WO2009102288A3 - Method for coating zinc aluminium alloy solder wires with cesium fluoride or aluminium fluoride based flux and coated solder wire - Google Patents
Method for coating zinc aluminium alloy solder wires with cesium fluoride or aluminium fluoride based flux and coated solder wire Download PDFInfo
- Publication number
- WO2009102288A3 WO2009102288A3 PCT/TR2009/000021 TR2009000021W WO2009102288A3 WO 2009102288 A3 WO2009102288 A3 WO 2009102288A3 TR 2009000021 W TR2009000021 W TR 2009000021W WO 2009102288 A3 WO2009102288 A3 WO 2009102288A3
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- flux
- coating
- aluminium
- wire
- fluoride
- Prior art date
Abstract
The invention relates to a method for coating the solder wire (Z) used in the soldering process with the flux (D) 1 comprising the process steps of - mixing a certain proportion of a compound having the copolymer structure with the flux (cesium fluoride/aluminum fluoride compounds) (D) inside a solution, according to the flux preparation process (II), - preparing and pressing the metal alloy prepared in a certain ratio, and, providing the same with the thickness desired for coating, - coating the wire (L) with the flux (D) mixture provided under pressure according to the flux preparation process (II), to obtain the flux coating (D) on the wire (L). The employed solution comprises preferably 10-40% metacrylic copolymer in the organic solvent mixture. That said metal alloy is preferably a zinc-aluminium alloy comprising 2 to 16 % aluminium.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
TR2008/00942 | 2008-02-13 | ||
TR2008/00942A TR200800942A2 (en) | 2008-02-13 | 2008-02-13 | Coating of zinc aluminum alloy solder wires with cesium based deoxidizing chemical (pickling) |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2009102288A2 WO2009102288A2 (en) | 2009-08-20 |
WO2009102288A3 true WO2009102288A3 (en) | 2009-10-01 |
Family
ID=40853809
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/TR2009/000021 WO2009102288A2 (en) | 2008-02-13 | 2009-02-10 | Method for coating zinc aluminium alloy solder wires with cesium fluoride or aluminium fluoride based flux and coated solder wire |
Country Status (2)
Country | Link |
---|---|
TR (1) | TR200800942A2 (en) |
WO (1) | WO2009102288A2 (en) |
Families Citing this family (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN102699496B (en) * | 2012-05-23 | 2015-04-22 | 中国化学工程第三建设有限公司 | Welding process method of brass H62 |
CN113579547B (en) * | 2021-08-12 | 2023-03-10 | 郑州机械研究所有限公司 | Brazing filler metal paste for copper-aluminum dissimilar metal brazing flux-free brazing and brazing method |
Citations (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6070789A (en) * | 1997-11-18 | 2000-06-06 | S. A. Day Mfg. Co., Inc. | Method for soldering aluminum and soldering rod therefor |
-
2008
- 2008-02-13 TR TR2008/00942A patent/TR200800942A2/en unknown
-
2009
- 2009-02-10 WO PCT/TR2009/000021 patent/WO2009102288A2/en active Application Filing
Patent Citations (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6070789A (en) * | 1997-11-18 | 2000-06-06 | S. A. Day Mfg. Co., Inc. | Method for soldering aluminum and soldering rod therefor |
Also Published As
Publication number | Publication date |
---|---|
TR200800942A2 (en) | 2008-12-22 |
WO2009102288A2 (en) | 2009-08-20 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
ATE435716T1 (en) | ADDITIONAL MATERIAL FOR JOINING JOINTS AND METHOD FOR THE PRODUCTION THEREOF | |
NZ601842A (en) | Aluminium alloy welding wire | |
MY151120A (en) | Solder pastes with resin-free fluxing agent | |
WO2004029316A3 (en) | Corrosion-resistant coated copper and method for making the same | |
WO2014022619A3 (en) | Dual solder layer for fluidic self assembly and electrical component substrate and method employing same | |
EP2309009A3 (en) | Method For preparing A Metallic Article Having An Other Additive Constituent, Without Any Melting | |
EP2014317A3 (en) | Implant with a near-surface diffusion layer containing magnesium and corresponding production method | |
CA2371207A1 (en) | Composite sheet material for brazing | |
RU2014147321A (en) | METHOD FOR PRODUCING A METAL SHEET WITH Zn-AI-Mg COATING, INCLUDING THE APPLICATION OF AN ACID AND GLUE SOLUTION, AND THE RELATED METAL SHEET AND ASSEMBLY | |
CN107433400A (en) | A kind of preformed solder for including scaling powder and preparation method thereof | |
AU2003238721A1 (en) | Method of binding a compound to a surface | |
WO2009102288A3 (en) | Method for coating zinc aluminium alloy solder wires with cesium fluoride or aluminium fluoride based flux and coated solder wire | |
WO2005037467A3 (en) | Method for manufacturing components with a nickel base alloy as well as components manufactured therewith | |
WO2009044825A1 (en) | Process for producing metal member, structure member with thus produced metal member, and method of repairing metal member | |
EP2441855A3 (en) | Method of forming a diffusion aluminide coating on a surface of a turbine component and a homogeneous paste for coating such surfaces | |
HK1047256A1 (en) | Components coated with an aluminium-silicon alloy. | |
KR20150011847A (en) | ASSEMBLY OF AN ALUMINUM COMPONENT AND OF A STEEL COMPONENT HAVING A ZnAlMg ALLOY COATING | |
CA2595516A1 (en) | Lead free desoldering braid | |
EP1247593A3 (en) | Die for extruding aluminium or aluminium alloys | |
CA2358298A1 (en) | Aluminum metal-core weld wire and method for forming the same | |
CN102265719A (en) | Magnesium alloy member and method for producing same | |
US20100047616A1 (en) | Wire Feedstock and Process for Producing the Same | |
WO2005035835A3 (en) | Workpieces coated with an aluminum/magnesium alloy | |
US11183779B2 (en) | Press-in pin and method for producing same | |
JP6814488B2 (en) | Steel structure repair method and steel structure repair kit |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 09711313 Country of ref document: EP Kind code of ref document: A2 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 09711313 Country of ref document: EP Kind code of ref document: A2 |