WO2007132436A3 - Process for the production of fine-grained carbon steel strips and strips thus obtainable - Google Patents
Process for the production of fine-grained carbon steel strips and strips thus obtainable Download PDFInfo
- Publication number
- WO2007132436A3 WO2007132436A3 PCT/IB2007/051889 IB2007051889W WO2007132436A3 WO 2007132436 A3 WO2007132436 A3 WO 2007132436A3 IB 2007051889 W IB2007051889 W IB 2007051889W WO 2007132436 A3 WO2007132436 A3 WO 2007132436A3
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- temperature
- strip
- ranging
- strips
- rolling
- Prior art date
Abstract
The present invention relates to a process for the production of Carbon steel strips with a mainly fine grained ferrite microstructure, comprising the following steps : • transferring a strip, optionally coiled in the form of a coil, having a thickness ranging from 1.5 to 15 mm, of steel having a composition (expressed in mass percent) comprising: C 0.001-0.20; Mn 0.05-1.9; Si 0.002- 0.35; Al<0.06; S<0.03; P<0.1; N 0.003-0.02, the remaining part being, unavoidable impurities apart, substantially Fe, to a first reel placed near the ingoing side of a reversible rolling mill, having at least one stand and equipped at the outgoing side thereof with a second reel; • adjusting the temperature of the (optionally rapidly heated and oiled) strip, optionally under inert or non-oxidizing atmosphere, so that the start of the rolling occurs in ferritic field, preferably at a temperature higher than 550 °C and lower than (Ar1 - 20) °C; • controlled rolling in ferritic phase at a temperature adjusted in a range of ± 300C, by suitable heating, cooling and/or holding treatments, so as to accumulate an overall deformation εtot ranging from 0.7 to 1.6 in a temperature interval ranging from 550 °C to (Ar1 - 2O) °C; • in-line treating of the strip, optionally under inert or non-oxidizing atmosphere, upon reaching the desired end thickness, ranging from 0.3 to 7.0 mm, according to one of the following modes: - coiling at a temperature equal to or lower - at most of 40 °C - than the end-of-rolling one, followed by slow cooling of the coil - heating to a temperature <Ac1, and subsequent coiling thereat. - heating the strip up to a temperature in which ferrite and austenite phases coexist, followed by cooling the strip down to coiling temperatures lower than that of the start of martensite formation (Ms). Subject of the present invention are also the strips and the sheets of a thickness ranging from 0.3 to 7 mm, obtainable via said process.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
ITRM20060262 ITRM20060262A1 (en) | 2006-05-17 | 2006-05-17 | PROCEDURE FOR THE PRODUCTION OF FINE CARBON STEEL RIBBONS AND RIBBONS AS SUCH POSSIBLE |
ITRM2006A000262 | 2006-05-17 |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2007132436A2 WO2007132436A2 (en) | 2007-11-22 |
WO2007132436A3 true WO2007132436A3 (en) | 2009-05-07 |
Family
ID=38610654
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/IB2007/051889 WO2007132436A2 (en) | 2006-05-17 | 2007-05-17 | Process for the production of fine-grained carbon steel strips and strips thus obtainable |
Country Status (2)
Country | Link |
---|---|
IT (1) | ITRM20060262A1 (en) |
WO (1) | WO2007132436A2 (en) |
Families Citing this family (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2009072303A1 (en) | 2007-12-05 | 2009-06-11 | Honda Motor Co., Ltd. | High-strength steel sheet, automotive strengthening member comprising the same, and process for producing automotive strengthening member |
AT509707B1 (en) * | 2010-05-04 | 2011-11-15 | Siemens Vai Metals Tech Gmbh | METHOD FOR HOT ROLLING OF STEEL STRIPS AND HOT ROLLING STRIP |
US11885025B2 (en) * | 2018-12-11 | 2024-01-30 | Nippon Steel Corporation | High-strength steel sheet having excellent moldability and impact resistance, and method for manufacturing high-strength steel sheet having excellent moldability and impact resistance |
Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4466842A (en) * | 1982-04-03 | 1984-08-21 | Nippon Steel Corporation | Ferritic steel having ultra-fine grains and a method for producing the same |
JPS59166651A (en) * | 1983-03-10 | 1984-09-20 | Nippon Steel Corp | Two-phase high tensile hot rolled steel plate comprising two-phase structure of ultra-fine grain ferrite phase and hardening phase and preparation tehereof |
EP0524162A2 (en) * | 1991-07-17 | 1993-01-20 | CENTRE DE RECHERCHES METALLURGIQUES CENTRUM VOOR RESEARCH IN DE METALLURGIE Association sans but lucratif | Method of manufacturing a thin sheet of low carbon steel |
DE19600990A1 (en) * | 1996-01-14 | 1997-07-17 | Thyssen Stahl Ag | Process for hot rolling steel strips |
JPH10168542A (en) * | 1996-12-12 | 1998-06-23 | Nippon Steel Corp | High strength steel excellent in low temperature toughness and fatigue strength and its production |
EP0903413A1 (en) * | 1997-09-22 | 1999-03-24 | National Research Institute For Metals | Fine-grained ferrite-based structural steel and manufacturing process of this steel |
JP2000158006A (en) * | 1998-11-26 | 2000-06-13 | Ishikawajima Harima Heavy Ind Co Ltd | Equipment for refining ferrite grain |
-
2006
- 2006-05-17 IT ITRM20060262 patent/ITRM20060262A1/en unknown
-
2007
- 2007-05-17 WO PCT/IB2007/051889 patent/WO2007132436A2/en active Application Filing
Patent Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4466842A (en) * | 1982-04-03 | 1984-08-21 | Nippon Steel Corporation | Ferritic steel having ultra-fine grains and a method for producing the same |
JPS59166651A (en) * | 1983-03-10 | 1984-09-20 | Nippon Steel Corp | Two-phase high tensile hot rolled steel plate comprising two-phase structure of ultra-fine grain ferrite phase and hardening phase and preparation tehereof |
EP0524162A2 (en) * | 1991-07-17 | 1993-01-20 | CENTRE DE RECHERCHES METALLURGIQUES CENTRUM VOOR RESEARCH IN DE METALLURGIE Association sans but lucratif | Method of manufacturing a thin sheet of low carbon steel |
DE19600990A1 (en) * | 1996-01-14 | 1997-07-17 | Thyssen Stahl Ag | Process for hot rolling steel strips |
JPH10168542A (en) * | 1996-12-12 | 1998-06-23 | Nippon Steel Corp | High strength steel excellent in low temperature toughness and fatigue strength and its production |
EP0903413A1 (en) * | 1997-09-22 | 1999-03-24 | National Research Institute For Metals | Fine-grained ferrite-based structural steel and manufacturing process of this steel |
JP2000158006A (en) * | 1998-11-26 | 2000-06-13 | Ishikawajima Harima Heavy Ind Co Ltd | Equipment for refining ferrite grain |
Non-Patent Citations (2)
Title |
---|
DATABASE INSPEC [online] THE INSTITUTION OF ELECTRICAL ENGINEERS, STEVENAGE, GB; 2006, SALVATORI I: "Ultrafine grained steels by advanced thermomechanical processes and severe plastic deformations", XP002457200, Database accession no. 9183206 * |
METALLURGIA ITALIANA ASSOC. ITALIANA DI METALLURGIA ITALY, no. 5, 4 November 2005 (2005-11-04), pages 41 - 47, ISSN: 0026-0843 * |
Also Published As
Publication number | Publication date |
---|---|
WO2007132436A2 (en) | 2007-11-22 |
ITRM20060262A1 (en) | 2007-11-18 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP2103697B1 (en) | High carbon hot-rolled steel sheet | |
EP2880190B1 (en) | Method of production of grain-oriented silicon steel sheet grain oriented electrical steel sheet and use thereof | |
JP5082451B2 (en) | Method for producing high-strength cold-rolled steel sheet excellent in deep drawability and ductility, and method for producing high-strength hot-dip galvanized steel sheet using the cold-rolled steel sheet | |
KR101461583B1 (en) | Method for manufacturing flat steel products from a multiphase steel microalloyed with boron | |
KR20150084062A (en) | High-formability and super-strength hot galvanizing steel plate and manufacturing method thereof | |
EP2878689B1 (en) | Method of producing grain-oriented electrical steel sheet | |
RU2016151391A (en) | METHOD FOR PRODUCING HIGH-STRENGTH STEEL SHEET AND THE RECEIVED SHEET | |
ES2325961T3 (en) | PROCEDURE FOR MANUFACTURING STEEL FLAT PRODUCTS FROM A STEEL FORMING A MARTENSITICAL STRUCTURE. | |
IN2015DN02521A (en) | ||
JP5845275B2 (en) | Method for producing grain-oriented silicon steel having magnetic performance | |
WO2010074463A3 (en) | High carbon steel sheet with superior heat treatment characteristics, and manufacturing method thereof | |
RU2011142785A (en) | METHOD FOR PRODUCING A TEXTURED ELECTRICAL STEEL SHEET, A TEXTURED ELECTRICAL STEEL SHEET FOR A TAPE CORE AND A TAPE CORE | |
CA2537560A1 (en) | Hot rolled steel sheet and method for manufacturing the same | |
CA2496212A1 (en) | High strength cold rolled steel sheet and method for manufacturing the same | |
EP3164519B1 (en) | Method for producing a high strength coated steel sheet having improved strength, formability | |
CN109906277A (en) | The manufacturing method of orientation electromagnetic steel plate | |
US10323293B2 (en) | High-carbon hot rolled steel sheet with excellent hardenability and small in-plane anistropy and method for manufacturing the same | |
WO2007132436A3 (en) | Process for the production of fine-grained carbon steel strips and strips thus obtainable | |
US20220010400A1 (en) | Method of manufacturing non-oriented electrical steel sheet | |
EP1453984B8 (en) | Method for the production of hot strip or sheet from a micro-alloyed steel | |
KR101344651B1 (en) | Manufacturing method of steel-sheet | |
CN109923222A (en) | The manufacturing method of orientation electromagnetic steel plate | |
KR100561144B1 (en) | Process for the inhibition control in the production of grain-oriented electrical sheets | |
KR20190049294A (en) | Ultra high strength steel sheet having good cold workability and its manufacturing method | |
WO2003076675A1 (en) | Steel plate subjected to heat treatment and process for producing the same |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 07735953 Country of ref document: EP Kind code of ref document: A2 |
|
DPE1 | Request for preliminary examination filed after expiration of 19th month from priority date (pct application filed from 20040101) | ||
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 07735953 Country of ref document: EP Kind code of ref document: A2 |