WO2010039606A2 - High elastic modulus polymer electrolytes suitable for preventing thermal runaway in lithium batteries - Google Patents

Abstract

A polymer that combines high ionic conductivity with the structural properties required for Li electrode stability is useful as a solid phase electrolyte for high energy density, high cycle life batteries that do not suffer from failures due to side reactions and dendrite growth on the Li electrodes, and other potential applications. The polymer electrolyte includes a linear block copolymer having a conductive linear polymer block with a molecular weight of at least 5000 Daltons, a structural linear polymer block with an elastic modulus in excess of 1 x 107 Pa and an ionic conductivity of at least 1 x 10-5 Scm-1. The electrolyte is made under dry conditions to achieve the noted characteristics. In another aspect, the electrolyte exhibits a conductivity drop when the temperature of electrolyte increases over a threshold temperature, thereby providing a shutoff mechanism for preventing thermal runaway in lithium battery cells.

Description

HIGH ELASTIC MODULUS POLYMER ELECTROLYTES SUITABLE FOR PREVENTING THERMAL RUNAWAY IN LITHIUM BATTERIES

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of U.S. Provisional Patent Application Ser.

No. 61/195,012, filed on October 1, 2008, titled HlGH ELASTIC MODULUS

POLYMER ELECTROLYTES SUITABLE FOR PREVENTING THERMAL

RUNAWAY IN LITHIUM BATTERIES, naming Mullin et al. as inventors, which is herein incorporated by reference for all purposes in its entirety. This application is related to the international application PCT/US2007/008435 filed on April 03, 2007, titled HIGH ELASTIC MODULUS POLYMER ELECTROLYTES; which claims priority to U.S. Provisional Patent Application No. 60/744,243 filed April 4, 2006, titled HIGH ELASTIC MODULUS POLYMER ELECTROLYTES; and to U.S.

Provisional Patent Application No. 60/820,331 filed July 25, 2006, titled SYNTHESIS OF DRY POLYMER ELECTROLYTES. The disclosures of applications listed above are incorporated herein by reference in their entirety and for all purposes.

STATEMENT OF GOVERNMENTAL SUPPORT

This invention was made with government support under Contract DE- AC02- 05CH 11231 awarded by the United States Department of Energy to The Regents of the University of California for the management and operation of the Lawrence Berkeley National Laboratory. The government has certain rights in this invention.

FIELD OF THE INVENTION

The invention relates to polymer electrolytes. More particularly, the invention relates to high elastic modulus, high ionic conductivity polymer electrolytes comprising linear block copolymers, and methods of making them. The invention further relates to methods for preventing thermal runaway in lithium batteries. BACKGROUND OF THE INVENTION

Polymer membranes with high ionic conductivity are important for applications such as solid-state batteries and fuel cells. The performance of these materials depends not only on their electrical properties but also on other properties such as shear modulus, permeability, and the like. The mechanical properties of polymer electrolytes are particularly important in secondary solid-state lithium (Li) batteries. One of the challenges in the field of rechargeable Li ion batteries is to combine high energy density with good cyclability and electrode stability. Batteries that employ Li metal anodes for high energy density applications suffer from failures due to side reactions and dendrite growth on the Li electrodes. Repeated cycling of the batteries causes roughening of the Li surface and eventually to dendrite formation, which reduces battery life and compromises safety.

Recent theoretical work indicates that dendrite growth can be stopped if the shear modulus of current polymer electrolytes can be increased by three orders of magnitude without a significant decrease in ionic conductivity. Other studies have shown that cation transport is intimately coupled to segmental motion of the polymer chains. These studies indicate that dendrite growth on the electrode surface can be prevented by introducing a highly rigid electrolyte (elastic modulus of about 1 GPa) between the two electrodes. This high modulus requirement essentially renders most rubbery polymer electrolytes incompatible with the electrode material, as the elastic moduli of typical rubbery polymers are about 1 MPa. For example, poly(ethylene oxide) (PEO) melt, one of the most studied polymer electrolytes, has an elastic modulus of less than 1 MPa. High ionic conductivity is obtained in soft polymers such as PEO because rapid segmental motion needed for ion transport also decreases the rigidity of the polymer. Glassy polymers such as polystyrene offer very high moduli (about 3 GPa) but are poor ion conductors. Thus, conductivity and high modulus have appeared to be almost mutually exclusive goals in polymer electrolytes.

There is, therefore, a need to develop a new methodology for decoupling the electrical and mechanical properties of polymer electrolyte materials. Such a material would be useful as a solid phase electrolyte for high energy density, high cycle life batteries that do not suffer from failures due to side reactions and dendrite growth on the Li electrodes. A separate problem encountered during operation of rechargeable lithium batteries is thermal runaway characterized by uncontrolled heating of the battery cell during operation (e.g., during charging). Such uncontrolled heating occurs because of a positive feedback which generally exists between cell temperature and conductivity of the electrolyte in a battery. As the temperature of the cell rises, the conductivity of electrolyte increases, leading to additional increase in cell temperature, leading, in turn, to an increase in electrolyte conductivity, and so on. When uncontrolled, this cycle can lead to overheating (thermal runaway) of the cell, which can cause melting of lithium metal and violent chemical reactions. Thermal runaway is a serious safety problem in lithium battery design, which is currently addressed by complex engineering solutions. Development of additional methods for preventing thermal runaway in rechargeable lithium batteries is desirable.

SUMMARY OF THE INVENTION

The present invention provides a polymer that combines high ionic conductivity with the structural properties required for Li electrode stability. The polymer is useful as a solid phase electrolyte for high energy density, high cycle life batteries that do not suffer from failures due to side reactions and dendrite growth on the Li electrodes, and other potential applications. In one aspect, the polymer electrolyte includes a linear block copolymer having a conductive linear polymer block with a molecular weight of at least 5000 Daltons, a structural linear polymer block with an elastic modulus in excess of 1 x 10⁷ Pa and an ionic conductivity of at least 1 x 10^"5 Son^"1. The electrolyte is made under dry conditions to achieve the noted characteristics. The electrolyte includes a lithium salt dissolved within the conductive linear block of the block copolymer.

In specific embodiments, the linear block copolymer is a diblock copolymer characterized by bicontinuous lamellar phases of the polymer block constituents. In some embodiments the structural polymer block can form a continuous rigid framework through which the conductive polymer block forms continuous nano structured ionically conductive channels. In one embodiment, the structural polymer block occupies at least 50%, e.g., at least 60% of block copolymer by volume, while the conductive block forms cylindrical nanostructure embedded within the rigid framework of the structural block. Notably, in some embodiments the structural block is a glassy polymer in a large temperature range (e.g., up to 90 ⁰C, or even up to 100 ⁰C). In some embodiments, the entire block copolymer is effectively glassy at least to a temperature of up to 70 ⁰C.

In one aspect, the invention relates to a polymer electrolyte. The electrolyte includes a linear block copolymer having a conductive polymer block with a molecular weight of at least 5000 Daltons, a structural polymer block with an elastic modulus in excess of 1 x 10⁷ Pa, and an ionic conductivity of at least 1 x 10^"5 Scm ¹.

In another aspect, the invention relates to a polymer electrolyte which is suitable for preventing thermal runaway in a lithium battery cell. It was unexpectedly discovered that conductivity of certain polymer electrolytes doped with lithium salts (specifically, block copolymers) decreases once the temperature increases above a threshold value. These polymer electrolytes may be suitable for preventing thermal runaway in lithium battery cells. Specifically, in some embodiments, the threshold temperature at which the conductivity drop occurs is between 90 ⁰C and 150 ⁰C, e.g., between 100 ⁰C and 120 ⁰C. In some embodiments the conductivity drop is at least 5- fold, preferably at least 10-fold. This conductivity drop is due to precipitation of the lithium salt in the block copolymer, which, unexpectedly occurs with temperature increase. Accordingly, in some aspects, a block-copolymer configured for dissolving a lithium salt at a first temperature and precipitating this salt at a higher temperature, wherein the precipitation is accompanied with a conductivity drop, is provided.

In another aspect, the invention relates to a method of making a polymer electrolyte. The method involves, in an oxygen and moisture free environment, forming a linear block copolymer having a conductive polymer block with a molecular weight of at least 5000 Daltons and a structural polymer block with an elastic modulus of at least 1 x 10⁷ Pa and incorporating a Li salt into the linear block copolymer such that the resulting polymer electrolyte has an ionic conductivity of at least 1 x 10^"5 Scm^"1.

In some embodiments, the method of making the polymer electrolyte further involves heating the block copolymer having the lithium salt dissolved therein in a casting and/or annealing process, to form the polymer electrolyte film. In some embodiments the casting and/or annealing is performed at a temperature, at which lithium salt does not precipitate. For example, for those block copolymers which exhibit salt precipitation with increase of temperature, the film may be heated at a temperature that is below the threshold temperature from the range of 90 ⁰C to 15O⁰C. The threshold temperature at which the salt precipitation occurs therefore, is an important parameter, which is considered for determining the optimal temperature range for copolymer film processing. In some embodiments, casting and/or annealing is performed at a temperature above the glass transition temperature of the structural block of the copolymer but below the threshold temperature at which salt precipitation occurs.

In a further aspect, the invention relates to battery cells comprising a Li anode, a cathode and linear block copolymer electrolyte in accordance with the invention disposed between the anode and cathode. The cell can be cycled without detrimental dendrite growth on the anode. In one embodiment, the battery cell includes a linear block copolymer electrolyte which exhibits a drop in conductivity once the temperature exceeds a threshold temperature. In some embodiments, the threshold temperature is in a range from 90 ⁰C to 150 ⁰C, and the conductivity drop is at least 2- fold, or at least 5-fold, and, preferably, at least 10-fold. Such polymer electrolytes can be used to prevent thermal runaway in a lithium metal battery.

In a further aspect, the invention relates to a method of operating a rechargeable lithium cell. The method involves providing a battery cell having a lithium anode, a cathode, and a solid block copolymer electrolyte having a lithium salt dissolved therein, wherein the block copolymer electrolyte is configured for precipitating the dissolved lithium salt with increase of temperature above a threshold temperature. The method includes charging and discharging the battery cell, with the cell being configured for cooling or reduced heating once the electrolyte reaches the threshold temperature. The cooling or reduced heating is due to conductivity drop in the electrolyte which is caused by lithium salt precipitation.

In a further aspect, the invention provides a method for screening block copolymer electrolytes for those which are suitable for preventing thermal runaway in a battery cell. The screening method involves providing a plurality of block copolymers, having a lithium salt dissolved therein; measuring dependence of conductivity versus temperature for at least some of the provided block copolymers; and, based on the obtained measurements, identifying the block copolymers which exhibit a drop in conductivity with increase of temperature above a threshold temperature. For example, block copolymers exhibiting a 5-fold, preferably 10-fold decrease in conductivity, after the temperature is increased above the threshold temperature from the range of between 90 ⁰C and 150 ⁰C, may be selected for use in battery cells configured for thermal runaway shutoff.

These and other aspects and advantages of the present invention are described below.

BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawings, which are incorporated into and constitute a part of this specification, illustrate one or more embodiments and, together with the detailed description, serve to explain principles and implementations of the invention.

In the drawings:

Fig. IA is an illustration of a block copolymer in accordance with the present invention in isolation, showing the linearity of the polymer block chains.

Fig. IB depicts the chemical structure of a polystyrene-b-poly(ethylene oxide) (PS-b-PEO, also referred to as SEO) diblock in accordance with one embodiment of the present invention.

Figs. 2A-C illustrate embodiments of a PS-b-PEO diblock.

Fig. 3 is a graph illustrating Small Angle X-ray Scattering (SAXS) profiles obtained from SEO/salt and SIEO/salt mixtures in accordance with the present invention.

Fig. 4A is a graph illustrating the dependence of ionic conductivity on r (Li salt per EO unit) and temperature in SEO (36-25), a block copolymer electrolyte in accordance with the present invention.

Fig. 4B is a graph illustrating the dependence of ionic conductivity on r (Li salt per EO unit) in SEO (74-98), a block copolymer electrolyte in accordance with the present invention. Figs. 5A-5C are plots illustrating the dependence of ionic conductivity of block copolymer electrolytes in accordance with the present invention on the molecular weight of their respective PEO blocks.

Fig. 6 is a graph illustrating the frequency dependence of the storage and loss shear moduli of SEO(36-25), a block copolymer electrolyte in accordance with the present invention, with and without salt, and PEO.

Fig. 7 is a graph illustrating the frequency dependence of elastic moduli for the series of copolymers referenced in Fig. 3.

Fig. 8 is a plot of the results of DC cycling of a Li/SEO/Li cell with an electrolyte in accordance with the present invention.

Fig. 9A is a bright field electron micrograph of a block copolymer in accordance with the present invention.

Fig. 9B is a lithium energy filtered electron micrograph of the same block copolymer region as Fig. 9 A.

Fig. 10 presents data showing lamellae thicknesses for block copolymers in accordance with the present invention obtained from various measurements.

Fig. 11 is a plot of Li lamellae thickness normalized by the PEO lamellae thickness as a function of molecular weight.

Fig. 12 is a plot comparing the normalized Li lamellae thickness and normalized conductivity versus molecular weight for various block copolymers in accordance with the present invention.

Fig. 13 is a simple schematic diagram of a battery cell in accordance with the present invention.

Fig. 14 is a plot illustrating the dependence of conductivity on inverse temperature for a SEO (54-23) block copolymer. A drop in conductivity above a threshold temperature is illustrated. Fig. 15 is a SAXS plot illustrating precipitation of lithium salt in a SEO (54- 23) block copolymer with increase in temperature.

DETAILED DESCRIPTION OF SPECIFIC EMBODIMENTS

Reference will now be made in detail to specific embodiments of the invention. Examples of the specific embodiments are illustrated in the accompanying drawings. While the invention will be described in conjunction with these specific embodiments, it will be understood that it is not intended to limit the invention to such specific embodiments. On the contrary, it is intended to cover alternatives, modifications, and equivalents as may be included within the spirit and scope of the invention as defined by the appended claims. In the following description, numerous specific details are set forth in order to provide a thorough understanding of the present invention. The present invention may be practiced without some or all of these specific details. In other instances, well known process operations have not been described in detail in order to not unnecessarily obscure the present invention.

It will, of course, be appreciated that in the development of any actual implementation of the invention, numerous implementation- specific decisions must be made in order to achieve the developer's specific goals, such as compliance with application- and business-related constraints, and that these specific goals will vary from one implementation to another and from one developer to another. Moreover, it will be appreciated that such a development effort might be complex and time- consuming, but would nevertheless be a routine undertaking of engineering for those of ordinary skill in the art having the benefit of this disclosure.

INTRODUCTION

As noted above, in one aspect, the present invention provides a polymer that combines high ionic conductivity with the structural properties required for Li electrode stability. The polymer is useful as a solid phase electrolyte for high energy density, high cycle life batteries that do not suffer from failures due to side reactions and dendrite growth on the Li electrodes, and other potential applications. The polymer electrolyte includes a linear block copolymer having a conductive linear polymer block with a molecular weight of at least 5000 Daltons, a structural linear polymer block with an elastic modulus in excess of 1 x 10⁷ Pa and an ionic conductivity of at least 1 x 10^~5 Son^"1. In some embodiments, the block copolymer has an elastic modulus of greater than 100 MPa, e.g., 300 - 700 MPa. The electrolyte is made under dry conditions to achieve the noted characteristics.

In specific embodiments, the linear block copolymer is a diblock copolymer characterized by bicontinuous lamellar phases of the polymer block constituents, and the structural polymer block can form a rigid framework in which the conductive polymer block forms nanostructured ionically conductive channels. In other embodiments, the conductive block forms a cylindrical nanostructure within the rigid framework formed by the structural block.

LINEAR BLOCK COPOLYMERS

A linear block copolymer can be used to produce a polymer electrolyte that can combine high ionic conductivity with the structural properties required for Li metal electrode stability. The electrolyte is useful as a solid phase electrolyte for high energy density, high cycle life batteries that do not suffer from failures due to side reactions and dendrite growth on the Li electrodes. The linear block copolymer may be a composite polymer electrolyte having relatively soft (e.g., having an elastic modulus on the order of 1 MPa or less) nanoscale conducting channels embedded in a relatively hard (e.g., having an elastic modulus on the order of 1 x 10⁷ Pa or more) polymer matrix that need not be ionically conductive. The resulting block copolymer preferably has an elastic modulus of at least 100 MPa, e.g., 300 - 700 MPa. Ionic conductivity in the channels is conferred by a Li salt incorporated with the soft polymer block. It has been found that particular configurations and fabrications of such linear block copolymers enable the combination of high ionic conductivity and high elastic modulus in a polymer electrolyte.

While prior work in the field has suggested block copolymers as suitable materials for electrolytes, these prior block copolymers were composed of relatively soft (non-glassy) polymer blocks that were modified with various side chains.

The electrolytes of the present invention, however, comprise block copolymers with linear polymer block constituents, one of which is soft and conductive to Li ions; another of which is hard and need not be ionically conductive. Fig. IA provides an illustration of such a copolymer in isolation, showing the linearity of the polymer block chains.

The inventive polymer electrolytes, in one aspect, include a linear block copolymer having a conductive linear polymer block with a molecular weight of at least 5000 Daltons, a structural linear polymer block with an elastic modulus in excess of 1 x 10⁷ Pa and an ionic conductivity of at least 1 x 10^"5 Son^"1. The polymer, in some embodiments, is non-crosslinked. Remarkably, even without crosslinking high elastic modulus values of at least 100 MPa are achieved, due to rigidity of the structural block. In other embodiments, the structural block of the copolymer is cross- linked, while the conductive block remains non-crosslinked.

In a specific embodiment, the copolymer is a linear diblock copolymer of poly(ethylene oxide) (a rubbery, linear polymer, highly ionically conductive when embedded with an appropriate Li salt) with polystyrene (a non-conductive, glassy, linear polymer); a polystyrene-b-poly(ethylene oxide) (PS-b-PEO) diblock, the chemical structure of which, is illustrated in Fig. IB. Notably, both polystyrene (PS) and polyethyleneoxide (PEO) blocks are linear and are covalently connected with one another without forming branches. This combination has been found to provide both the high ionic conductivity and high rigidity sought after for high performance solid state polymer electrolytes. It is understood that the SEO polymer can have a variety of terminating groups instead of illustrated sec-Butyl group at the polystyrene terminus and OH at the PEO terminus. For example, a variety of alkyl groups can be introduced at the polystyrene terminus (such as methyl, ethyl, propyl, z-prpoyl, n- butyl, etc.). The PEO terminus, in some embodiments, contains an alkoxy terminal group (such as methoxy, ethoxy, propoxy group, etc.). In some embodiments alkoxy- terminated polymers are preferable over hydroxy- terminated polymers, due to the lower reactivity of the former.

Figs. 2A-C illustrate embodiments of a PS-b-PEO diblock in accordance with the invention. The PS-b-PEO diblock, generally numbered 10, exhibits an extensive phase behavior, which allows for bicontinuous phases. In these embodiments, in the bicontinuous PS-b-PEO phases, the major (e.g., greater than 50%) phase (PS) 12 provides a rigid framework for the nanostructured ionically conducting channels (PEO) 14. Figs. 2A-C illustrate the shape and placement of polymer blocks comprising conceptual diblocks in accordance with the present invention, and are not meant to be limiting. It will be known and understood that the micro structure of the diblock may be in any shape that is necessary and the placement of the polymers within the diblock may vary as needed. As schematically illustrated in the Fig. 2A, the cylindrical PEO channels 14 may be positioned in an orderly placement within the PS matrix 12. The nanostructure, shown in Figure 2A is referred to as cylindrical nano structure. Alternatively, as illustrated in Fig. 2B, the PEO channels 14 may be branched, such as in a gyroid phase, within the PS matrix 12. Fig. 2C illustrates another specific embodiment in which the PEO channels 18 are layered in a lamellar arrangement with the PS matrix 16. While it has previously been believed that network morphologies are essential for ion transport, it was surprisingly found that diblock copolymers in accordance with the present invention with such non-network lamellar morphologies are very effective ion transporters.

In many instances, the diblock copolymer has a non-conducting phase that is continuous, and, in most cases, the major component, which differs from previously proposed block copolymer electrolytes. The mechanical properties of such block copolymer electrolytes are dominated by those of the non-conducting component. This enables independent control over the electrical and mechanical properties of the electrolyte. The structural linear polymer block major phase forms a rigid framework, with the conductive polymer block forming nanostructured ionically conductive channels through the rigid framework.

In specific embodiments, the linear block copolymer is a diblock copolymer and may be characterized by bicontinuous phases of the polymer block constituents such that there are continuous ionically-conductive channels (or pathways) through a continuous rigid framework. In this way, the beneficial properties of both polymer block materials (structural and conductive) exist throughout the material. Block copolymers are known in the art to self-assemble into a variety of structures or arrangements. As noted above, a particular arrangement for diblock copolymers in accordance with the present invention with advantageous properties is lamellar, although other arrangements are possible. An important feature of the block copolymers is the combination of soft and hard polymer blocks to form a rigid material that is also highly ionically conductive. Thus, the structural polymer block has an elastic modulus of at least 1 x 10⁷ Pa, and generally from about 1 x 10⁷ Pa to 3 GPa. A suitable polymer for the structural block is polystyrene, a glassy polymer with an elastic modulus of about 3 GPa. Other mechanisms for obtaining suitable rigid frameworks include cross-linking and crystallization of structural blocks. The ionically conductive polymer, on the other hand, typically has an elastic modulus of no more than 1 MPa; poly(ethylene oxide), a specific material for which advantageous properties have been found in block polymers of the present invention, has an elastic modulus of less than 1 MPa. The resulting block copolymer in some embodiments has an elastic modulus of at least 100 MPa. Further, the resulting block-copolymer, in some embodiments, is glassy at a relatively large temperature range (e.g., up to 70 ⁰C, and even up to 90 ⁰C).

Other examples of polymers suitable as conductive or structural polymers for these block copolymer electrolytes include poly vinyl pyrrolidine (conductive), poly acrylates (conductive), polyvinylcyclohexane (structural), epoxies (structural), and polypropylene (structural).

As noted above, the conductive polymer block chains of the block copolymer have a molecular weight of at least 5000 Daltons. This is notable since prior work in the field has indicated an inverse relationship between the molecular weight of conductive polymers and their ionic conductivity. To the contrary, it has been found that the ionic conductivity of the block copolymers of the present invention increases with increasing molecular weight of the constituent polymer blocks. Accordingly, in various embodiments, the structural polymer has a molecular weight of at least 5000 Daltons. Further, in various embodiments, the ionic conductivity of the block copolymer increases with increasing molecular weight of the conductive polymer block, so the conductive and structural polymer block chains have molecular weights of at least 15,000 Daltons; or at least 20,000 Daltons; or at least 50,000 Daltons; or up to about 100,000 Daltons or more. In some embodiments, the molecular weight of the structural block is at least 200,000, e.g., or at least 300,000. Ionic conductivity of greater than 1 x 10^"4 Scm ¹ and up to about 1 x 10^"3 Scm ¹ has been achieved with these relatively high molecular weight block copolymers in accordance with the present invention.

As noted above, ionic conductivity is achieved for the conductive polymer block by incorporating an appropriate Li salt into the conductive polymer block. It is important that incorporation of the Li salt be done in a controlled environment and under conditions selected to achieve the desired performance in the resulting polymer electrolyte product. This is discussed further below. Suitable Li salts include lithium bis (pentafluoroethane sulfonyl) imide, lithium bis[l,2-oxalato(2-)-O,O ]borate (LiBOB), and lithium bis(trifluoromethane sulfonyl) imide (LiN[SO₂CFs]₂, also known as LiTFSI) LiClO₄, LiPF₆, LiAsF₆, LiSO₂CF₃ (also known as lithium triflate), and others known in the art. One specific salt is LiN[SO₂CF₃]₂ (also known as LiTFSI). Self-assembly of the conductive polymer block results in ionically conductive channels in the rigid structural polymer block framework. The salts and the polymers are selected such that the lithium salt is capable of dissolving within the conductive portion of the block copolymer. For example LiTFSI has a solubility limit of 56 wt % in PEO. The concentration of lithium salt within the block copolymer is also given by a ratio of molar concentration of lithium ion per molar concentration of conductive block monomer unit. For example, for SEO block copolymers, the concentration of lithium salt is given by r = [Li]/[EO], where EO is ethylene oxide monomer unit. In some embodiments r ranges from 0.02 to 0.12, e.g., from 0.05 to 0.1.

Further, as also described below, it has been found that the enhanced ionic conductivity obtained with increasing molecular weight of the conductive polymer block is correlated with a concentration of Li salt in a central portion of the ionically conductive channels in the block copolymer electrolytes.

While many specific embodiments of the invention exhibit a diblock copolymer structure, other structures are also possible. For example, an additional polymer block may be added to adjust the properties of the resulting copolymer, in this case a triblock copolymer. One suitable triblock copolymer is a polystyrene- block-polyisoprene-block poly(ethylene oxide) (S-I-EO) triblock copolymer. For example, a S-I-EO triblock copolymer with molecular weights of 11,000 Daltons for the polystyrene block, 6000 Daltons for the polyisoprene block, and 9000 Daltons for the poly(ethylene oxide) block was found to have a measured conductivity range from 4xlO^~4 Scm ¹ to 9xlO^~4 Scm ¹ in the 90-120⁰C temperature range, for a molar ratio of Li ions to ethylene oxide, r=0.02.

In a separate aspect, solid polymer electrolytes which exhibit a conductivity drop upon increase of temperature above a threshold temperature value are provided.

This intrinsic property of certain polymer electrolytes can be used to prevent thermal runaway in lithium battery cells. The term "prevent", as used herein, means "to decrease the probability of thermal runaway failure in a battery cell", and is not intended to mean that the described polymers entirely eliminate the possibility of thermal runaway under all conditions.

It was unexpectedly discovered that certain Li salt doped block copolymers, such as linear block copolymers described above, exhibit a drop in conductivity when the temperature of polymer electrolyte increases above a threshold value. The conductivity drop was found to be caused by precipitation of dissolved lithium salt, which occurs above a threshold temperature. This behavior is entirely unexpected, because it is typical for the conductivity of salt-doped polymers to increase with the temperature increase. For example, conductivity of Li salt doped PEO polymer increases with increasing temperature, without exhibiting a drop, and without any indication of lithium salt precipitation with temperature increase. Remarkably, in block copolymers described herein, the conductivity increases until a threshold temperature value which lies in a range of between 90 ⁰C and 150 ⁰C, and starts to drop after the threshold temperature value has been reached. In some embodiments conductivity drop is at least 2-fold, or at least 5-fold, or even at least 10-fold. For example, the conductivity can increase until a threshold temperature of 110 ⁰C is reached. Above this temperature, the conductivity can drop by an order of magnitude because of salt precipitation. The conductivity drop typically occurs at least within 30 minutes of exceeding the threshold temperature.

A number of block copolymers described above were found to exhibit this interesting and valuable property. While it is preferable to use copolymers having improved structural properties as described in the previous sections, the conductivity drop is considered to be an intrinsic property of certain block copolymer systems, and is not limited to block copolymers having high elastic modulus. While many of the copolymers described above exhibit the conductivity drop, it is particularly pronounced in copolymers having cylindrical nanostructure morphology (such as illustrated in Figure 2A). At least some lamellar samples also exhibit the drop, but sometimes to a lesser degree. The drop is also particularly pronounced in block copolymers having a volume fraction of conductive block in the range of 0.2 - 0.6, more preferably, of 0.2 - 0.5, such as 0.25 - 0.35. Further, the conductivity drop, in some embodiments, was found to be pronounced in relatively high molecular weight block copolymers, e.g., in block copolymers having molecular weight of greater than 200 kg/mol, and even greater than 300 kg/mol. For example, SEO samples SEO (54-23), SEO (216-102), and SEO (360-165) having cylindrical ordered nanostructure and having volume fraction of conductive EO phase 0.28, 0.3, and 0.3 respectively, all exhibited a conductivity drop of at least 2-fold (e.g., a 10-fold drop) upon reaching a threshold temperature in a range of 90-120 ⁰C. In SEO (54 - 23), the first value (54) refers to a molecular weight of polystyrene structural block, while the second value (23) refers to molecular weight of conductive PEO block, where both values are given in kg/mol. Other polymer samples are labeled using an analogous scheme.

In one aspect, a method of screening block copolymers for a block copolymer electrolyte suitable for preventing thermal runaway in a cell, is provided. The method involves providing a plurality of block copolymers doped with a lithium salt (such as LiTFSI or other salt mentioned above), and measuring the conductivity dependence of the formed solid electrolyte versus temperature. The measurements will preferably, include at least a portion of the 90 ⁰C- 150 ⁰C temperature range. For example conductivity dependence can be measured in a range from 25 ⁰C to 150 ⁰C. The plurality of block copolymers can include any block copolymer without limitation, but, in some embodiments, includes only linear block copolymers having linear conductive and structural phases, such as polymers described above. Further, preferably, but not necessarily, all block copolymers used for screening should have good structural properties, such as high elastic modulus, e.g., a modulus of greater than 100 MPa. The measurement of conductivity vs. temperature dependence is performed individually for each polymer and can be performed either serially or in parallel. Such measurements can be performed, for example, using ac impedance spectroscopy on a Solartron 1260 frequency response analyzer available from Solartron Analytical of Farnborough, UK.

Based on the results of this measurement, copolymers exhibiting a conductivity drop at a threshold temperature are identified, and are selected as candidates for solid polymer electrolytes suitable for thermal shutoff of a Li battery cell. In some embodiments, copolymers exhibiting at least a 2-fold conductivity drop, or at least a 5-fold conductivity drop, or at least a 10-fold conductivity drop are selected. Further, preferably, polymers having high conductivity (e.g., at least 1 x 10^"5

Scm^"1 prior to the conductivity drop) and good structural properties (as previously described) are selected. In some embodiments only polymers having high conductivity and good structural properties are screened.

Table 1 illustrates linear SEO block copolymers which were screened for conductivity drop by measuring the dependence of conductivity on temperature. The conductivities were measured during heating from 25 to 120 ⁰C. The samples contained LiTFSI salt, which was obtained from Acros Organics (catalog no. 381030100). Of the 13 samples that were screened, five samples exhibited conductivity drops greater than about 2-fold. "About" as used herein refers to a range which includes +0.5 interval around the recited value. The molecular weights for PS and PEO fraction, a volume fraction of EO in the polymer, and the conductivity drop data are shown in Table 1.

Table 1. Block copolymers screened for conductivity drop

Of the polymers listed in Table 1, SEO9, SEO15, and SEO16 had a cylindrical morphology. The remaining polymers which showed a conductivity drop had a lamellar morphology.

An alternative method for identifying polymers that are suitable for preventing thermal runaway in batteries involves screening salt-doped polymers for evidence of salt precipitation occurring with temperature increase. In one embodiment, a plurality of salt-doped polymers are screened using SAXS. A SAXS profile for each polymer is measured at several temperatures, starting at lower temperature, and up to e.g., 120- 150 ⁰C. Precipitation of salt (which correlates with conductivity drop) manifests itself in a SAXS profile by increase of intensity in low-q scattering. The samples which exhibit increase in low-q scattering with increase of temperature are identified as candidate polymers for preventing thermal runaway in lithium batteries.

In another embodiment screening for salt precipitation is performed by measuring light scattering of a plurality of samples. Salt precipitation manifests itself by an increase in light scattering. Similarly to the SAXS-based screening method described above, a plurality of salt-doped polymers are subjected to light scattering measurement. Light scattering for each polymer sample is recorded at several temperatures, typically starting at lower temperature, and increasing the temperature to, e.g., 120 - 150 ⁰C. Those polymers which exhibit increase in light scattering after the temperature reaches a threshold value, are then selected.

ELECTROLYTE FABRICATION

In one aspect, a method of making a polymer electrolyte in accordance with the present invention comprises, in an oxygen and moisture free environment, forming a linear block copolymer having a Li ion conductive linear polymer block with a molecular weight of at least 5000 Daltons and a structural linear polymer block with an elastic modulus of at least 1 x 10⁷ Pa; and incorporating a Li salt into the linear block copolymer, such that the resulting polymer electrolyte has an ionic conductivity of at least 1 x 10^~5 Son^"1. Care must be taken in the manufacture of the linear block copolymer electrolytes to prevent adverse reaction of the Li salt and to obtain the polymer product with the advantageous performance noted herein.

A block copolymer electrolyte in accordance with the present invention can be made by synthesizing the structural polymer block by living anionic polymerization.

Then, a monomer of the conductive polymer block and a cryptand catalyst are added to the structural polymer block living anionic polymerization mixture. The polymerization of the conductive block is then allowed to proceed. The reaction may proceed to completion and, after it is terminated with a suitable reagent, the resulting diblock copolymer product is precipitated and freeze-dried. Other living polymerization methods like cationic and radical polymerization techniques can also be used to synthesize the block copolymers.

To render the copolymer conductive to Li ions, a Li salt is blended with the freeze-dried diblock copolymer using a moisture-free solvent such that the Li salt is dissolved with the conductive polymer block. The resulting polymer/salt solution is then freeze dried to remove the solvent. The freeze-dried dry polymer/salt mixture can then be subjected to heat and pressure (compression molded) to form a freestanding polymer electrolyte film.

A detailed description of a method of making a linear diblock copolymer as applied to a specific embodiment follows. The following example will be described using SEO; however, it will now be realized that other materials and preparation methods may be used. As such, the following example is discussed for exemplary purposes only and is not intended to be limiting.

Synthesis ofPS-b-PEO

In an exemplary embodiment of the invention, the diblock copolymer, polystyrene-b-poly(ethylene oxide) (SEO) is synthesized using living anionic polymerization to attain good control of the molecular weight and achieve low polydispersity. All of the synthetic steps are performed on a high-vacuum line and inside an argon glove box to ensure an oxygen and moisture free environment. The first step is to purify the solvent, benzene, over calcium hydride for at least 12 hours at room temperature. Benzene is then distilled onto a sec-butyllithium stage for further purification.

The next step is purification of the styrene monomer, and synthesis of polystyrene. The styrene monomer is purified on calcium hydride (CaH₂) by stirring for a few hours to remove trace amounts of water. The monomer is then distilled into a flask (e.g., short- neck round-bottom flask) containing dibutyl magnesium (DBM). The monomer is stirred over DBM overnight. A clean reactor, in which polymerization will take place, is placed on the high-vacuum line and flamed with a torch to remove adsorbed water and solvent. After flaming, about 20 mL of the purified solvent is distilled from the sec-butyllithium stage into the clean reactor. This is done to prevent freezing and degassing a large amount of solvent. After the addition of 20 mL of benzene, the reactor is taken off the vacuum line, and into the glove box at which point the calculated amount of sec-butyllithium initiator required for reaction is pipetted into the reactor.

A very good seal is maintained during transfer back onto the vacuum line. After the reactor is placed back on the line, the mixture is frozen with liquid nitrogen and degassed 1, 2, 3, 4, or 5 times to remove trapped argon from the vessel and promote fast distillation. The remainder of the solvent can then be distilled into the reactor. In one arrangement, enough solvent is added to yield a mixture of approximately 8-10 wt% polymer in solution.

The first block, polystyrene (seen as 12 in Figures 2A-B, and 16 in Figure 2C) is synthesized by distilling a calculated amount of styrene from the DBM stage into a graduated ampoule and then into the reacting vessel, which contains benzene and the sec-butyllithium initiator. The reaction is carried out at room temperature for approximately 12 hours and a characteristic yellow "living" polymer mixture is obtained upon completion. The mixture is stirred continuously during the reaction to ensure uniform mixing of the monomer. The reactor is then taken into the glove box and an aliquot is taken out and terminated with degassed methanol or isopropanol for characterization using gel permeation chromatography to determine its molecular weight. This completes the synthesis of the first block, ready for the addition of the ethylene oxide (EO) block. A flask (e.g., short-neck round-bottom flask) with freshly powdered calcium hydride is placed on the vacuum line and opened up to vacuum to remove all air. The flask is maintained at 0⁰C. Ethylene oxide monomer, a gas at room temperature (b.p. 10⁰C) is condensed onto the calcium hydride at 0⁰C and left to stir overnight to remove residual moisture. The monomer-containing flask is maintained at a dry ice/ IPA mixture temperature. The ethylene oxide is kept cold at all times during purification. The ethylene oxide/calcium hydride mixture is frozen and degassed twice before the purification steps.

The monomer is purified with two stages of n-butyllithium by stirring for 30 minutes at 0⁰C at each stage. 1OmL of n-butyllithium in cyclohexane is used for each stage. The purifying agent, n-butyllithium, is completely dried by pulling vacuum to get rid of the cyclohexane solvent in which the n-butyllithium is dissolved. This can prevent contamination and ensures an accurate measurement of the amount of ethylene oxide (EO) monomer. The ethylene oxide monomer is distilled into a graduated ampoule maintained at 0⁰C after purifying at both stages of n-butyllithium.

Following purification and distillation into a graduated ampoule, 1 ml of the EO monomer is distilled into the living polystyrene reactor for addition of a single EO unit. Only one EO unit is added to the living polystyrene chain because of the strong complexation of the lithium cation to the oxygen in the ethylene oxide unit. The Li cation shows a strong association with the ethylene oxide unit and, thus, no propagation reaction can occur. To polymerize the second block, a cryptand catalyst (e.g., tert-butyl phosphazene base l-fert-Butyl-4,4,4-tris(dimethylamino)-2,2- bis[tris(dimethylamino)-phosphoranylidenamino]-2Λ⁵,4Λ⁵-catenadi(phosphazene) (^Bu-P₄), available from Aldrich. Milwaukee, WI) is added to the reaction mixture (containing living EO capped polystyrene chains) to complex the lithium ions and facilitate the polymerization of ethylene oxide. To prepare the catalyst base, the solvent in which it is dissolved is removed and a known amount of benzene distilled into the flask. This solution can then be pipetted into the reactor in the glovebox. The reactor is then reattached to the high- vacuum line and degassed 1, 2, 3, 4, or 5 times to remove trapped argon from the vessel and promote fast distillation. The remainder of the EO is then distilled from the graduated ampoule into the reactor. The reaction is allowed to proceed for three to four days at 45°C during which time the color changes to a dark blue. The diblock copolymer (SEO) is then terminated with methanol in the glove box and purified by precipitation in cold hexane. In those instances, when alkoxy-terminated polymer is desired, the reaction is quenched with an alkylating agent, such as alkyl iodide (e.g., methyl iodide). The precipitated polymer is dissolved in benzene and filtered through a 0.2 μm filter. The filtered polymer is then freeze dried to remove all solvent. The freeze-dried polymer is characterized by gel permeation chromatography (GPC) to determine the molecular weight and by nuclear magnetic resonance (NMR) to calculate the volume fraction of each block.

Electrolyte Preparation

Polymer electrolytes are prepared by blending the freeze-dried SEO copolymers with the lithium salt, LiN[SO₂CFs]₂ (LiTFSI, available from Aldrich) in a moisture free environment. This is achieved in a few steps. A LiTFSI/THF solution (about 10% w/w) is prepared in the glove box, and stored as a stock solution. All the copolymer samples are weighed and vacuum dried in a heated antechamber and brought into the glove box. The dry copolymer samples are then dissolved in dry benzene. To this copolymer/benzene solution, the necessary amount of the LiTFSI stock solution is added in the argon glove box. All solvents used in the electrolyte preparation are doubly-distilled to remove trace amounts of moisture. The polymer/salt solution is then freeze-dried in a glove box compatible desiccator for one week to remove all solvent. The freeze-dried polymer/salt mixture is loosely packed into a pellet in a die that has a diameter slightly less than the spacer inner diameter. The pellet is placed in a Teflon™ bag along with a spacer, such that the pellet is in the center of the spacer's slot. The spacer is made of a non-conducting reinforced resin, and can withstand high pressure and temperature without deforming. The pellet is then subjected to a high pressure (about 1 kpsi) at about 100⁰C. This yields a clear, freestanding polymer electrolyte film with the spacer around it. The spacer defines the edge and the thickness (and hence the area, and the volume) of the freestanding polymer electrolyte film, and provides a means for easy transfer in and out of the membrane-electrode assembly. All the steps are carried out in the glove box. In a separate aspect, a method of making block copolymers is adjusted such that during preparation, the block copolymer with an embedded salt is not exposed to a temperature that is higher than the threshold temperature for lithium salt precipitation. This adjustment is made for those polymers which exhibit conductivity drop above a threshold temperature due to salt precipitation. Therefore, in these embodiments after the polymer/salt mixture is made and is freeze-dried, the freeze- dried pellet is subjected to high temperature and pressure to form a freestanding polymer electrolyte film, where the temperature of the anneal is adjusted to be below the threshold temperature at which lithium salt precipitation occurs. Depending on a particular polymer and the threshold temperature, the anneal is performed below 150 ⁰C, or below 110 ⁰C. In some embodiments, due to these considerations, a relatively narrow temperature range for anneal is found to be preferable, such as 80 - 120 ⁰C, or 100 - 110 ⁰C. When annealing is performed above the threshold temperature for lithium salt precipitation, due to precipitation of the salt, the conductivity of polymer electrolyte substantially drops. When annealing is performed at too low a temperature, the film cannot always properly form to have the desired nanostructure. In some embodiments the temperature for annealing and/or casting is selected such that it is greater than the glass transition temperature of the structural block material of the copolymer but is lower than the threshold salt precipitation temperature. One of skill in the art will understand how to select a temperature range for annealing a polymer electrolyte sample, given these guidelines.

In a separate, but related aspect, the method of making the polymer electrolyte film involves casting the polymer at high temperature. In this case, instead of freeze- drying, evaporation of the solvent from the solution of the polymer and the salt dissolved in a solvent, is performed. Upon evaporation, the polymer is heated and is casted such that it adopts a shape needed for the electrolyte film. Similarly to the previous example, in those embodiments where the polymer electrolyte precipitates the lithium salt above a threshold temperature, the process is adjusted such that casting and/or evaporation of the solvent is performed below the threshold temperature of salt precipitation. In some embodiments, these considerations provide a relatively narrow temperature window for the casting and/or evaporation process. Specifically, many copolymers described herein can be cast only above 90 - 100 ⁰C (or their corresponding Tg temperature), as they are too hard and glassy at lower temperatures. However, above the threshold temperature for lithium salt precipitation, the polymer loses a lot of its conductivity. Therefore, casting is performed at a temperature range at which the polymer is sufficiently soft for casting and at which salt precipitation does not occur. In some embodiments, this temperature range is between 90 - 110 ⁰C

STRUCTURE AND PERFORMANCE

While the invention is not limited by any particular theory, it is believed that the high elastic modulus, high ionic conductivity block copolymers of the present invention are correlated with a particular morphology. It has been found that for at least some specific embodiments of the invention with advantageous properties, the bicontinuous phases of the polymer block constituents of the diblock copolymer have a lamellar arrangement and that the Li salt segregates itself to the ionically conductive block channels. In addition, with increasing molecular weight of the polymer block constituents, the Li salt increasingly concentrates itself to a central portion of the ionically conductive block channels and ionic conductivity increases.

Further, block copolymers having cylindrical morphology were also found to be suitable in terms of conductivity and structural properties. Further, the conductivity drop is often more pronounced in samples having cylindrical morphology, which makes them attractive as polymer electrolytes having an intrinsic property of preventing thermal runaway in lithium battery cells.

As described further below with reference to Fig. 8, the linear block copolymer electrolytes of the present invention exhibit good cycling performance. No dendrite formation was observed for 80 cycles in DC Li/polymer/Li test cells.

EXAMPLES

The following examples provide details relating to composition, fabrication and performance characteristics of block copolymer electrolytes in accordance with the present invention. It should be understood the following is representative only, and that the invention is not limited by the detail set forth in these examples. To characterize the electrolyte, experimental data results were obtained by methods such as transmission electron microscopy (TEM), small angle X-ray scattering (SAXS), AC impedance spectroscopy, and rheology. AC impedance spectroscopy measurements were made using a test cell on thermo-stated pressed 5 samples in the glove box, and a Solartron 1260 Frequency Response Analyzer machine connected to a Solartron 1296 Dielectric Interface. The polymer samples for TEM and SAXS were annealed using the same thermal history as that used for conductivity measurements. The electrolyte samples were kept at 120⁰C for 2 hrs, and cooled to room temperature. Thin sections (about 50 nm) were prepared using an

10 RMC Boeckeler PT XL Cryo-Ultramicrotome operating at -100⁰C. Imaging was done on a Zeiss LIBRA 200FE microscope operating at 200 kV. SAXS measurements were made on hermetically sealed samples. The data were collected for various temperatures between 140⁰C and room temperature during cooling. Rheological measurements were performed using an ARES rheometer from

15 Rheometric Scientific Inc. with a parallel-plate geometry. Approximately 1 mm thick samples were placed between 8 mm plates for SEO, and 50 mm plates for PEO, in a closed oven with a Nitrogen (N₂) atmosphere. The ratio of Li ions to ethylene oxide moieties, r, in the electrolyte was varied from 0.02 to 0.10. Unless otherwise noted, due to the lack of qualitative changes in properties with salt concentration, data was

20 obtained at r=0.02. Alternating current (AC) impedance and rheological data, obtained from mixtures of a 20 kg/mol PEO homopolymer and Li[N(SOiCFs)₂], serve as the baseline for evaluating the properties of the composite electrolyte.

Table 2 lists the characteristics of the different kinds of copolymers that will be discussed:

Table 2 Two different block polymer types were utilized to obtain the experimental data. The first is polystyrene-b/ocfc-poly(ethylene oxide) diblock copolymers (SEO) doped with lithium bis(trifluoromethylsulfonyl)imide, Li[N(SO₂CFs)₂]. The PS-rich phase provides mechanical rigidity, while the PEO phase provides ionic conductivity. The second is a polystyrene-b/ocfc-polyisoprene-b/ocfc-poly(ethylene oxide) triblock copolymer (SIEO). The presence of the polyisoprene rubbery domains is known to increase the impact strength of polystyrene.

FIG. 3 is a graph illustrating SAXS profiles obtained from SEO/salt and SIEO/salt mixtures. The SAXS data were obtained from SEO/salt and SIEO/salt mixtures with r=0.02 and at a temperature of 90⁰C. For clarification, SIEO (11-6-9) (marked A) has a ratio of polystyrene-polyisoprene-poly(ethylene oxide) of 11-6-9. SAXS data obtained from pure SEO and SIEO samples were indistinguishable from the data shown in Fig. 3. The long range order, as gauged by the sharpness of the primary and higher order peaks, is better in low molecular weight samples than in the high molecular weight samples. This is expected due to the slow diffusion in strongly segregated block copolymers.

The SAXS profiles of SEO(36-25) (marked C) are similar to perforated lamellar phases, while those from the other samples show the presence of a lamellar phase. TEM images of SEO(36-25) (not shown for brevity) indicate that the PEO lamellae appear dark and perforated, while the PS lamellae show no evidence of perforations, in agreement with the SAXS data shown in Fig. 3. Based on the similarity in the SAXS profiles obtained with and without salt, the addition of salt at low concentrations to the SEO copolymer may not affect the morphology. The TEM and SAXS data indicate the absence of an interpenetrating network phase in the block copolymer electrolytes.

Fig. 4A is a graph illustrating the dependence of ionic conductivity on r and temperature, respectively, in SEO(36-25). Figure 4B illustrates the dependence of ionic conductivity on r at 100 ⁰C in SEO(74-98). Fig. 4B illustrates that the conductivity has a maximum at r ⁵^ 0.06 - 0.09. This trend is similar to that observed in PEO-salt homopolymer-based systems. At low salt concentrations, ionic conductivity increases with salt concentration due to the increase in the number of charge carriers. At high salt concentrations, transient cross linking of the polymer chains and neutral ion pairs result in reduced conductivity. Fig. 4A illustrates the conductivity at various temperature ranges. It illustrates that SEO (36-25) was conductive at 90⁰C and higher.

Figs. 5A-5C are graphs comparing ionic conductivity of the composite electrolytes as a function of the molecular weights of the PEO blocks. Fig. 5 A illustrates a systematic increase in conductivity with the molecular weight of the PEO block (MpEo)- The observed trend is opposite to that obtained in pure PEO/salt mixtures where the conductivity decreases with increasing molecular weight and eventually reaches a plateau. The conductivity, O_PEO, of the PEO homopolymer with r = 0.02 at 90⁰C and 120⁰C was measured to be 3.7 x 10^"4 S/cm and 5.6 x 10^"4 S/cm, respectively. The conductivity obtained in the highest molecular weight sample, SEO(74-98) (marked F in Fig. 3), is comparable to that of pure PEO. Data obtained (not shown) from SEO(74-98) at 100⁰C show σ peaks at a value of about 10^"3 S/cm at r=0.085. These values of conductivity are adequate for some battery applications. Figure 5C illustrates dependence of conductivity on the molecular weight of the PEO block separately for lamellar and cylindrical samples. It can be seen that in lamellar samples the conductivity increases with increase of molecular weight of PEO and then plateaus above 60 kg/mol. In samples having cylindrical morphology, increase of conductivity with increase in PEO block weight is observed, for all molecular weights screened.

The PEO volume fraction in the composite electrolyte, Φ_PEO, varied from 0.38 to 0.55. If all of the PEO channels in the nano structured electrolyte provided conducting pathways for the ions, and if the conductivity of the PEO channels were identical to that of PEO homopolymers, then the value of the conductivity of a doped SEO sample, σ_max would be the product of φpEoσpEo- The ratio σ/σ_max thus normalizes the measured conductivity data for differences in φpεo- Fig. 5B is a plot of σ/σ_max versus M_PEO- Fig. 5B shows that the ionic conductivity of the electrolytes may be mainly affected by M_PEo_, and not by block copolymer composition.

Figs. 5 A and 5B illustrate that: (1) it is possible to make self-assembled conducting nanostructured electrolytes with non-conducting matrix phases, and (2) the magnitude of the conductivity of such electrolytes is in the range of the theoretical upper limit that can be expected from such systems. The samples were not subjected to any special processing steps to ensure that the PEO lamellae were connected or aligned. Connectivity of the PEO phase occurs reproducibly by quiescent annealing at 120 ⁰C. In other embodiments, annealing is performed at lower temperatures to avoid salt precipitation within the polymer. Although it has been widely understood that highly connected network phases are essential for high conductivity, the above data indicates that that is not the case.

Fig. 5B illustrates the fact that σ/σ_max for the highest molecular weight sample is close to the theoretical maximum of 0.67 expected for a structure comprised of randomly oriented grains. It is believed that dissociated Li ions are tightly coordinated with the ether linkages in PEO, and thus disruption of this coordination could lead to faster ion transport. The disruption of coordination may be due to two reasons: (1) the contact between the ions and the polystyrene/poly(ethylene oxide) interfaces, and (2) the deformation of PEO chains due to self-assembly. The polystyrene/poly(ethylene oxide) interfacial area (per unit volume) decreases with increasing molecular weight. As noted above with reference to Fig. 3, potential reason (1) appears incorrect. As such, ion transport within microphases may be faster than in bulk.

In contrast, it is known that block copolymer chains stretch when they form ordered phases due to the traditional balance of energy and entropy. On average, PEO chains are stretched in the lamellae, compared to the homopolymer. The extent of stretching depends on copolymer chain length, N, and the Flory-Huggins interaction parameter between the blocks, χ. The range of the product χN in the SEO diblock copolymers ranged from 25 to 130 at 90⁰C, indicating that these copolymers in accordance with the invention are far from the weak segregation limit. Another indication of the stretched nature of the PEO chains is the scaling of the PEO lamellae thickness, dp_Eo, calculated from the periodic length scale, d, given in Table 1 with

N _Eo, the number of EO units in PEO block. A least squares power law fit through the d versus N data yields dpEo = 0.18*N_EO° ⁶⁹ (both the prefactor and exponent were free parameters in the fit), which is the expected result in the strongly segregated limit.

Thus, the stretched PEO chains in the high molecular weight block copolymers are not as tightly coordinated with Li ions compared to PEO random coils, which leads to enhanced conductivity.

Fig. 6 is a graph illustrating the frequency dependence of the storage and loss shear moduli. The graph shows the frequency (ω) dependence of the storage and loss shear moduli, G' and G", respectively, of pure SEO(36-25), SEO(36-25) with r = 0.020, and pure PEO homopolymer. The data obtained from the pure SEO(36-25) and SEO(36-25) with r = 0.020 are indistinguishable. The frequency-independence of the moduli and the fact that G' is an order of magnitude larger than G" indicate that the block coploymer electrolytes are elastic solids. The data also indicates that the addition of small amounts of salt has no detrimental effect on the mechanical properties of the materials. The value of G' obtained from the SEO(36-25) electrolyte is 100 times larger than the plateau modulus of pure PEO and 6 orders of magnitude larger than G' of the PEO homopolymer. The molecular weight of the PEO homopolymer is similar to that of the PEO block in the SEO(36-25) copolymer. Thus, nano structured electrolytes have roughly half the conductivity of homopolymer PEO but larger shear moduli by several orders of magnitude.

Fig. 7 is a graph illustrating the frequency dependence of elastic moduli for the diblock copolymers referenced in Fig. 3. The higher molecular weight copolymers that exhibit high ionic conductivity yield elastic moduli of the order of 10⁸ Pa. By adding the PS block to the PEO chain, the shear modulus increases by several orders of magnitude while keeping the ionic conductivity near the level of pure PEO.

Fig. 8 plots the results of cycling a Li/SEO(74-98) r=0.02fLi cell with a 250 μm thick electrolyte at 90⁰C. The cell was formed with a freestanding polymer electrolyte film formed as described above herein. A spacer with the freestanding polymer electrolyte film was then sandwiched between two aluminum masks that defined the exposed electrolyte area available for lithium (Li) deposition. This assembly was then secured to a slotted disk. The slots in the disk ensure that the electrolyte surface was exposed for Li deposition. The slotted-disk with 30 electrolyte/mask assemblies was then secured to a spindle in the Li deposition chamber. The spindle was connected to a motor that can rotate the spindle, along with the slotted plate with electrolyte/mask assemblies. Once the slotted plate was secured to the spindle, Li pellets were placed in the crucible of the vapor-deposition chamber. The deposition chamber was then closed and left overnight under a very high vacuum (< 10^~3 mbar). The high vacuum ensures that the electrolyte and Li pellets are free of any adsorbed solvent molecules that may react with Li vapors. When the pressure in the deposition chamber was below 10^~3 mbar, the crucible was heated to -200 ⁰C, and Li was deposited from Li vapors onto the exposed surface of the electrolyte. The thickness of the deposited Li layer/film was monitored, and vapor deposition was stopped once a desired (~1 μm) Li-layer thickness was achieved. Then the deposition chamber was opened and the slotted plate was flipped and secured back to the spindle, exposing the other face of the freestanding electrolyte film that had not yet received any deposited Li. The deposition chamber was closed and the process of Li-deposition was repeated. This yields symmetric Li/SEO/Li cells for performing DC cycling measurements. In each cycle, a 50 μA/cm² current density was applied to the cell for 2 h, followed by a rest period of 1 h, followed by a 50 μA/cm² current density applied in the opposite direction. The voltage required to achieve this current density was independent of time over 80 cycles, indicating the lack of dendrite growth during these experiments.

The structure of the block copolymer electrolytes of the present invention was investigated to determine if a structural correlation for the observed properties could be determined. Poly(styrene-b/ocfc-ethylene oxide) (SEO) copolymer electrolytes were prepared as described above. Samples were pressed at 120⁰C into 0.1-lmm thick disks using a mechanical press. All sample preparation was done without exposing the materials to atmospheric water or oxygen.

Electron microscopy images were analyzed to determine the width of the lithium and poly(ethylene oxide) channels. Micrographs were segmented into boxes that were approximately two times the periodicity of the structures. The minimum periodicity, d_mm, was taken to be the true spacing of the nanostructured electrolyte. Regions which show a periodicity within 10% of d_mm were selected for further quantification. The intensity distribution of these images was normalized to maximize the dynamic range of contrast. A high-pass filter which removes low- frequency data below a radius of 30 pixels was used to remove some of the noise from the images. The image was thresholded, such that pixels are either black or white, to measure systematically the lamellae thicknesses. The channel thicknesses were measured by hand every 0.04-d_mm along the lamellae normal.

Figure 9A is a bright field image of SEO(16-16)/salt mixture (r = 0.085). The amorphous nature of the polymer is clearly visible. Figure 9B is the lithium energy filtered micrograph of the same region as Figure 9A. The light regions correspond to the presence of lithium, and the dark regions to the absence of lithium. Since the salt segregates itself to the PEO channels, the micro structure is now clearly visible and it is highly suggestive of a lamellar morphology.

Measurements of the thickness of the lithium salt and poly(ethylene oxide) lamellae are shown in Figure 10 for SEO(74-98) at a salt concentration of r = 0.085.

The first column corresponds to the product of the periodicity observed in our images and the volume fraction of ethylene oxide in the copolymer. The second column is the thicknesses of PEO lamellae measured from bright field images of neat SEO copolymers stained with RuO₄. The last three columns correspond to lamellae measurements taken on energy filtered TEM images of O, Li and F. The first three columns are a measure of the PEO lamellae thickness, while the last two are a measure of the Li channels. It is clear from Figure 10 that the salt lamellae are thinner than the PEO channels for SEO(74-98) at a salt concentration of r = 0.085. The size of the Li domains were normalized by the ethylene oxide domains to determine the extent of this concentration effect as a function of the molecular weight of PEO,

Mp_Eo, and these results are plotted in Figure 11. It is clear that the thinning of the lithium lamellae is more dramatic for polymers with higher molecular weight.

Fig. 12 is a comparison of the lithium salt distribution and the ionic conductivity of the copolymer electrolytes. There is a clear inverse relationship between the extent to which the Li segregates away from the interface and the ionic conductivity. It is concluded that by constructing SEO copolymer/salt mixtures where Mp_Eo is high, a novel lithium salt structure within the nanostructured copolymer, with Li salt concentrated in a central portion of the ionically conductive polymer block, is produced, which results in highly conductive materials.

Fig. 14 illustrates dependence of conductivity on inverse temperature (1000/T) in a SEO (54-23) sample, having lithium salt concentration r = 0.05. Heating and cooling plots are shown with arrows. It can be seen that during heating the conductivity increases with the increase in temperature until a threshold of 100 - 110 ⁰C is reached. Above this temperature range, the conductivity stops rising and eventually drops by almost an order of magnitude. Interestingly, during cooling the conductivity does not rise to the initial high value. Therefore, it appears that at least in this sample, and at the time scale used during measurement (about 30 minutes for each data point), the salt precipitation is irreversible.

Figure 15 provides evidence that the observed conductivity drop is due to lithium salt precipitation. Figure 15 provides SAXS plots for the same SEO polymer. SAXS profiles at 53 ⁰C, 88 ⁰C, and 134 ⁰C in a heating regime. The 134 ⁰C temperature value is above the threshold temperature for conductivity drop in this polymer. It can be observed that the profile at this temperature exhibits increased low- Q scattering, which is a sign of macrophase separation (salt precipitation). The profiles at lower temperatures do not show signs of salt precipitation.

Nano structured polymer electrolytes with soft conducting channels embedded in a hard insulating matrix are beneficial for applications that require independent control over mechanical and electrical properties. The data presented above indicate that network phases are not necessary to obtain ionic conductivity, which allows for the possibility of using a wide variety of morphologies for designing ionically conducting polymers. No special processing is needed to create percolating conducting pathways in these materials; they are formed entirely by quiescent self- assembly. This suppresses dendrite growth in Li-polymer batteries and provides a cost-effective solution for combining high energy density with good cyclability.

APPLICATIONS

The electrolytes of the present invention are useful as solid phase electrolytes for high energy density, high cycle life batteries that do not suffer from failures due to side reactions and dendrite growth on the Li electrodes. In one aspect, the invention relates to a battery cell, a simple schematic diagram of which is provided in Figure 13, comprising a lithium anode, a cathode, and a solid phase block copolymer electrolyte in accordance with the present invention disposed between the anode and cathode. The cell can be cycled without detrimental dendrite growth on the anode. In one aspect the battery cell includes a polymer electrolyte which is configured for preventing thermal runaway in the battery cell. The polymer electrolyte has a lithium salt dissolved therein, and is configured for precipitating this salt once the temperature of electrolyte exceeds a threshold value. In some embodiments, this threshold value lies in the range between 90 ⁰C and 150 ⁰C, e.g., between 100 ⁰C and 110 ⁰C. The precipitation of lithium salt leads to a drop or at least a plateau in conductivity of the polymer above the threshold temperature, which, in turn, leads to cooling, or at least reduced heating of the cell.

Advantageously, the precipitation of lithium salts in the block copolymers described herein is an intrinsic unexpected property of the copolymers, related to the thermodynamics of the copolymer/salt system. Therefore, in some embodiments the electrolyte itself provides a thermal shutoff mechanism for the lithium battery cell, without the need for complicated mechanical shutoff designs. In other embodiments, both shutoff designs may complement each other and be used in concert.

Preferably, the polymer electrolyte is configured to have a conductivity drop and a threshold temperature which are sufficient to prevent melting of lithium metal in the battery cell. For example, polymer electrolytes having a threshold temperature at which conductivity drops or plateaus (or lithium salt precipitates) well below the melting point of Li metal (180 ⁰C) are preferred.

Further, in another aspect, a method of using a lithium battery cell is provided.

The cell includes a lithium anode, a cathode, and a solid block copolymer electrolyte having a lithium salt dissolved therein. The block copolymer electrolyte is configured for precipitating the lithium salt above a threshold temperature (e.g., above a temperature from the range of 90 ⁰C - 150 ⁰C). The method of operating a cell involves charging and discharging the rechargeable cell. The cell is configured for cooling or for reduced heating once the electrolyte reaches the threshold temperature during battery cell operation. As it was described, the reduced heating or cooling is due to conductivity drop in the electrolyte which occurs above the threshold temperature upon salt precipitation.

The invention may also be used, for example, as a power source for electronic media such as cell phones, media players (MP3, DVD, and the like), laptops and computer peripherals, digital cameras, camcorders, and the like. It may also be beneficial for applications in electric vehicles and hybrid electric vehicles.

In addition, as it was previously mentioned, it has been discovered that careful processing of polymer films needs to be performed in order to prevent salt precipitation during fabrication of the polymer films. The choice of processing temperatures used in annealing and/or casting operations will depend on the polymer system, specific polymer chain architecture, the type of salt, the salt concentration and other parameters. One of skill in the art will understand how to select optimal temperature window for polymer film fabrication, based on provided considerations and guidelines.

CONCLUSION

Although the foregoing invention has been described in some detail for purposes of clarity of understanding, it will be apparent that certain changes and modifications may be practiced within the scope of the appended claims. It should be noted that there are many alternative ways of implementing both the process and compositions of the present invention. Accordingly, the present embodiments are to be considered as illustrative and not restrictive, and the invention is not to be limited to the details given herein, but may be modified within the scope and equivalents of the appended claims.

Claims

Claims

1. A polymer electrolyte, comprising:

a linear block copolymer having,

a Li-ion conductive non-crosslinked linear polymer block with a molecular weight of at least 5000 Daltons;

and a structural linear polymer block;

wherein the linear block copolymer is configured for dissolving a lithium salt at a first temperature and precipitating the lithium salt at a higher threshold temperature such that the precipitation of the lithium salt is accompanied by at least a 2-fold decrease in a conductivity of the polymer.

2. The electrolyte of Claim 1, wherein the linear block copolymer is a diblock copolymer.

3. The electrolyte of Claim 2, wherein the diblock copolymer is characterized by bicontinuous phases of the conductive polymer block and the structural polymer block.

4. The electrolyte of Claim 3, wherein the structural linear polymer block comprises a major phase of the block copolymer.

5. The electrolyte of Claim 4, wherein the major phase structural polymer block forms a rigid framework and the conductive polymer block forms nano structured ionically conductive channels with the rigid framework.

6. The electrolyte of claim 5, wherein the block copolymer has a cylindrical nanostructure such that the conductive polymer block forms cylindrical phases within a rigid framework of the structural polymer block.

7. The electrolyte of claim 1, wherein the structural polymer has a molecular weight of at least 5000 Daltons.

8. The electrolyte of claim 1, wherein the structural polymer has an elastic modulus of from about 1 x 10⁷ Pa to 3 GPa.

9. The electrolyte of claim 1, wherein the conductive polymer has an elastic modulus of no more than 1 MPa.

10. The electrolyte of claim 3, wherein the conductive and structural polymers each have molecular weights of at least 15,000 Daltons.

11. The electrolyte of claim 3, wherein the conductive and structural polymers each have molecular weights of at least 50,000 Daltons.

12. The electrolyte of Claim 1, wherein the structural polymer block is ionically non-conductive.

13. The electrolyte of Claim 1, wherein the structural polymer block comprises polystyrene.

14. The electrolyte of Claim 1, wherein the conductive polymer block comprises poly(ethylene oxide).

15. The electrolyte of Claim 5, wherein the conductive polymer block further comprises a Li salt.

16. The electrolyte of Claim 15, wherein the Li salt is concentrated in a central portion of the ionically conductive channels.

17. The electrolyte of claim 1, wherein the ionic conductivity of the block copolymer increases with increasing molecular weight of the conductive polymer block.

18. The electrolyte of claim 1, wherein the ionic conductivity is at least 1 x 10^"4 Son ¹.

19. The electrolyte of claim 3, wherein the bicontinuous phases have a lamellar arrangement.

20. The electrolyte of Claim 1, wherein the block copolymer is a triblock copolymer further comprising an additional linear polymer block.

21. The electrolyte of Claim 20, wherein the triblock copolymer is a polystyrene- block-polyisoprene-block poly(ethylene oxide) (S-I-EO) triblock copolymer.

22. The electrolyte of claim 1, wherein the block copolymer is a polystyrene- block-poly(ethylene oxide) (SEO) diblock copolymer.

23. The electrolyte of claim 22, wherein the poly(ethylene oxide) block has a molecular weight of at least 50,000 Daltons.

24. The electrolyte of claim 23, wherein the polystyrene block has a molecular weight of at least 50,000 Daltons.

25. The electrolyte of claim 22, wherein the volume fraction of poly(ethylene oxide) block is between 0.2 - 0.5.

26. The electrolyte of claim 25, wherein the volume fraction poly(ethylene oxide) block is between 0.25 - 0.35.

27. The electrolyte of claim 1, wherein the electrolyte has a cylindrical or lamellar nanostructure with the structural block forming the major phase of the nanostructure by volume.

28. The electrolyte of claim 27, wherein the precipitation occurs at a threshold temperature between 90 ⁰C and 150 ⁰C.

29. The electrolyte of claim 28, wherein the precipitation occurs at the threshold temperature between 100 ⁰C and 120 ⁰C.

30. The electrolyte of claim 28, wherein the precipitation occurs at the threshold temperature between 105 ⁰C and 115 ⁰C.

31. The electrolyte of claim 27, wherein the precipitation is accompanied by at least 5-fold drop of conductivity of the electrolyte comprising a lithium salt.

32. The electrolyte of claim 31, wherein the precipitation is accompanied by at least 10-fold drop of conductivity of the electrolyte comprising a lithium salt.

33. A method of making a polymer electrolyte, comprising:

in an oxygen and moisture free environment,

forming a linear block copolymer having a Li-ion conductive linear polymer block with a molecular weight of at least 5000 Daltons and a structural linear polymer block, wherein the formed linear block copolymer is configured for dissolving a lithium salt at a first temperature and precipitating the lithium salt above a higher threshold temperature;

incorporating a Li salt into the linear block copolymer at the first temperature;

heating the resulting polymer above the glass transition temperature of the structural block but below the threshold temperature above which salt precipitation occurs;

wherein the resulting polymer electrolyte has a ionic conductivity of at least 1 x 10^"5 Son^"1.

34. The method of Claim 33, wherein the linear block copolymer is a diblock copolymer.

35. The method of claim 33. wherein heating comprises annealing and/or casting of the polymer electrolyte film.

36. The method of claim 35 comprising performing annealing and/or casting at a temperature below 150 ⁰C.

37. The method of claim 36 comprising performing annealing and/or casting at a temperature below 110 ⁰C.

38. The method of claim 35, wherein the block copolymer is a polystyrene-block- poly(ethylene oxide) (SEO) diblock copolymer, and wherein the annealing and/or casting is performed at a temperature range of between 90 - 110 ⁰C.

39. The method of claim 33, wherein the method comprises:

synthesizing the structural polymer block by living anionic polymerization; adding a monomer of the conductive polymer block and a cryptand catalyst to the structural polymer block living anionic polymerization mixture;

allowing a diblock copolymerization reaction to proceed;

terminating the reaction;

precipitating and freeze-drying the resulting diblock copolymer product,

blending the freeze-dried diblock copolymer with the Li salt in a dry solution such that the Li salt is dissolved into the conductive polymer block;

freeze-drying the polymer/salt solution;

heating the formed polymer/salt solution.

40. The method of claim 39, wherein the heating comprising subjecting a portion of the freeze-dried polymer/salt solution to heat and pressure to form a freestanding polymer electrolyte film.

41. The method of claim 40, wherein subjecting a portion of the freeze-dried polymer/salt solution to heat and pressure to form a freestanding polymer electrolyte film comprises subjecting the solution to a temperature that does not cause lithium salt precipitation.

42. The method of claim 33, wherein the conductive polymer block comprises poly(ethylene oxide).

43. The method of claim 42, wherein the structural polymer block comprises polystyrene.

44. The method of claim 43, wherein the Li salt is LiN[SO₂CF₃J₂.

45. The method of claim 33, wherein incorporating a Li salt into the linear block copolymer comprises blending solutions of the lithium salt and the linear block copolymer in one or more liquid solvents, and subjecting the formed solution to heat to evaporate the one or more liquid solvents and to cast a copolymer film of desired dimensions, wherein said subjecting to heat dose not expose the formed solution to the threshold temperature above which lithium salt precipitation occurs.

46. A battery cell, comprising:

a Li anode;

a cathode; and

a solid phase polymer electrolyte disposed between the anode and cathode, the electrolyte, comprising:

a linear block copolymer having,

a Li-ion conductive non-crosslinked linear polymer block with a molecular weight of at least 5000 Daltons and a lithium salt dissolved therein;

a structural linear polymer block with an elastic modulus in excess of 1 x 10⁷ Pa; and

an ionic conductivity of at least 1 x 10^"5 Scm^"1, wherein the cell is configured for thermal run-away shutoff by providing a conductivity drop in the linear block copolymer responsive to a temperature increase of the block copolymer beyond a threshold temperature.

47. The cell of claim 46, wherein the conductive polymer block has an elastic modulus of no more than 1 MPa.

48. The cell of claim 46, wherein the conductivity drop is at least 2-fold.

49. The cell of claim 48, wherein the conductivity drop is at least 5-fold.

50. The cell of claim 48, wherein the conductivity drop is at least 10-fold.

51. The cell of claim 48, wherein the conductivity drop occurs at a temperature range of 90 - 150 ⁰C.

52. The cell of claim 48, wherein the conductivity drop occurs at a temperature range of 100 - 120 ⁰C.

53. The cell of claim 48, wherein the conductivity drop decreases the cell temperature and prevents lithium metal from melting.

54. The cell of claim 46, wherein the conductive and structural polymers each have molecular weights of at least 15,000 Daltons.

55. The cell of claim 46, wherein the conductive and structural polymers each have molecular weights of at least 50,000 Daltons.

56. The cell of claim 46, wherein the conductive polymer block comprises poly(ethylene oxide).

57. The cell of claim 56, wherein the structural polymer block comprises polystyrene.

58. The cell of claim 57, wherein the Li salt is LiN[SO₂CF₃]₂.

59. The cell of claim 46, wherein the cell can be cycled at least once without dendrite growth on the anode.

60. A method of operating a battery cell equipped with a thermal run-away shutoff, the method comprising:

(a) providing a battery cell comprising a Li anode, a cathode, and a solid block copolymer electrolyte having a lithium salt dissolved therein, wherein the block copolymer electrolyte is configured for precipitating lithium salt above a threshold temperature;

(b) charging the battery cell; and

(c) discharging the battery cell, wherein

the battery cell is configured for cooling or for reduced heating once the electrolyte reaches the threshold temperature during battery cell operation, wherein said cooling or reduced heating is due to conductivity drop in the electrolyte associated with lithium salt precipitation.

61. The method of claim 60, wherein the threshold temperature is between 90 ⁰C and 150 ⁰C.

62. The method of claim 60, wherein the threshold temperature is between 100 ⁰C and 120 ⁰C.

63. The method of claim 60, wherein during operation of the cell lithium melting does not occur.

64. The method of claim 60, wherein the block copolymer electrolyte comprises polystyrene-block-poly(ethylene oxide) (SEO) di-block copolymer.

65. The method of claim 64, wherein the volume fraction of poly(ethylene oxide) block is between 0.2 and 0.6.

66. A method of screening block copolymer electrolytes for a block-copolymer electrolyte suitable for preventing thermal runaway in a cell, the method comprising:

(a) providing a plurality of block-copolymers having a lithium salt dissolved therein;

(b) measuring dependence of conductivity, SAXS, or light scattering profiles versus temperature for at least some of the provided block copolymers;

(c) based on the measurements obtained in (b), identifying the block copolymers which exhibit a drop in conductivity or exhibit evidence of salt precipitation in the SAXS or light scattering profile with increase of temperature above a threshold temperature.

67. The method of claim 66, wherein the block copolymers provided in (a) have a conductivity of at least 1 x 10^"5 Scm^"1 at least at some temperatures of the measured temperature range.

68. The method of claim 66, further comprising identifying block copolymers exhibiting at least 5-fold drop in conductivity at a temperature range of about 90 ⁰C - 150 ⁰C.