WO2010028975A2 - Polyamide thermoconducteur présentant une plus grande fluidité - Google Patents

Polyamide thermoconducteur présentant une plus grande fluidité Download PDF

Info

Publication number
WO2010028975A2
WO2010028975A2 PCT/EP2009/061231 EP2009061231W WO2010028975A2 WO 2010028975 A2 WO2010028975 A2 WO 2010028975A2 EP 2009061231 W EP2009061231 W EP 2009061231W WO 2010028975 A2 WO2010028975 A2 WO 2010028975A2
Authority
WO
WIPO (PCT)
Prior art keywords
weight
acid
molding compositions
component
thermoplastic molding
Prior art date
Application number
PCT/EP2009/061231
Other languages
German (de)
English (en)
Other versions
WO2010028975A3 (fr
Inventor
Rebekka Von Benten
Daniel SCHÖNFELDER
Bernd Bruchmann
Volker Warzelhan
Matthias Scheibitz
Sachin Jain
Peter Eibeck
Original Assignee
Basf Se
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Basf Se filed Critical Basf Se
Publication of WO2010028975A2 publication Critical patent/WO2010028975A2/fr
Publication of WO2010028975A3 publication Critical patent/WO2010028975A3/fr

Abstract

L'invention concerne des matières à mouler thermoplastiques comportant : A) entre 10 à 99 % en poids d'au moins un polyamide thermoplastique; B) entre 0,01 et 30 % en poids d'au moins une polyétheramine très ramifiée ou hyperramifiée; C) entre 0,5 et 80 % en poids d'une charge thermoconductrice; D) entre 0 et 70 % en poids d'additifs supplémentaires, la somme desdits pourcentages en poids des composants A) à D) étant égale à 100 %.
PCT/EP2009/061231 2008-09-09 2009-09-01 Polyamide thermoconducteur présentant une plus grande fluidité WO2010028975A2 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP08163960 2008-09-09
EP08163960.1 2008-09-09

Publications (2)

Publication Number Publication Date
WO2010028975A2 true WO2010028975A2 (fr) 2010-03-18
WO2010028975A3 WO2010028975A3 (fr) 2010-07-15

Family

ID=41657564

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2009/061231 WO2010028975A2 (fr) 2008-09-09 2009-09-01 Polyamide thermoconducteur présentant une plus grande fluidité

Country Status (1)

Country Link
WO (1) WO2010028975A2 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014135624A1 (fr) 2013-03-07 2014-09-12 Basf Se Compositions de moulage thermoplastique thermoconducteur comprenant un agent ignifugeant
CN109504083A (zh) * 2018-11-21 2019-03-22 杭州本松新材料技术股份有限公司 聚酰胺树脂用双组份除味剂及含其的聚酰胺树脂复合材料
CN109810616A (zh) * 2019-02-02 2019-05-28 宁夏瑞锦新材料技术有限公司 一种高耐磨环氧陶瓷复合涂层及其制备方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1424360A1 (fr) * 2002-11-26 2004-06-02 Bayer Aktiengesellschaft Compositions de polymères à écoulement élevé comportant des agents régulateurs de fluidité ramifiés
WO2007113116A1 (fr) * 2006-03-29 2007-10-11 Basf Se Polyamides thermoconducteurs
WO2009077492A2 (fr) * 2007-12-18 2009-06-25 Basf Se Polyamides thermoplastiques comprenant des polyétheramines
WO2009115535A2 (fr) * 2008-03-18 2009-09-24 Basf Se Nanocomposite de polyamide avec polyétheramines hyperramifiées

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1424360A1 (fr) * 2002-11-26 2004-06-02 Bayer Aktiengesellschaft Compositions de polymères à écoulement élevé comportant des agents régulateurs de fluidité ramifiés
WO2007113116A1 (fr) * 2006-03-29 2007-10-11 Basf Se Polyamides thermoconducteurs
WO2009077492A2 (fr) * 2007-12-18 2009-06-25 Basf Se Polyamides thermoplastiques comprenant des polyétheramines
WO2009115535A2 (fr) * 2008-03-18 2009-09-24 Basf Se Nanocomposite de polyamide avec polyétheramines hyperramifiées

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014135624A1 (fr) 2013-03-07 2014-09-12 Basf Se Compositions de moulage thermoplastique thermoconducteur comprenant un agent ignifugeant
CN109504083A (zh) * 2018-11-21 2019-03-22 杭州本松新材料技术股份有限公司 聚酰胺树脂用双组份除味剂及含其的聚酰胺树脂复合材料
CN109810616A (zh) * 2019-02-02 2019-05-28 宁夏瑞锦新材料技术有限公司 一种高耐磨环氧陶瓷复合涂层及其制备方法

Also Published As

Publication number Publication date
WO2010028975A3 (fr) 2010-07-15

Similar Documents

Publication Publication Date Title
EP2227507B1 (fr) Polyamides thermoplastiques comprenant des polyétheramines
EP2257597B1 (fr) Nanocomposite de polyamide avec polyétheramines hyperramifiées
EP2001951B1 (fr) Polyamides thermoconducteurs
EP1851265B1 (fr) Polyamides resistants au vieillissement thermique
WO2009115536A1 (fr) Nanocomposite polyamide avec polyéthylène imines hyperramifiées
EP2652032B1 (fr) Polyamides résistants au fil incandescent
EP2294120B1 (fr) Polyamide thermoconducteur avec terre de diatomées
WO2010076145A1 (fr) Polyamides résistants au vieillissement thermique
WO2010054933A1 (fr) Polyamide stabilisé
EP2861666B1 (fr) Polyamide ignifuge comprenant un homopolymère polyacrylonitrile
WO2006010543A1 (fr) Polyamides thermostabilises
WO2010028975A2 (fr) Polyamide thermoconducteur présentant une plus grande fluidité
EP2665777B1 (fr) Polyamides stables à l'hydrolyse
EP2817363B1 (fr) Mélanges cuo/zno servant de stabilisants pour des polyamides ignifugés
EP2641939A1 (fr) Polyamide ignifuge teinté en nuances claires
EP2650331A1 (fr) Polyamide pour utilisations en rapport avec l'eau potable
EP2756033B1 (fr) Mélanges d'argent et d'oxyde de zinc en tant que stabilisant pour des polyamides ignifugés contenant du phosphore rouge
EP2702102A1 (fr) Matières à mouler ignifugées
DE102010051726A1 (de) Amorphe Polyamide mit bicyclischen aliphatischen Diaminen
DE102008058246A1 (de) Hochmolekulare Polyamide
DE102009035974A1 (de) Amorphe Polyamide
DE102008043863A1 (de) Teilaromatische Polyamide mit hyperverzweigten Polyoxazolinen

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 09782418

Country of ref document: EP

Kind code of ref document: A2

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase