WO2008157075A1

WO2008157075A1 - Method of forming panels using an in-situ tape placement process and panels formed therefrom

Info

Publication number: WO2008157075A1
Application number: PCT/US2008/066024
Authority: WO
Inventors: Alan R. Goodworth; James A. Anthony; William V. Forster
Original assignee: Sikorsky Aircraft Corporation
Priority date: 2007-06-21
Filing date: 2008-06-06
Publication date: 2008-12-24
Also published as: US8043458B2; EP2162350A1; US20100266820A1; EP2162350A4

Abstract

A composite panel and method of manufacture includes a support structure and a tape skin wound about the support structure. A mandrel assembly with extractable longitudinal mandrels facilitates winding of the tape skin onto the support structure. The composite panel is suitable for use in an aircraft floor system.

Description

METHOD OF FORMING PANELS USING AN IN-SITU TAPE PLACEMENT PROCESS AND PANELS FORMED THEREFROM

BACKGROUND OF THE INVENTION This invention was made with government support under Contract No.:

DAHH10-03-2-0003, awarded by the Department of Army. The government therefore has certain rights in this invention.

The present application claims priority to United States Provisional Patent Application Serial No. 60/936597, filed June 21, 2007. The present invention relates to composite structures, and more particularly to composite panels and methods for making such panels.

Current aircraft floor systems incorporate thin metallic or composite prepreg skin materials adhesively bonded to either a metallic or non-metallic honeycomb core. Current metallic aircraft floor systems require minimal tooling and have high tolerances, but may not achieve the weight benefits of composite floor systems.

Current aircraft composite floor system floor panels utilize a honeycomb core material with pre-cured fiberglass or prepreg composite skins bonded thereto in a large heated press or autoclave. Local hard points and edge closeouts are typically accomplished with an epoxy potting compound. The floor panels may require relatively complicated and labor intensive process steps including: pre-curing of the inboard and outboard skins; cutting, machining, and forming of the honeycomb core; local densification of the honeycomb core at attachment hard points and edge closeouts; preparation of the skins and core assembly for bonding; assembly of the pre-cured skins, lay-up of film adhesive layers for bonding; curing of the assembled skins, adhesive, and core; secondary machining, densification, and splicing operations of the honeycomb core material; and multiple processing cycles in an autoclave, oven or press, to complete fabrication of an individual panel.

Although composite floor systems are generally lighter in weight than metallic floor systems, composite floor systems may be more expensive and labor intensive to manufacture.

Moreover, usage of honeycomb core structures in rotary-wing aircraft floor systems may suffer inherent moisture absorption due to the open cell structure. Such moisture absorption may result in increased weight and a resultant performance degradation over a prolonged service period.

Accordingly, it is desirable to provide panels suitable for use in an aircraft floor system that are lighter in weight and manufactured in fewer steps relative to current panels, yet meet or exceed design requirements therefor.

SUMMARY OF THE INVENTION

A composite panel suitable for use in an aircraft floor system according to an exemplary aspect of the present invention includes a support structure; and a tape skin wound about the support structure.

A method of manufacture of a composite panel according to an exemplary aspect of the present invention includes assembling a support structure with a multiple of longitudinal mandrels; assembling a mandrel assembly with the multiple of longitudinal mandrels to retain the support structure and define an axis of rotation; winding a tape about the assembled mandrel assembly while the mandrel assembly is rotated about the axis of rotation to bond the tape to the support structure and form a tape skin onto the support structure to thereby form a composite panel; and disassembling the mandrel assembly from the composite panel.

BRIEF DESCRIPTION OF THE DRAWINGS

The various features and advantages of this invention will become apparent to those skilled in the art from the following detailed description of the currently disclosed embodiment. The drawings that accompany the detailed description can be briefly described as follows: Figure IA is a schematic perspective view of a rotary- wing aircraft for use with the present invention;

Figure IB is a general perspective view of a cabin cargo floor section of the rotary- wing aircraft of Figure IA

Figure 1C is a general perspective view of a ramp floor system for use with the cargo floor section of Figure IB;

Figure 2 is a schematic partially phantom view of one floor panel of the floor system of Figures IB and 1C; Figure 3 is a sectional view of a floor panel with a reversible roller assembly;

Figure 4 is a perspective view of the floor panel;

Figures 5A-5G illustrate steps of the in-situ tape placement manufacturing process according to the present invention; Figure 6 is a schematic view of the fiber placement process;

Figure 7 is a sectional view of one embodiment of a flush tie-down pan installation;

Figure 8 is a sectional view of another embodiment of a flush tie-down pan installation; Figure 9 A is an exploded view of a tube and block tie-down row subassembly installation;

Figure 9B is a sectional view through the tube and block tie-down row subassembly illustrated in Figure 9A;

Figure 1OA is an exploded view of a tube and pan tie-down row subassembly installation; and

Figure 1OB is a sectional view through the tube and pan tie-down row subassembly illustrated in Figure 1OA.

DETAILED DESCRIPTION OF THE DISCLOSED EMBODIMENT Figure IA schematically illustrates a rotary- wing aircraft 10 having a main rotor system 12. The aircraft 10 includes an airframe 14 having an extending tail 16 which mounts a tail rotor system 18, such as an anti-torque system. The airframe 14 includes an airframe section 14A. The main rotor assembly 12 is driven about an axis of rotation through a main gearbox by one or more engines 22. The main rotor system 12 includes a multiple of rotor blades mounted to a rotor hub. Although a particular helicopter configuration is illustrated and described in the disclosed embodiment, other configurations and/or machines, such as high speed compound rotary wing aircraft with supplemental translational thrust systems, dual contra- rotating, coaxial rotor system aircraft, turbo-props, tilt-rotors and tilt-wing aircraft, will also benefit from the present invention.

An airframe cabin section 14A, includes a cabin floor system 30 (Figure IB) and a ramp section 3OR (Figure 1C), which may include, inter alia, a multitude of frame members 24 and a multitude of beam members 26 which support an aircraft outer skin 28 and the cabin floor system 30 formed of a multiple of composite floor panels 32. It should be understood that although a composite floor panel 32 is illustrated in many of the figures herein, it should be understood that numerous structures with various features (Figure IB) may be manufactured in accordance with the present invention. The multitude of frame members 24 and beam members 26 may be arranged in a generally rectilinear pattern, however, any arrangement may be used with the present invention.

Referring to Figure 2, each composite floor panel 32 generally includes a support structure 34 about which is wound a tape 36 and bonds thereto in an in-situ tape placement process. The support structure 34 includes a multiple of stiffeners 40, a multiple edge stiffeners 42, a multiple of roller trough stiffeners 44, and a multiple of tie-down pans 46. The support structure 34 may be manufactured from non-metallic material, metallic materials or various combinations thereof. The support structure section 34 may be manufactured from a thermoplastic composite matrix material including, but not limited to, PEEK, PEKK, Ultem, PPS, Urethane, Nylon, PEI, PES, PEK, as well as in combination with other material enhancements such as nano-particulate inclusions. Furthermore, these materials may also contain fibers which include but are not limited to pan carbon, pitch carbon, s-fiberglass, e- fiberglass, quartz, LCP, M5, and ceramic.

The tape 36 defines a tape upper skin 48 A, a tape lower skin 48B. The tape upper skin 48A and tape lower skin 48B is wound about the support structure 34 such that the in-situ tape upper skin 48A and in-situ tape lower skin 48B is essentially a continuous fiber reinforced thermoset and/or thermoplastic composite material (e.g., tow or slit tape) prior to a trimming operation (Figure 5C) to yield a nearly fastener-less skin surface. That is, the trimming operation separates the contiguous wound tape skin into the tape upper skin 48A and tape lower skin 48B (Figure 5C to Figure 5D). The trimming operation also provides other feature openings such as the opening 46P for installation of each of the multiple of tie-down pans 46 (Figure 5E).

The stiffeners 40 may be of various cross-sectional shapes. Although the cross-sectional shapes are illustrated as a "Z," shape they may include other cross- sectional configurations. Such other shapes may include but are not limited to "I", "L", "C", "J" etc.

The edge stiff eners 42 are generally of a jogged or step- shape and are longitudinally arranged to facilitate attachment of each panel to an adjacent panel or other interface (FigurelB). Various seals, raised splice straps as well as bonded-on carbon spacers, "form-in-place gaskets" and such like may additionally be provided to provide a moisture seal interface.

Each of the multiple of roller trough stiffeners 44 receive a reversible roller assembly 50 (Figures IB, 1C and 3). Four rows of reversible roller assembly 50 are typical and include a locking feature which secures the reversible roller assembly 50 in both the "roller-up" and stowed positions. A typical composite floor panel 32 has two full length trough stiffeners 44 that receive the reversible roller assembly 50.

A multiple of end cap members 52 (Figure 4) are arranged generally transverse to the stiffeners 40, 42, 44 to seal the composite floor panel 32. The end cap members 52 closes-off the lateral open end section 54 of the composite floor panel 32. The end cap members 52 double as transverse stiffeners to reinforce the open end sections 54 and may also include various stowable lifting handles. Various seals, raised splice straps as well as bonded-on carbon spacers, "form-in-place gaskets" and such like may additionally be provided in the end cap members 52 to provide a moisture seal interface.

Figures 5A-5E illustrates an exemplary embodiment of a manufacturing sequence for the composite floor panel 32 using an in-situ tape placement process (tape placement process schematically illustrated in Figure 6).

Referring to Figure 5 A, a multiple of longitudinal mandrels 60 are assembled with the support structure 34. The longitudinal mandrels 60 may be of various shapes. The longitudinal mandrels 60 in one non-limiting embodiment are shaped to fill the void defined between: each of the multiple of stiffeners 40; the multiple edge stiffeners 42; within the multiple of roller trough stiffeners 44; and about an outer edge of the edge stiffeners 42 to provide a smoothed winding surface. That is, the longitudinal mandrels 60 fill voids in the support structure 34 so as to react the tape placement roller (Figure 6). A winding mandrel 62 is removably assembled transverse to the longitudinal mandrels 60 to form a mandrel assembly 64. The mandrel assembly 64 retains and positions the support structure 34 (Figure 5B). Various mandrel assembly 64 structures may be utilized. The mandrel assembly 64 defines an axis of rotation M (Figure 5C) about which the mandrel assembly 64 is rotated to wind the tape skin 36. The wound tape 36 is applied through in-situ processing of thermoplastic tape or tow to successively "weld" one layer of tape such as IM7/PEEK tape at a time over the support structure 34 to yield a nearly fastener-less skin surface. The in-situ process joins one thermoplastic layer to another on the fly, to thereby minimize or eliminate autoclave preparation and subsequent post processing. One such in-situ process is that provided by ADC Acquisition Company, doing business as Automated Dynamics, of Schenectady, NY, USA. It should be understood that multiple plies or layers of thermoplastic tape or tow having various or no overlap may be applied to provide a desired rigidity as generally understood.

Referring to Figure 5D, the mandrel assembly 64 is disassembled and the multiple of longitudinal mandrels 60 are longitudinally extracted from the support structure 34. That is, the longitudinal mandrels 60 slide out of the support structure subsequent to removal of the winding mandrel 62. The longitudinal open ended construction of the composite floor panel 32 facilitates removal of the longitudinal mandrels 60.

Once the mandrel assembly 64 is disassembled and the multiple of longitudinal mandrels 60 are extracted from the support structure 34, the wound tape 36 is trimmed. The wound tape 36 is trimmed to, for example, open the roller trough stiffeners 44 and provide an opening 46P for installation of each of the multiple of tie-down pans 46 (Figure 5E). The wound tape skin 36 is also trimmed from the outer edge of the edge stiffeners 42 to essentially define the separate tape upper skin 48 A and tape lower skin 48B which were heretofore contiguous.

Referring to Figure 5E, the multiple of end cap members 52 are arranged generally transverse to the stiffeners 40, 42, 44 to seal the composite floor panel 32. The end cap members 52 close-off the open end sections 54 of the composite floor panel 32. The multiple of tie-down pans 46 are also installed in each respective opening 46P (Figure 5F). The multiple of tie-down pans 46 may be non-flush with the tape upper skin 48 A (Figure 5G). This secondary detail component installation arrangement facilitates extraction of the longitudinal mandrels 60 as potential trapped areas are eliminated were detail components earlier integrated into the composite floor panel 32. Detail components other than tie-down pans 46 such as floor mounted equipment and cargo hook doors may be readily incorporated into the composite floor panel 32 in a similar manner. The non-flush arrangement is lightweight and provides uncomplicated manufacturability.

The process eliminates fasteners; utilizes low cost thermoforming and tape placement process to build detail parts; provides the potential for low cost commodity parts; utilizes a tough resin which offers impact resistance; and utilizes thermoplastics which can be reconsolidated and reformed if required. The thermoplastic panel is superior in cost and impact strength to conventional thermoset composite sandwich panels with the potential to reduce weight by 25%, as compared with riveted or machined aluminum floors.

The method of manufacture also provides various options to achieve non- flush or flush component integration.

Referring to Figure 7, another non-limiting embodiment facilitates flush mounting of the multiple of tie-down pans 46. The tie-down pans 46 are installed from a lower surface such that the tie-down pans 46 are flush with an upper surface of the support structure 34'. The lower skin 48B is then bonded to the support structure 34 with a secondary bond subsequent to mandrel removal.

Referring to Figure 8, another non-limiting embodiment facilitates flush mounting the multiple of tie-down pans 46 by "joggling" the tape upper skin 48A during winding. That is, the tape upper skin 48A is shifted vertically or "jogged" so as to accommodate each of the multiple of tie-down pans 46. The tape upper skin 48 A provides a step-like shape adjacent each tie-down pain 46. Alternatively, a lesser number of layers or plies may be provided in the localized area.

Referring to Figure 9A, another embodiment facilitates flush mounting the multiple of tie-down pans 46 as the pans 46 are incorporated within a tube and block subassembly 70. The subassembly 70 reacts the tape placement roller pressure (Figure 6) and essentially replaces a longitudinal mandrel at that location. That is, the tube and block subassembly 70 (Figure 9B) is essentially a longitudinal support which replaces individual tie-down pans to facilitate winding of the tape 36 thereon.

Referring to Figure 1OA, another embodiment facilitates flush mounting of the multiple of tie-down pans 46 with a tube and pan subassembly 80. The tube and pan subassembly 80 is generally as the above tube and block subassembly 70 with a lighter weight open structure (Figure 10B). The open structure includes transverse supports 82 which are relatively closely spaced to support the tape placement roller pressure (Figure 6).

It should be understood that relative positional terms such as "forward," "aft," "upper," "lower," "above," "below," and the like are with reference to the normal operational attitude of the vehicle and should not be considered otherwise limiting.

It should be understood that although a particular component arrangement is disclosed in the illustrated embodiment, other arrangements will benefit from the instant invention.

Although particular step sequences are shown, described, and claimed, it should be understood that steps may be performed in any order, separated or combined unless otherwise indicated and will still benefit from the present invention. The foregoing description is exemplary rather than defined by the limitations within. Many modifications and variations of the present invention are possible in light of the above teachings. The disclosed embodiments of this invention have been disclosed, however, one of ordinary skill in the art would recognize that certain modifications would come within the scope of this invention. It is, therefore, to be understood that within the scope of the appended claims, the invention may be practiced otherwise than as specifically described. For that reason the following claims should be studied to determine the true scope and content of this invention.

Claims

1. A composite panel comprising: a support structure; and a tape skin formed of tape wound about said support structure.

2. The panel as recited in claim 1, wherein said support structure includes a multiple of stiff eners.

3. The panel as recited in claim 1, wherein said support structure includes a multiple of roller trough stiff eners.

4. The panel as recited in claim 1, further comprising a multiple of tie-down pans mounted to said skin.

5. The panel as recited in claim 1, wherein said tape skin includes a multiple of layers.

6. The panel as recited in claim 1, wherein said support structure defines an open end section.

7. The panel as recited in claim 6, further comprising an end cap member transverse to said support structure configured to close said open end section.

8. The panel as recited in claim 6, wherein said open end section is defined transverse to a multiple of stiffeners which define said support structure.

9. The panel as recited in claim 8, wherein said open end section is defined in part by a multiple of roller trough stiffeners.

10. A method of manufacturing a composite panel comprising:

(A) assembling a support structure with a multiple of longitudinal mandrels;

(B) assembling a mandrel assembly with the multiple of longitudinal mandrels to retain the support structure and define an axis of rotation;

(C) winding a tape about the assembled mandrel assembly while the mandrel assembly is rotated about the axis of rotation to bond the tape with the support structure to form a tape skin onto the support structure to thereby form a composite panel; and (D) disassembling the mandrel assembly from the composite panel; and

11. A method as recited in claim 10, wherein said step (A) further comprises:

(a) assembling at least one of the multiple of longitudinal mandrels into a void defined by at least one of a multiple of stiffeners which at least partially define the support structure.

12. A method as recited in claim 10, wherein said step (D) further comprises:

(a) axially sliding the multiple of longitudinal mandrels out of the composite panel generally parallel to the support structure.

13. A method as recited in claim 10, further comprising:

(a) trimming the composite panel tape skin to form a tape upper skin and a tape lower skin.

14. A method as recited in claim 13, further comprising:

(a) trimming a tie-down pan opening; and

(b) trimming an opening defined by a roller trough stiffener.

15. A method as recited in claim 14, further comprising:

(c) mounting a tie down pan into the tie-down pan opening; and

(d) mounting an end cap member configured to close an open end section of the composite panel transverse to said support structure, the end cap member in contact with the tape upper skin and the tape lower skin.