WO2008069865A1 - Styrene acrylonitrile copolymer foam with infrared attenuating agents - Google Patents
Styrene acrylonitrile copolymer foam with infrared attenuating agents Download PDFInfo
- Publication number
- WO2008069865A1 WO2008069865A1 PCT/US2007/021954 US2007021954W WO2008069865A1 WO 2008069865 A1 WO2008069865 A1 WO 2008069865A1 US 2007021954 W US2007021954 W US 2007021954W WO 2008069865 A1 WO2008069865 A1 WO 2008069865A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- foam
- polymer
- weight
- less
- polymer composition
- Prior art date
Abstract
Description
Claims