WO2009153321A1 - Processing method for recovering iron oxide and hydrochloric acid - Google Patents
Processing method for recovering iron oxide and hydrochloric acid Download PDFInfo
- Publication number
- WO2009153321A1 WO2009153321A1 PCT/EP2009/057623 EP2009057623W WO2009153321A1 WO 2009153321 A1 WO2009153321 A1 WO 2009153321A1 EP 2009057623 W EP2009057623 W EP 2009057623W WO 2009153321 A1 WO2009153321 A1 WO 2009153321A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- chloride
- concentration
- weight
- hydrochloric acid
- liquid
- Prior art date
Abstract
Description
Claims