WO2008111997A1 - Panneau sandwich composite et procédé de fabrication de celui-ci - Google Patents

Panneau sandwich composite et procédé de fabrication de celui-ci Download PDF

Info

Publication number
WO2008111997A1
WO2008111997A1 PCT/US2007/074080 US2007074080W WO2008111997A1 WO 2008111997 A1 WO2008111997 A1 WO 2008111997A1 US 2007074080 W US2007074080 W US 2007074080W WO 2008111997 A1 WO2008111997 A1 WO 2008111997A1
Authority
WO
WIPO (PCT)
Prior art keywords
skin
core
fiber
composite panel
axis
Prior art date
Application number
PCT/US2007/074080
Other languages
English (en)
Inventor
David W. Johnson
Original Assignee
Ebert Composites Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US11/780,392 external-priority patent/US7731046B2/en
Application filed by Ebert Composites Corporation filed Critical Ebert Composites Corporation
Publication of WO2008111997A1 publication Critical patent/WO2008111997A1/fr

Abstract

La présente invention concerne un procédé de fabrication d'un panneau composite comprenant les étapes consistant à fabriquer un panneau composite ayant une première peau, une seconde peau, un noyau et une pluralité de regroupements distincts de fibres d'axe Z qui s'étendent à travers le noyau de la première peau vers la seconde peau, les fibres d'axe Z comprenant des extrémités opposées se terminant respectivement au niveau de la première peau et de la seconde peau et étant intégrées dans la première peau et la seconde peau; et à créer des chapelets structurels dans le panneau composite en retirant la seconde peau et sensiblement l'ensemble du noyau et les fibres d'axe Z en descendant vers la première peau ou à côté de celle-ci.
PCT/US2007/074080 2006-07-26 2007-07-23 Panneau sandwich composite et procédé de fabrication de celui-ci WO2008111997A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US82038006P 2006-07-26 2006-07-26
US60/820,380 2006-07-26
US11/780,392 2007-07-19
US11/780,392 US7731046B2 (en) 2001-04-06 2007-07-19 Composite sandwich panel and method of making same

Publications (1)

Publication Number Publication Date
WO2008111997A1 true WO2008111997A1 (fr) 2008-09-18

Family

ID=39759787

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2007/074080 WO2008111997A1 (fr) 2006-07-26 2007-07-23 Panneau sandwich composite et procédé de fabrication de celui-ci

Country Status (1)

Country Link
WO (1) WO2008111997A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN101508190B (zh) * 2009-03-26 2012-05-23 北京航空航天大学 具有纤维束的增强泡沫夹层结构以及采用缝纫-热膨胀固化成型的制备方法
EP3470214A1 (fr) * 2017-10-10 2019-04-17 Groz-Beckert KG Dispositif et procédé de fabrication d'une partie support comportant une pluralité des faisceaux de fibres

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20020153084A1 (en) * 2001-04-06 2002-10-24 Johnson David W. Method of inserting z-axis reinforcing fibers into a composite laminate
US6808142B2 (en) * 2000-06-06 2004-10-26 Mitsubishi Heavy Industries, Ltd. Aircraft with a plurality of upper and lower cabins functioning as cargo compartments or passenger cabins and method of loading cargos for aircraft
US20050074593A1 (en) * 2000-12-27 2005-04-07 Webcore Technologies, Inc. Fiber reinforced composite cores and panels

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6808142B2 (en) * 2000-06-06 2004-10-26 Mitsubishi Heavy Industries, Ltd. Aircraft with a plurality of upper and lower cabins functioning as cargo compartments or passenger cabins and method of loading cargos for aircraft
US20050074593A1 (en) * 2000-12-27 2005-04-07 Webcore Technologies, Inc. Fiber reinforced composite cores and panels
US20020153084A1 (en) * 2001-04-06 2002-10-24 Johnson David W. Method of inserting z-axis reinforcing fibers into a composite laminate

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN101508190B (zh) * 2009-03-26 2012-05-23 北京航空航天大学 具有纤维束的增强泡沫夹层结构以及采用缝纫-热膨胀固化成型的制备方法
EP3470214A1 (fr) * 2017-10-10 2019-04-17 Groz-Beckert KG Dispositif et procédé de fabrication d'une partie support comportant une pluralité des faisceaux de fibres
WO2019072641A1 (fr) * 2017-10-10 2019-04-18 Groz-Beckert Kommanditgesellschaft Dispositif et procédé de fabrication d'un élément de support présentant plusieurs faisceaux de fibres
US10858771B2 (en) 2017-10-10 2020-12-08 Groz-Beckert Kg Device and method for producing a carrier part having a plurality of fiber bundles
JP2020537059A (ja) * 2017-10-10 2020-12-17 グロツ・ベッケルト コマンディートゲゼルシャフト 複数の繊維束を備えた担体部材を製造するための装置及び方法
RU2762030C2 (ru) * 2017-10-10 2021-12-14 Гроц-Беккерт Коммандитгезелльшафт Устройство и способ для изготовления несущего элемента, снабженного множеством пучков волокон
JP7220016B2 (ja) 2017-10-10 2023-02-09 グロツ・ベッケルト コマンディートゲゼルシャフト 複数の繊維束を備えた担体部材を製造するための装置及び方法

Similar Documents

Publication Publication Date Title
US7731046B2 (en) Composite sandwich panel and method of making same
US7846528B2 (en) Composite laminate structure
US20050025948A1 (en) Composite laminate reinforced with curvilinear 3-D fiber and method of making the same
CA2746636C (fr) Structure composite stratifiee
US8002919B2 (en) Method of inserting Z-axis reinforcing fibers into a composite laminate
JP4266990B2 (ja) Ｚ軸繊維の頂部端部および底部端部を、複合積層体の頂部表面および底部表面それぞれに締め付ける方法
US7056576B2 (en) 3D fiber elements with high moment of inertia characteristics in composite sandwich laminates
AU2002319748A1 (en) Method of clinching top and bottom ends of z-axis fibers into the respective top and bottom surfaces of a composite laminate
WO2008111997A1 (fr) Panneau sandwich composite et procédé de fabrication de celui-ci
JP2004536726A5 (fr)
AU2005237155B2 (en) Composite laminate structure

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 07873975

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

NENP Non-entry into the national phase

Ref country code: RU

122 Ep: pct application non-entry in european phase

Ref document number: 07873975

Country of ref document: EP

Kind code of ref document: A1