WO2009037410A1 - Enduit monocouche pour facade et sa fabrication - Google Patents
Enduit monocouche pour facade et sa fabrication Download PDFInfo
- Publication number
- WO2009037410A1 WO2009037410A1 PCT/FR2008/051475 FR2008051475W WO2009037410A1 WO 2009037410 A1 WO2009037410 A1 WO 2009037410A1 FR 2008051475 W FR2008051475 W FR 2008051475W WO 2009037410 A1 WO2009037410 A1 WO 2009037410A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- coating
- silane
- composition
- water
- facade
- Prior art date
Abstract
Description
Claims