WO2010057549A1 - Réseau optique pouvant être commuté électriquement et ayant des propriétés de laser à rétroaction distribuée, laser à rétroaction distribuée le contenant et son procédé de fabrication - Google Patents

Réseau optique pouvant être commuté électriquement et ayant des propriétés de laser à rétroaction distribuée, laser à rétroaction distribuée le contenant et son procédé de fabrication Download PDF

Info

Publication number
WO2010057549A1
WO2010057549A1 PCT/EP2009/006649 EP2009006649W WO2010057549A1 WO 2010057549 A1 WO2010057549 A1 WO 2010057549A1 EP 2009006649 W EP2009006649 W EP 2009006649W WO 2010057549 A1 WO2010057549 A1 WO 2010057549A1
Authority
WO
WIPO (PCT)
Prior art keywords
areas
mixture
grating
laser
nematic
Prior art date
Application number
PCT/EP2009/006649
Other languages
English (en)
Inventor
Oksana Sakhno
Joachim Stumpe
Sigurd Schrader
Viachaslau Ksianzou
Original Assignee
Fraunhofer-Gesellschaft Zur Foerderung Der Angewandten Forschung E.V.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fraunhofer-Gesellschaft Zur Foerderung Der Angewandten Forschung E.V. filed Critical Fraunhofer-Gesellschaft Zur Foerderung Der Angewandten Forschung E.V.
Publication of WO2010057549A1 publication Critical patent/WO2010057549A1/fr

Abstract

La présente invention porte sur une structure dont de premières zones consistent en un réseau de matériau polymère organique ou comprennent celui-ci et dont de secondes zones consistent en un matériau à cristaux liquides nématiques et/ou smectiques et comprennent au moins un ou plusieurs cristaux liquides smectiques et/ou nématiques et un matériau à photoluminescence, les premières et secondes zones alternant dans au moins un premier plan, alors que la composition du film est sensiblement invariable dans au moins une direction qui forme un angle avec ledit premier plan, ou bien les secondes zones étant complètement entourées par les premières zones, et lesdites zones étant situées selon un motif périodique, le matériau à cristaux liquides smectiques et/ou nématiques dans les secondes zones s'étendant dans la direction longitudinale desdites zones d'une extrémité de la zone à l'autre, la structure étant disposée entre deux substrats, dont au moins l'un transmet la lumière. La structure, conjointement avec les substrats, peut former un réseau de Bragg et peut être utilisée comme laser à rétroaction distribuée. Ladite structure peut être préparée par l'utilisation d'un mélange isotrope et homogène comprenant un monomère/oligomère pouvant durcir à la lumière, un cristal liquide smectique et/ou nématique et un matériau à photoluminescence, le remplissage par ledit mélange de l'espace entre les deux substrats et l'irradiation de celui-ci avec un champ lumineux de telle sorte que des zones du mélange sont irradiées tandis que d'autres ne le sont pas. Sous l'effet de l'irradiation, le mélange se sépare en zones comportant un polymère durci à la lumière et des zones consistant en des cristaux liquides et un matériau à photoluminescence ou comprenant ceux-ci.
PCT/EP2009/006649 2008-11-18 2009-09-14 Réseau optique pouvant être commuté électriquement et ayant des propriétés de laser à rétroaction distribuée, laser à rétroaction distribuée le contenant et son procédé de fabrication WO2010057549A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP08169354.1 2008-11-18
EP08169354A EP2187254A1 (fr) 2008-11-18 2008-11-18 Réseau optique commutable électriquement ayant des propriétés de laser DFB, laser DFB le comprenant, et son procédé de production

Publications (1)

Publication Number Publication Date
WO2010057549A1 true WO2010057549A1 (fr) 2010-05-27

Family

ID=40198358

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2009/006649 WO2010057549A1 (fr) 2008-11-18 2009-09-14 Réseau optique pouvant être commuté électriquement et ayant des propriétés de laser à rétroaction distribuée, laser à rétroaction distribuée le contenant et son procédé de fabrication

Country Status (2)

Country Link
EP (1) EP2187254A1 (fr)
WO (1) WO2010057549A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017087374A1 (fr) * 2015-11-16 2017-05-26 Kent State University Laser accordable électriquement comportant une structure héliconique de cristaux liquides cholestériques
CN109119883A (zh) * 2018-07-25 2019-01-01 沈阳理工大学 一种基于su8光栅的可调谐液晶激光器及制作方法
WO2024031102A3 (fr) * 2022-08-05 2024-03-14 Star Voltaic, LLC Matériaux optiques et procédés associés

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN106785867B (zh) * 2016-12-27 2019-10-11 东南大学 一种控制聚合物分散液晶随机激光器的激光强度的方法
EP3435139A1 (fr) 2017-07-25 2019-01-30 Essilor International Article optique comprenant un guide d'ondes holographique

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1612596A1 (fr) * 2004-06-29 2006-01-04 Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung e.V. Filtre optique, commutable et accordable à base de composites et de films cristaux-liquides / polymères, les mélanges et le pocédé pour les fabriquer.

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3771065A (en) 1972-08-09 1973-11-06 Us Navy Tunable internal-feedback liquid crystal-dye laser
US4517280A (en) 1982-11-04 1985-05-14 Sumitomo Electric Industries, Ltd. Process for fabricating integrated optics
US5942157A (en) 1996-07-12 1999-08-24 Science Applications International Corporation Switchable volume hologram materials and devices
ITTO20030530A1 (it) 2003-07-09 2005-01-10 Infm Istituto Naz Per La Fisi Ca Della Mater Reticolo olografico di diffrazione, procedimento per la

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1612596A1 (fr) * 2004-06-29 2006-01-04 Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung e.V. Filtre optique, commutable et accordable à base de composites et de films cristaux-liquides / polymères, les mélanges et le pocédé pour les fabriquer.

Non-Patent Citations (4)

* Cited by examiner, † Cited by third party
Title
ABBATE G ET AL: "New generation of holographic gratings based on polymer-LC composites: POLICRYPS and POLIPHEM", MOLECULAR CRYSTALS AND LIQUID CRYSTALS GORDON & BREACH SWITZERLAND, vol. 453, 2006, pages 1 - 13, XP009110607, ISSN: 1058-725X *
SAKHNO O ET AL: "POLIPHEM: new type of nanoscale polymer-LC-switchable photonic devices", PROCEEDINGS OF THE SPIE - THE INTERNATIONAL SOCIETY FOR OPTICAL ENGINEERING SPIE-INT. SOC. OPT. ENG USA, vol. 5521, no. 1, 2004, pages 38 - 45, XP002510319, ISSN: 0277-786X *
SLUSSARENKO S, BAZHENOV V, VASNETSOV M, ABBATE G, STUMPE J, SAKHNO O: "Lasing in POLIPHEM based planar waveguides", 12TH INTERNATIONAL TOPICAL MEETING ON OPTICS OF LIQUID CRYSTALS, BOOK OF ABSTRACTS, 1 October 2007 (2007-10-01), Puebla City, Mexico, pages 125, XP002559931, Retrieved from the Internet <URL:http://www-optica.inaoep.mx/~olc07/Book%20of%20abstracts%20OLC07.pdf> [retrieved on 20090727] *
VASNETSOV M V; BAZHENOV V YU; SLUSSARENKO S S; SAKHNO O; STUMPE J; ABBATE G: "First approach to the analysis of the lasing conditions in POLIPHEM<(c)> structures", MOLECULAR CRYSTALS AND LIQUID CRYSTALS, GORDON AND BREACH SCIENCE PUBLISHERS SA, vol. 488, 1 August 2008 (2008-08-01), Switzerland, pages 135 - 147, XP009110603 *

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017087374A1 (fr) * 2015-11-16 2017-05-26 Kent State University Laser accordable électriquement comportant une structure héliconique de cristaux liquides cholestériques
US11444427B2 (en) 2015-11-16 2022-09-13 Kent State University Electrically tunable laser with cholesteric liquid crystal heliconical structure
CN109119883A (zh) * 2018-07-25 2019-01-01 沈阳理工大学 一种基于su8光栅的可调谐液晶激光器及制作方法
WO2024031102A3 (fr) * 2022-08-05 2024-03-14 Star Voltaic, LLC Matériaux optiques et procédés associés

Also Published As

Publication number Publication date
EP2187254A1 (fr) 2010-05-19

Similar Documents

Publication Publication Date Title
Natarajan et al. Holographic polymer dispersed liquid crystal reflection gratings formed by visible light initiated thiol-ene photopolymerization
TWI379109B (en) High-efficient, tuneable and switchable optical elements based on polymer-liquid crystal composites and films, mixtures and a method for their production
US6878494B2 (en) Switchable volume hologram materials and devices
US7077984B1 (en) Electrically switchable polymer-dispersed liquid crystal materials
US7413678B1 (en) Electrically switchable polymer-dispersed liquid crystal materials
He et al. Tunable two-photon pumped lasing using a holographic polymer-dispersed liquid-crystal grating as a distributed feedback element
WO2010057549A1 (fr) Réseau optique pouvant être commuté électriquement et ayant des propriétés de laser à rétroaction distribuée, laser à rétroaction distribuée le contenant et son procédé de fabrication
Qi et al. Holographically formed polymer dispersed liquid crystal displays
Sakhno et al. Distributed feedback dye laser holographically induced in improved organic–inorganic photocurable nanocomposites
US9303209B2 (en) Continuous wave directional emission liquid crystal structures and devices
JP4925029B2 (ja) 切断あるいは曲げ加工を可能とするレーザー共振器製造方法
Sakhno et al. POLIPHEM: new type of nanoscale polymer-LC-switchable photonic devices
Natarajan et al. Visible light initiated thiol-ene based reflection H-PDLCs
WO2000062104A1 (fr) Systeme et procede de modulation de l&#39;intensite de la lumiere
Woltman et al. Survey of switchable lasing configurations using structures of liquid crystal and polymer dispersions
EP1257613B1 (fr) Liaison optique des guides d&#39;ondes d&#39;un element optique utilisant une composition photopolymerisable sensible au proche infrarouge
JP2004175949A (ja) 高分子／液晶ハイブリッド材料、その製造方法、光学素子、その製造方法および光学装置
CN115275753A (zh) 一种温度调谐的rgb胆甾相液晶激光器及其制备方法
Caputo et al. POLICRYPS: A multipurpose, application-oriented platform
Liu Tunable polymer/liquid crystal composite devices
JP2004198477A (ja) 光学素子及びその製造方法
Bunning et al. Effect of gel-point versus conversion on the real-time dynamics of holographic polymer-dispersed liquid crystal (HPDLC) formation

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 09778519

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 09778519

Country of ref document: EP

Kind code of ref document: A1