WO2009097082A1 - Spray-dried transition metal zeolite and its use - Google Patents
Spray-dried transition metal zeolite and its use Download PDFInfo
- Publication number
- WO2009097082A1 WO2009097082A1 PCT/US2009/000260 US2009000260W WO2009097082A1 WO 2009097082 A1 WO2009097082 A1 WO 2009097082A1 US 2009000260 W US2009000260 W US 2009000260W WO 2009097082 A1 WO2009097082 A1 WO 2009097082A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- catalyst
- transition metal
- spray
- titania
- zeolite
- Prior art date
Abstract
Description
Claims