprises the vapor-phase oxidation of ethylene with molecular oxygen, in the presence of the inventive catalyst, in a fixed-bed tubular reactor. Conventional, commercial fixed-bed ethyl ene-oxide reactors are typically in the form of a plurality of parallel elongated tubes (in a suitable shell) approximately 0.7 to 2.7 inches O.D. and 0.5 to 2.5 inches LD. and 15-45 feet long filled with catalyst. Typical operating conditions for the ethylene epoxidation process involve temperatures in the range of from about 1800C to about 33O°C, and preferably, about 2000C to about 325°C, and more preferably from about 225°C to about 2700C. The operating pressure may vary from about atmospheric pressure to about 30 atmospheres, depending on the mass velocity and productivity desired. Higher pressures may be employed within the scope of the invention. Residence times in commercial -scale reactors are generally on the order of about 0.1 -5 seconds. The present catalysts are effective for this process when operated within these ranges of conditions.
[0045] The resulting ethylene oxide is separated and recovered from the reaction products using conventional methods. For this invention, the ethylene epoxidation process may include a gas recycle wherein substantially all of the reactor effluent is readmitted to the reactor inlet after substantially or partially removing the ethylene oxide product and the byproducts. In the recycle mode, carbon dioxide concentrations in the gas inlet to the reactor may be, for example, from about 0.3 to 6 volume percent.
[0046] The inventive catalysts have been shown to be particularly selective for oxidation of ethylene with molecular oxygen to ethylene oxide. The conditions for carrying out such an oxidation reaction in the presence of the catalysts of the present invention broadly comprise those described in the prior art. This applies to suitable temperatures, pressures, residence times, diluent materials, moderating agents, and recycle operations, or applying successive conversions in different reactors to increase the yields of ethylene oxide. The use of the present catalysts in ethylene oxidation reactions is in no way limited to the use of specific conditions among those which are known to be effective.
[0047] Conditions suitable for use in current commercial ethylene oxide reactor units are well-known to those of ordinary skill in the art.
[0048] The following non-limiting examples serve to illustrate the invention.
EXAMPLES
Aluminum oxides
[0049] The following aluminas were used for the preparation of the catalysts. The different types of alumina supports are available from Saint-Gobain Norpro Co., Noritake Co., Sued Chemie AG and/or CeramTec AG.
Figure imgf000018_0001
[0050] (a) Determined according to the method of Brunauer, Emmet and Teller
[0051] (b) Mercury intrusion data to 44.500 psia using Micrometrics AutoPore IV 9500 (140° contact angle, 0.480 N/m surface tension of mercury)
Catalyst preparation Silver solution
[0052 J An 834 g portion of high purity silver oxide (Ames Goldsmith Corp.) was added to a stirred solution of 442 g oxalic acid dehydrate (ACS Certified Reagent, Fisher) in about 2,800 g deionized water, A precipitate of hydrated silver oxalate salt formed on mixing. Stirring was continued for 0.5 hours. The precipitate was then collected on a filter and washed with deionized water. Analysis showed that the precipitate contained 50.5 wt % silver. Next, 213.9 g of the silver oxalate precipitate was dissolved in a mixture of '77, .2 grams ethyl enediamine (99+%, Aldrich) and 60.3 g deionized water. The temperature of the solution was kept below 4O0C by combining the reagents slowly, and by cooling the solution. After filtration, the solution contained roughly 30 wt % silver, and had a specific gravity of 1.52 g/mL.
EXAMPLE 1 : CATALYST A
[0053] A 150 g portion of alumina support A was placed in a flask and evacuated to ca. 0.1 torr prior to impregnation. To the above silver solution were added aqueous solutions of cesium hydroxide, perrhenic acid, and ammonium sulfate in order to prepare a catalyst composition according to examples 5-10 of U.S. Patent 4,766,105. After thorough mixing, the promoted silver solution was aspirated into the evacuated flask to cover the carrier while maintaining the pressure at ca. 0.1 torr. The vacuum was released after about 5 minutes to restore ambient pressure, hastening complete penetration of the solution into the pores. Subsequently, the excess impregnation solution was drained from the impregnated carrier. Calcination of the wet catalyst was done on a moving belt calciner, In this unit, the wet catalyst is transported on a stainless steel belt through a multi-zone furnace. All zones of the furnace are continuously purged with pre-heated, ultrahigh purity nitrogen and the temperature is increased gradually as the catalyst passes from one zone to the next. The heat is radiated from the furnace walls and from the preheated nitrogen.
[0054] In this Example 1, the wet catalyst entered the furnace at ambient temperature. The temperature was then increased gradually to a maximum of about 45O0C as the catalyst passed through the heated zones. In the last (cooling) zone, the temperature of the now activated catalyst was immediately lowered to less than 1000C before it emerged into ambient atmosphere. The total residence time in the furnace was approximately 45 minutes. The bimodal pores size distribution of the alumina support A is illustrated in Table I.
EXAMPLE 2: CATALYST B
[0055] Catalyst B was prepared with alumina support B following the procedure of Catalyst A. The bimodal pore size distribution of the alumina support B is illustrated in Table I.
EXAMPLE 3: CATALYST C (COMPARATIVE EXAMPLE)
[0056) Catalyst C was prepared with alumina support C following the procedure of Example 1. The monomodal pore size distribution of the alumina support C is illustrated in Table I. In addition, three catalysts containing only silver and cesium were prepared with the same alumina.
EXAMPLE 4: CATALYST D
[0057] A 150 g portion of alumina support A was placed in a flask and evacuated to ca. 0.1 torr prior to impregnation. To the above silver solution were added aqueous solutions of cesium hydroxide in order to prepare a catalyst with 14.1 wt% silver, similar to Examples 1 through 3, based on the total weight of the catalyst, and an amount of cesium. After thorough mixing, the cesium-promoted silver solution was aspirated into the evacuated flask to cover the carrier while maintaining the pressure at ca. 0.1 torr. The vacuum was released after about 5 minutes to restore ambient pressure, hastening complete penetration of the solution into the pores. Subsequently, the excess impregnation solution was drained from the impregnated carrier. Calcination of the wet catalyst was done on a moving belt calciner. In this unit, the wet catalyst is transported on a stainless steel belt through a multi-zone furnace. All zones of the furnace are continuously purged with pre-heated, ultrahigh purity nitrogen and the temperature is increased gradually as the catalyst passes from one zone to the next. The heat is radiated from the furnace walls and from the preheated nitrogen. In this Example 4, the wet catalyst entered the furnace at ambient temperature. The temperature was then increased gradually to a maximum of about 4500C as the catalyst passed through the heated zones. In the last (cooling) zone, the temperature of the now activated was immediately lowered to less than 1000C before it emerged into ambient atmosphere. The total residence time in the furnace was approximately 45 minutes.
EXAMPLE 5: CATALYST E
[0058] Catalyst E was prepared with alumina support B following the procedure of Catalyst D.
Testing of the catalyst
{Θ0S9] For testing, the catalyst was charged into a fixed-bed stainless steel tube reactor inch approximate inner diameter), which was embedded in a heated copper block. The catalyst charge consisted of 4 g crushed catalyst (1.0 -1.4 mm particle size) mixed with 8.6 grams of inert material and the inlet gas flow was adjusted to give a gas hour space velocity of 12375 h"1 and 0.83 Nl/min respectively. The feed gas composition by volume was 15% ethylene, 7 % oxygen, 5 % carbon dioxide, 1.7 ppmv ethyl chloride, and nitrogen balance. Reaction pressure was maintained at 19.4 atm. The reactor effluent was analyzed by mass spectrometry at roughly 1 hour intervals. In the case of Examples 1 through 3, the temperature was adjusted to maintain relatively constant EO production. The catalyst was kept under these conditions until the maximum selectivity was observed. The result is listed, hereinafter, in Table II. In the case of Examples 4 and 5, the temperature was adjusted to maintain relatively constant EO production. The catalyst was kept under these conditions until the maximum selectivity was observed. The result is listed, hereinafter, in Table III. Table I: Pore size distribution of used carrier
Figure imgf000022_0001
[0060] (a) Mercury intrusion data to 44.500 psia using Micrometrics AutoPore IV 9500 (140° contact angle, 0.480 N/m surface tension of mercury)
[0061] (b) Determined according to the method of Brunauer, Emmet and Teller a. * Percentage of the total pore volume of the catalyst
[0062] Pores larger than the second mode provide the remaining pore volume up to 100%. Table II: Test results with rhenium containing catalysts
Figure imgf000022_0002
Table III: Test results with catalyst containing silver and cesium only
Figure imgf000023_0001
[0063] Porosities are determined by the mercury porosimeter method; see Drake and Ritter, "Ind. Eng. Chern. anal, Ed.," 17, 787 (1945). Pore and pore diameter distributions are determined from the surface area and apparent porosity measurements. BET method: See J. Am. Chem. Soc. 60, 3098-16 (1938)
[0064] While the present invention has been demonstrated and described with reference to preferred embodiments, it will be readily appreciated by those of ordinary skill in the art that various changes and modifications may be made without departing from the spirit and scope of the invention. It is therefore intended that the claims be interpreted to cover the disclosed embodiment, those alternatives which have been discussed, and any and all equivalents thereto.

Claims

What is claimed is:
1. A catalyst for the epoxidation of an olefin to an olefin oxide comprising a support having at least two pore size distributions, each pore size distribution possessing a different mean pore size and a different pore size of maximum concentration, the catalyst further comprising a catalytϊcally effective amount of silver, a promoting amount of rhenium, and a promoting amount of one or more alkali metals, wherein the at least two pore size distributions are within a pore size range of about 0.01 μm to about 50 μm.
2. The catalyst of claim 1, wherein at least one of the pore size distributions is within a pore size range of about 0.01 μm to about 5 μm.
3. The catalyst of claim 1 , wherein at least one of the pore size distributions is within a pore size range of about 5 μm to about 30 μm.
4. The catalyst of claim 1 , wherein at least two pore size distributions are within a pore size range of about 0.01 μm to about 5 μm.
5. The catalyst of claim 1 , wherein at least two pore size distributions are within a pore size range of about 5 μm to about 30 μm.
6. The catalyst of claim 1 , wherein at least one of the pore size distributions is within a pore size range of about 0.01 μm to about 5 μm, and at least one of the pore size distributions is within a pore size range of about 5 μm to about 30 μm.
7. The catalyst of claim 1 , wherein a first mode of pores comprises at most 50 % of a total pore volume and a second mode of pores comprises at least 50 % of the total pore volume.
8. The catalyst of claim 1 , wherein a first mode of pores comprises at most 40 % of a total pore volume and a second mode of pores comprises at least 60 % of the total pore volume.
9. The catalyst of claim 1, wherein the support comprises alumina, charcoal, pumice, magnesia, zirconia, titania, kieselguhr, fuller's earth, silicon carbide, silica, silicon dioxide, magnesia, clays, artificial zeolites, natural zeolites, ceramics or combinations thereof.
10. The catalyst of claim 1, wherein the support comprises alumina.
1 1. The catalyst of claim 1 , wherein the support comprises alumina with a surface area of less than about 1 m2/g.
12. The catalyst of claim 1 , further comprising a promoting amount of one or more promoters selected from the group consisting of one or more Group IIA metals, one or more transition metals, sulfur, fluoride, phosphorus, boron, and combinations thereof.
13. The catalyst of claim 12, wherein the Group 1ΪA melal is selected from beryllium, magnesium, calcium, strontium, barium, and combinations thereof.
14. The catalyst of claim 12, wherein the transition metal is selected from elements of Groups IVA, VA, VIA, VIIA and VIIIA of the Periodic Table of the Elements, and combinations thereof.
15. The catalyst of claim 12, wherein the transition metal is selected from molybdenum, tungsten, chromium, titanium, hafnium, zirconium, vanadium, thorium, tantalum, niobium, and combinations thereof.
16. The catalyst of claim 12, wherein the transition melal is molybdenum, tungsten, or a combination thereof.
17. The catalyst of claim 1 wherein the catalyst further comprises a promoting amount of gallium, germanium, sulfur, phosphorus, boron, halogen, or a combination thereof, on the surface of the support.
18. The catalyst of claim 1 wherein the alkali metal is selected from lithium, sodium, potassium, rubidium, cesium, and combinations thereof.
19. The catalyst of claim 1 wherein the alkali metal is cesium.
20. A process for the oxidation of an olefin to an olefin oxide, the process comprising vapor phase oxidation of an olefin with molecular oxygen in a fixed bed, tubular reactor, in the presence of the catalyst of claim 1.
21. A process for the oxidation of an olefin to an olefin oxide which comprises the vapor phase oxidation of an olefin with molecular oxygen in a fixed bed, tubular reactor, in the presence of the catalyst produced by the process of claim 12.
22. A process for the oxidation of ethylene to ethylene oxide which comprises the vapor phase oxidation of ethylene with molecular oxygen in a fixed bed, tubular reactor, in the presence of the catalyst of claim 1.
23. A process for the oxidation of ethylene to ethylene oxide which comprises the vapor phase oxidation of ethylene with molecular oxygen in a fixed bed, tubular reactor, in the presence of the catalyst produced by the process of claim 12.
PCT/US2010/020070 2009-01-27 2010-01-05 Catalyst with bimodal pore size distribution and the use thereof Ceased WO2010088006A2 (en)