WO2008030313A1 - Methods for determining temperature value indicative of resin stickiness from data generated by polymerization reaction monitoring - Google Patents
Methods for determining temperature value indicative of resin stickiness from data generated by polymerization reaction monitoring Download PDFInfo
- Publication number
- WO2008030313A1 WO2008030313A1 PCT/US2007/017730 US2007017730W WO2008030313A1 WO 2008030313 A1 WO2008030313 A1 WO 2008030313A1 US 2007017730 W US2007017730 W US 2007017730W WO 2008030313 A1 WO2008030313 A1 WO 2008030313A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- temperature
- reactor
- reaction
- reference temperature
- melt
- Prior art date
Abstract
Description
Claims