WO2009097375A1 - Modifiers for oriented polypropylene - Google Patents
Modifiers for oriented polypropylene Download PDFInfo
- Publication number
- WO2009097375A1 WO2009097375A1 PCT/US2009/032317 US2009032317W WO2009097375A1 WO 2009097375 A1 WO2009097375 A1 WO 2009097375A1 US 2009032317 W US2009032317 W US 2009032317W WO 2009097375 A1 WO2009097375 A1 WO 2009097375A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- film
- pmp
- ptt
- packaging
- films
- Prior art date
Abstract
Description
Claims