WO2010032051A1 - Catalyst and process - Google Patents
Catalyst and process Download PDFInfo
- Publication number
- WO2010032051A1 WO2010032051A1 PCT/GB2009/051208 GB2009051208W WO2010032051A1 WO 2010032051 A1 WO2010032051 A1 WO 2010032051A1 GB 2009051208 W GB2009051208 W GB 2009051208W WO 2010032051 A1 WO2010032051 A1 WO 2010032051A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- catalyst
- oxidation
- gas stream
- ruthenium
- weight
- Prior art date
Abstract
Description
Claims