WO2007010237A1

WO2007010237A1 - Kickoff plugs and methods of directional drilling and forming kickoff plugs

Info

Publication number: WO2007010237A1
Application number: PCT/GB2006/002657
Authority: WO
Inventors: Mark R. Savery; Ashok K. Santra; Bradley L. Todd
Original assignee: Halliburton Energy Services, Inc.; Curtis, Philip, Anthony
Priority date: 2005-07-22
Filing date: 2006-07-18
Publication date: 2007-01-25

Abstract

Degradable kickoff plugs are provided, which may comprise a degradable material and an acid-base cement. Methods of drilling a well bore in a subterranean formation comprising placing a self-degrading kickoff plug or the like in the well bore are provided. An example of a method comprises: providing a self-degrading cement composition that comprises a degradable material, an acid source, a base source, and a water source; placing the self-degrading cement composition in a desired location in a well bore that penetrates a subterranean formation; and allowing the self-degrading cement composition to set to form a hardened kickoff plug.

Description

KICKOFF PLUGS AND METHODS OF DIRECTIONAL DRILLING AND

FORMING KICKOFF PLUGS

BACKGROUND

The present invention relates to subterranean drilling operations. More particularly, the present invention relates to methods of drilling a well bore in a subterranean formation comprising placing a self-degrading kickoff plug or the like in the well bore.

During drilling of a well for production of oil, gas, or other fluids, it may be desirable to perform directional drilling, which may result in drilling of a deviated well bore. Directional drilling operations may be conducted for a variety of reasons, including, but not limited to, evading obstructions (e.g., drilling equipment that may have become stuck in the original well bore), drilling multiple wells from a single vertical well bore, or increasing production by increasing flow from adjacent subterranean formations.

Directional drilling operations may involve the setting of a kickoff plug, or the like, in a primary well bore. A kickoff plug may have a length ranging from about 50 to about 500 feet, and may comprise a cement composition. The kickoff plug typically is set in the well bore by lowering a drillstring or an open-ended tubing string to the desired depth and pumping a cement composition into the well bore. The cement composition may set to form a plug. After the cement plug has been formed, a drillstring may be used to reinitiate drilling operations. The drillstring and drill bit intentionally may be contacted with the plug, so as to thereby deflect the drill string and change the direction in which subsequent drilling proceeds.

The use of conventional kickoff plugs may be problematic, for a variety of reasons. Conventional kickoff plugs may be difficult to remove from the primary well bore, and may block the well bore and/or impair production of hydrocarbons from the subterranean formation. Even where removal of the kickoff plug from the well bore is possible, the removal procedure may require additional trips into the well bore, adding cost to the drilling operation. Furthermore, in cases in which a mechanical kickoff plug assembly is used, retrieving the kickoff plug by pulling it back up through the well bore may be problematic, because the well bore may lack sufficient space through which to pull the kickoff plug without damaging upper portions of the well bore and/or casing strings set therein.

Conventional approaches to solving these problems have included, inter alia, the use of a salt plug which, once used, can be dissolved by the introduction of an acidic solution into the well bore. However, significant drawbacks may be associated with this approach, including, but not limited to, environmental and occupational safety risks that may result from the use of large quantities of the acidic solution, the risk that a portion of the acidic solution may escape into other regions of the subterranean formation, and the delay of waiting for the acidic solution to dissolve the plug.

Another conventional approach involves drilling through the kickoff plug. However, this approach may require the use of other drilling equipment (e.g., drilling strings capable of producing a greater force, and a stabilizer assembly to keep the drill string from being deflected by the plug) that may further complicate the drilling operation and/or risk damage to the well bore.

SUMMARY

An example of a composition of the present invention is a degradable kickoff plug, comprising: a degradable material; and an acid-base cement.

Another example of a composition of the present invention is a degradable kickoff plug formed by a method comprising: providing a self-degrading cement composition that comprises a degradable material, an acid source, a base source, and a water source; placing the self-degrading cement composition in a desired location in a well bore that penetrates a subterranean formation; and allowing the self-degrading cement composition to set to form a hardened kickoff plug.

An example of a method of the present invention is a method comprising: providing a self-degrading cement composition that comprises a degradable material, an acid source, a base source, and a water source; placing the self-degrading cement composition in a desired location in a well bore that penetrates a subterranean formation; and allowing the self- degrading cement composition to set to form a hardened kickoff plug.

Another example of a method of the present invention is a method of placing a degradable kickoff plug at a desired location in a well bore penetrating a subterranean formation, the method comprising: providing a self-degrading cement composition that comprises a degradable material, an acid source, a base source, and a water source; placing the self-degrading cement composition in the desired location in the well bore; and allowing the self-degrading cement composition to set to form the degradable kickoff plug. Another example of a method of the present invention is a method of drilling a directional hole through the side of a well bore penetrating a subterranean formation, the method comprising: providing a self-degrading cement composition that comprises a degradable material, an acid source, a base source, and a water source; placing the self- degrading cement composition in a desired location in the well bore; allowing the self- degrading cement composition to set to form a hardened kickoff plug; contacting the hardened kickoff plug with a drill string such that the path of the drill string deviates away from the well bore; and allowing the drill string to continue drilling a directional hole that deviates from the well bore.

The features and advantages of the present invention will be apparent to those skilled in the art. While numerous changes may be made by those skilled in the art, such changes are within the spirit of the invention.

BRIEF DESCRIPTION OF THE DRAWINGS

These drawings illustrate certain aspects of some of the embodiments of the present invention, and should not be used to limit or define the invention.

Figure 1 illustrates the relationship of the time- and temperature-dependence of the degradation of a degradable material in one embodiment of the present invention.

Figure 2 illustrates the relationship of the time- and temperature-dependence of the degradation of a degradable material in another embodiment of the present invention.

Figure 3 illustrates an example of an oil/gas reservoir in a subterranean formation.

Figure 4 illustrates an example of a well bore in the subterranean formation of Figure 3.

Figure 5 illustrates the well bore of Figure 4, having disposed therein an embodiment of a self-degrading cement composition of the present invention.

Figure 6 illustrates the well bore of Figure 5, in which the self-degrading cement composition has set to form a set cement.

Figure 7 illustrates the well bore of Figure 6, in which a directional hole has been drilled.

Figure 8 illustrates the well bore of Figure 7, in which the set cement has completely degraded, in accordance with an embodiment of the present invention.

Figure 9 illustrates an example of a well bore, having casing disposed therein, in the subterranean formation of Figure 3. Figure 10 illustrates the well bore of Figure 9, having disposed therein an embodiment of a self-degrading cement composition of the present invention.

Figure 11 illustrates the well bore of Figure 10, in which the self-degrading cement composition has set to form a set cement.

Figure 12 illustrates the well bore of Figure 11, in which a directional hole has been drilled.

Figure 13 illustrates the well bore of Figure 12, in which the set cement has completely degraded, in accordance with an embodiment of the present invention. DESCRIPTION OF PREFERRED EMBODIMENTS

1. Self-Degrading Cement Compositions

The self-degrading cement compositions utilized in the methods of the present invention generally comprise a degradable material, an acid source, a base source, and a water source. In certain embodiments of the present invention, the self-degrading cement composition initially will set to form a hardened mass that provides sufficient structural integrity to permit kickoff to occur, after which the degradable material may degrade either entirely, or partially. In certain embodiments in which the degradable material degrades only partially, such partial degradation may create voids within the hardened mass of the self- degrading cement composition that may permit fluid communication through the region of the well bore in which it is placed.

A broad variety of acid sources and base sources may be suitable for use in the self- degrading cement compositions utilized in the methods of the present invention. Examples of suitable acid sources include, inter alia, magnesium chloride (MgCl₂), potassium phosphate monobasic (KH₂PO₄), phosphoric acid (H₃PO₄), magnesium sulfate (MgSO₄), sodium phosphate monobasic (NaH₂PO₄), and ammonium phosphate monobasic (NH₆PO₄). Examples of suitable base sources include, inter alia, magnesium oxide (MgO), and ammonia (NH₃). An example of a suitable source of magnesium oxide is commercially available from Martin Marietta under the trade name "MagChem 10." An example of a suitable source of potassium phosphate monobasic is commercially available from Fisher Scientific. Generally, an acid source and base source may be chosen that may react so as to form an acid-base cement. For example, magnesium oxide may be chosen as a base source, and potassium phosphate monobasic may be chosen as an acid source, so that in the presence of water they may react to produce an acid-base cement having the chemical formula MgKPO₄-OH₂O. As another example, magnesium oxide may be chosen as a base source, and magnesium chloride may be chosen as an acid source, so that in the presence of water they may react to produce an acid-base cement having three oxychloride phases; one oxychloride phase may have the chemical formula 5 Mg(OH)₂MgCl₂-SH₂O, which may be referred to as "5-form." As another example, magnesium oxide may be chosen as a base source, and phosphoric acid may be chosen as an acid source, so that in the presence of water they may react to produce an acid-base cement having the chemical formula MgHPO₄-SH₂O. As still another example, magnesium oxide may be chosen as a base source, and magnesium sulfate may be chosen as an acid source, so that in the presence of water they may react to produce an acid-base cement having four possible oxysulfate phases; one oxysulfate phase may have the chemical formula 3 Mg(OH)₂MgSO₄- 8H₂O, which may be referred to as "3-form." As still another example, magnesium oxide may be chosen as a base source, and ammonium phosphate monobasic may be chosen as an acid source, so that in the presence of water they may react to produce an acid-base cement having the chemical formula Mg(NH₄)PO₄-OH₂O. A broad variety of acid sources and base sources may be used, and a broad variety of acid- base cements may be produced, in accordance with the present invention, including, but not limited to, those acid sources, base sources, and acid-base cements that are disclosed in "Acid-Base Cements: Their Biomedical and Industrial Applications," by Alan D. Wilson and John W. Nicholson (Cambridge Univ. Press, 1993).

Generally, the acid source and base source may be present in the self-degrading cement composition in a stoichiometric amount. For example, in certain embodiments of the present invention wherein magnesium oxide is used as a base source and potassium phosphate monobasic is used as an acid source, their relative concentrations may be illustrated by Equation 1 below:

0.15 grams MgO + 0.52 grams KH₂PO₄ + 0.33 grams H₂O *^* 1 gram MgKPO₄-OH₂O

EQUATION 1 Equation 1 is exemplary only, and may be modified as one of ordinary skill in the art will recognize, with the benefit of this disclosure. For example, additional quantities of magnesium oxide may be included, in amounts in the range of from about 1% excess by weight to about 25% excess by weight.

The self-degrading cement compositions utilized in the methods of the present invention generally comprise a water source. The water source may comprise fresh water, salt water (e.g., water containing one or more salts dissolved therein), brine (e.g., saturated salt water), or seawater. Generally, any water source may be used, provided that it does not contain an excess of compounds that may adversely affect other components in the self- degrading cement composition.

A broad variety of materials may be suitable as the degradable materials in the self- degrading cement compositions utilized in the methods of the present invention. In certain embodiments of the present invention, the degradable material may be a degradable polymer. The terms "degradation" or "degradable" refer to both the two relatively extreme cases of hydrolytic degradation that the degradable material may undergo, e.g., heterogeneous (or bulk erosion) and homogeneous (or surface erosion), and any stage of degradation in between these two. This degradation can be a result of, inter alia, a chemical or thermal reaction, or a reaction induced by radiation. The terms "polymer" or "polymers" as used herein do not imply any particular degree of polymerization; for instance, oligomers are encompassed within this definition.

A polymer is considered to be "degradable" herein if it is capable of undergoing an irreversible degradation when used in subterranean applications, e.g., in a well bore. The term "irreversible" as used herein means that the degradable material should degrade in situ (e.g., within a well bore) but should not recrystallize or reconsolidate in situ after degradation (e.g., in a well bore).

The degradability of a degradable polymer often depends, at least in part, on its backbone structure. For instance, the presence of hydroiyzable and/or oxidizable linkages in the backbone often yields a material that will degrade as described herein. The rates at which such polymers degrade are dependent on the type of repetitive unit, composition, sequence, length, molecular geometry, molecular weight, morphology (e.g., crystallinity, size of spherulites, and orientation), hydrophilicity, hydrophobicity, surface area, and additives. Also, the environment to which the polymer is subjected may affect how it degrades, e.g., temperature, presence of moisture, oxygen, microorganisms, enzymes, pH, and the like.

Suitable examples of degradable polymers that may be used in accordance with the present invention include, but are not limited to, those described in the publication of Advances in Polymer Science, Vol. 157 entitled "Degradable Aliphatic Polyesters," edited by A. C. Albertsson, pages 1-138. Specific examples include homopolymers, random, block, graft, and star- and hyper-branched aliphatic polyesters. Such suitable polymers may be prepared by polycondensation reactions, ring-opening polymerizations, free radical polymerizations, anionic polymerizations, carbocationic polymerizations, coordinative ring- opening polymerizations, as well as by any other suitable process. Examples of suitable degradable polymers that may be used in conjunction with the methods of this invention include, but are not limited to, aliphatic polyesters; poly(lactides); poly(glycolides); poly(ε- caprolactones); poly(hydroxy ester ethers); poly(hydroxybutyrates); poly(anhydrides); polycarbonates; poly(orthoesters); poly(amino acids); poly(ethylene oxides); poly(phosphazenes); poly ether esters, polyester amides, polyamides, and copolymers or blends of any of these degradable polymers, and derivatives of these degradable polymers. The term "copolymer" as used herein is not limited to the combination of two polymers, but includes any combination of polymers, e.g., terpolymers and the like. As referred to herein, the term "derivative" is defined herein to include any compound that is made from one of the listed compounds, for example, by replacing one atom in the base compound with another atom or group of atoms. Of these suitable polymers, aliphatic polyesters such as poly(lactic acid), poly(anhydrides), poly(orthoesters), and poly(lactide)-co-poly(glycolide) copolymers are preferred. Poly(lactic acid) is especially preferred. Poly(orthoesters) also may be preferred. Other degradable polymers that are subject to hydrolytic degradation also may be suitable. One's choice may depend on the particular application and the conditions involved. Other guidelines to consider include the degradation products that result, the time for required for the requisite degree of degradation, and the desired result of the degradation (e.g., voids).

Aliphatic polyesters degrade chemically, inter alia, by hydrolytic cleavage. Hydrolysis can be catalyzed by either acids or bases. Generally, during the hydrolysis, carboxylic end groups may be formed during chain scission, which may enhance the rate of further hydrolysis. This mechanism is known in the art as "autocatalysis," and is thought to make polyester matrices more bulk-eroding. Suitable aliphatic polyesters have the general formula of repeating units shown below:

Formula I where n is an integer between 75 and 10,000 and R is selected from the group consisting of hydrogen, alkyl, aryl, alkylaryl, acetyl, heteroatoms, and mixtures thereof. In certain embodiments of the present invention wherein an aliphatic polyester is used, the aliphatic polyester may be poly(lactide). Poly(lactide) is synthesized either from lactic acid by a condensation reaction or, more commonly, by ring-opening polymerization of cyclic lactide monomer. Since both lactic acid and lactide can achieve the same repeating unit, the general term poly(lactic acid) as used herein refers to writ of formula I without any limitation as to how the polymer was made (e.g., from lactides, lactic acid, or oligomers), and without reference to the degree of polymerization or level of plasticization.

The lactide monomer exists generally in three different forms: two stereoisomers (L- and D-lactide) and racemic D,L-lactide (mero-lactide). The oligomers of lactic acid and the oligomers of lactide are defined by the formula:

where m is an integer in the range of from greater than or equal to about 2 to less than or equal to about 75. In certain embodiments, m may be an integer in the range of from greater than or equal to about 2 to less than or equal to about 10. These limits may correspond to number average molecular weights below about 5,400 and below about 720, respectively. The chirality of the lactide units provides a means to adjust, inter alia, degradation rates, as well as physical and mechanical properties. Poly(L-lactide), for instance, is a semicrystalline polymer with a relatively slow hydrolysis rate. This could be desirable in applications of the present invention in which a slower degradation of the degradable material is desired. Poly(D,L-lactide) may be a more amorphous polymer with a resultant faster hydrolysis rate. This may be suitable for other applications in which a more rapid degradation may be appropriate. The stereoisomers of lactic acid may be used individually, or may be combined in accordance with the present invention. Additionally, they may be copolymerized with, for example, glycolide or other monomers like ε-caprolactone, l,5-dioxepan-2-one, trimethylene carbonate, or other suitable monomers to obtain polymers with different properties or degradation times. Additionally, the lactic acid stereoisomers can be modified by blending high and low molecular weight polylactide or by blending polylactide with other polyesters. In embodiments wherein polylactide is used as the degradable material, certain preferred embodiments employ a mixture of the D and L stereoisomers, designed so as to provide a desired degradation time and/or rate. Examples of suitable sources of degradable material are poly(lactic acids) that are commercially available from Cargill Dow under the trade names "6250D" and "5639A."

Aliphatic polyesters useful in the present invention may be prepared by substantially any of the conventionally known manufacturing methods such as those described in U.S. Patent Nos. 6,323,307; 5,216,050; 4,387,769; 3,912,692; and 2,703,316, the relevant disclosures of which are incorporated herein by reference.

Polyanhydrides are another type of degradable polymer that may be suitable for use in the present invention. Polyanhydride hydrolysis proceeds, inter alia, via free carboxylic acid chain-ends to yield carboxylic acids as final degradation products. Their erosion time can be varied over a broad range of changes in the polymer backbone. Examples of suitable polyanhydrides include poly(adipic anhydride), poly(suberic anhydride), poly(sebacic anhydride), and poly(dodecanedioic anhydride). Other suitable examples include, but are not limited to, poly(maleic anhydride) and poly(benzoic anhydride).

The physical properties of degradable polymers may depend on several factors including, but not limited to, the composition of the repeat units, flexibility of the chain, presence of polar groups, molecular mass, degree of branching, crystallinity, and orientation. For example, short chain branches may reduce the degree of crystallinity of polymers while long chain branches may lower the melt viscosity and may impart, inter alia, extensional viscosity with tension-stiffening behavior. The properties of the material utilized further may be tailored by blending, and copolymerizing it with another polymer, or by a change in the macromolecular architecture (e.g., hyper-branched polymers, star-shaped, or dendrimers, and the like). The properties of any such suitable degradable polymers (e.g., hydrophobicity, hydrophilicity, rate of degradation, and the like) can be tailored by introducing select functional groups along the polymer chains. For example, poly(phenyllactide) will degrade at about one-fifth of the rate of racemic poly(lactide) at a pH of 7.4 at 55⁰C. One of ordinary skill in the art, with the benefit of this disclosure, will be able to determine the appropriate functional groups to introduce to the polymer chains to achieve the desired physical properties of the degradable polymers.

Whichever degradable material is used in the present invention, the degradable material may have any shape, including, but not limited to, particles having the physical shape of platelets, shavings, flakes, ribbons, rods, strips, spheroids, toroids, pellets, tablets, or any other physical shape. In certain embodiments of the present invention, the degradable material used may comprise a mixture of fibers and spherical particles. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the specific degradable material that may be used in accordance with the present invention, and the preferred size and shape for a given application.

In certain embodiments of the present invention, the degradable material used may comprise a self-degrading fiber that comprises an outer shell and a core liquid, wherein the outer shell comprises a degradable polymer and substantially retains the core liquid. In certain embodiments of the present invention, the outer shell may comprise a degradable polymer that is subject to hydrolytic degradation. The core liquid may comprise a liquid that is able to at least partially facilitate or catalyze the hydrolysis of the degradable polymer in the outer shell. Optionally, the self-degrading fiber may comprise a coating on the outer shell and/or a suitable additive within the core liquid, e.g., an additive chosen to interact with the degradable polymer, its degradation products, or the surrounding subterranean environment. In certain embodiments, the outer shell may be non-porous. Methods of making the self- degrading fibers described herein include any suitable method for forming hollow fibers. One such method involves extruding hollow fibers made from a desired degradable polymer, soaking the hollow fibers in a liquid that will be the core liquid, saturating the hollow fibers with the liquid, and drying the exterior of the outer core of the fibers in such a manner that the liquid is retained in the hollow fibers and becomes a core liquid. Another method involves extruding a spinning solution of a chosen degradable polymer from an annular slit of a double pipe orifice to form a sheath solution while simultaneously extruding a liquid through the inside pipe of the double pipe orifice, to form a core liquid within the hollow fibers. Another method involves using capillary action to place the core liquid in an already- formed suitable hollow fiber. Other suitable methods known in the art may be used as well.

In choosing the appropriate degradable material, one should consider the degradation products that will result, and choose a degradable material that will not yield degradation products that would adversely affect other operations or components utilized in that particular application. The choice of degradable material also may depend, at least in part, on the conditions of the well {e.g., well bore temperature). For instance, lactides have been found to be suitable for lower temperature wells, including those within the range of 60⁰F to 15O⁰F, and polylactides have been found to be suitable for well bore temperatures above this range.

In certain embodiments, the degradation of the degradable material could result in a final degradation product having the potential to affect the pH of the self-degrading cement compositions utilized in the methods of the present invention. For example, in certain embodiments wherein the degradable material is poly(lactic acid), the degradation of the poly(lactic acid) to produce lactic acid may alter the pH of the self-degrading cement composition. In certain embodiments, a buffer compound may be included within the self- degrading cement compositions utilized in the methods of the present invention in an amount sufficient to neutralize the final degradation product. Examples of suitable buffer compounds include, but are not limited to, calcium carbonate, magnesium oxide, ammonium acetate, and the like. One of ordinary skill in the art, with the benefit of this disclosure, will be able to identify the proper type and concentration of a buffer compound to include in the self- degrading cement composition for a particular application. An example of a suitable buffer compound comprises ammonium acetate and is commercially available from Halliburton Energy Services, Inc., under the trade name "BA-20."

The degradable materials utilized in the methods of the present invention may degrade over time at a rate that depends upon, among other things, the well bore temperature. Referring now to Figures 1 and 2, illustrated therein are graphical relationships of the time- and temperature-dependence of the degradation of certain degradable materials. The experiment in which these data were obtained was conducted as follows. A synthetic sea water solution was prepared by adding 41.953 grams of sea salt to one liter of deionized water. Next, 1.33 grams of sodium p-toluene sulfonate was added to the sea water solution to form a solution that was 6.919 mM in sodium p-toluene sulfonate. Next, one gram of a degradable material (6250D or 5639A) was placed in a one liter round-bottom flask containing 500 mL of synthetic sea water solution. A reflux condenser then was placed on each flask, and the contents were heated to 75, 85 or 95 ⁰C.

Using a disposable pipette, an aliquot was removed from each flask and placed in a 10 mL beaker. A carefully measured aliquot of 5.00 mL was removed and placed in a 50 mL round-bottom flask. The contents of the flasks were frozen by placing the flasks in liquid nitrogen. The flasks then were placed on a high vacuum line and the samples were allowed to dry overnight. After 24 hours, 1 mL of D₂O was added to each flask, and the contents of the flask were stirred until the residue re-dissolved. The freeze drying was repeated to remove D₂O and residual water. The remaining materials were dissolved in D₂O for NMR measurement.

The ¹H NMR spectrum was collected using a Bruker 300 Avance NMR spectrometer operating at 300 MHz, using a 5 mm QNP probe at various time intervals. The integrated area of the methyl proton peak of lactic acid was compared to the integrated area of the 6.919 mM sodium p-toluene sulfonate internal standard, and the lactic acid concentration for each point displayed in Figures 1 and 2 was calculated from that ratio. Figure 1 illustrates the time- and temperature-dependence of the generation of lactic acid caused by the degradation of 6250D, while Figure 2 illustrates the time- and temperature-dependence of the generation of lactic acid caused by the degradation of 5639A.

For certain embodiments of the self-degrading cement compositions utilized in the methods of the present invention wherein poly(lactic acid) is used as the degradable material, Table 1 below demonstrates the relationship that may exist between the concentration of poly(lactic acid) in the self-degrading cement composition and the degree of void space that may result in the solid mass after the poly(lactic acid) is allowed to degrade. TABLE 1

Optionally, the self-degrading cement compositions utilized in the methods of the present invention may include a set retarder. Generally, any set retarder may be used with the self-degrading cement compositions utilized in the methods of the present invention. Examples of set retarders suitable for use in the self-degrading cement compositions utilized in the methods of the present invention include, but are not limited to, sodium citrate and sodium borate. An example of a suitable commercially-available set retarder is Component R, available from Halliburton Energy Services, Inc., of Duncan, Oklahoma. Where included, the set retarder may be present in the self-degrading cement compositions utilized in the methods of the present invention in an amount in the range of from about 0.05% to about 10% by weight of the self-degrading cement composition. In certain embodiments, the set retarder may be present in the self-degrading cement compositions utilized in the methods of the present invention in an amount in the range of from about 0.1% to about 4% by weight of the self-degrading cement composition.

The self-degrading cement compositions utilized in the methods of the present invention optionally may include a strength-enhancing additive, which may act, among other things, to increase the stability of the set cement. Examples of these strength-enhancing additives include, but are not limited to, Newberyite, calcium carbonate, and Struvite. Where included, the strength-enhancing additive may be present in the self-degrading cement compositions utilized in the methods of the present invention in an amount in the range of from about 5% to about 60% by weight of the self-degrading cement composition. In certain embodiments, the strength-enhancing additive may be present in the self-degrading cement compositions utilized in the methods of the present invention in an amount in the range of from about 10% to about 30% by weight of the self-degrading cement composition. Examples of other additional additives that may be added to the self-degrading cement compositions of the present invention include, among other things, fluid loss control additives, salts, vitrified shale, fly ash, fumed silica, bentonite, viscosifiers, suspending agents, dispersants, and the like. An example of a suitable fly ash is "POZMTX^® A," commercially available from Halliburton Energy Services, Inc., of Duncan, Oklahoma. An example of a suitable source of fumed silica is "SILICALITE™," commercially available from Halliburton Energy Services, Inc., of Duncan, Oklahoma. An example of a suitable viscosifϊer is "VERSASET™," commercially available from Halliburton Energy Services, Inc., of Duncan, Oklahoma. One skilled in the art, with the benefit of this disclosure, will be able to determine which additional additives are appropriate for a particular application of the methods of the present invention, as well as the amounts of those additives that should be used.

2. Methods of Forming and Using Kickoff Plugs

In one embodiment, the present invention provides a method of placing a plug in a well bore in a subterranean formation. The well bore in which the self-degrading cement composition is placed may be an open hole, a cased hole, or any combination thereof.

In another embodiment, the present invention provides a method of placing a degradable kickoff plug in a well bore in a subterranean formation. The well bore in which the degradable kickoff plug placed may be an open hole, a cased hole, or any combination thereof.

Referring now to Figure 3, a cross-section of a subterranean formation is illustrated therein. In the formation illustrated in Figure 3, a reservoir 1 (comprising hydrocarbons, e.g., oil and/or gas) is depicted, bounded above and below by shale zones. Reservoir 1 has an upper portion 30 and a lower portion 35.

Referring now to Figure 4, a well bore 100 has been drilled within the formation. As shown in Figure 4, production of hydrocarbons has been commenced, which gradually will cause upper portion 30 of reservoir 1 to be depleted over time; hydrocarbons will remain in lower portion 35 of reservoir 1.

Referring now to Figure 5, a self-degrading cement composition 2 is placed in well bore 100, via any suitable manner. In some embodiments, the self-degrading cement composition 2 may be pumped through the drillstring. In some embodiments, the self- degrading cement composition 2 may be pumped through an open-ended coiled tubing 160 to the desired location in well bore 100. One skilled in the art, with the benefit of this disclosure, will recognize the appropriate techniques and equipment for placing the self- degrading cement composition 2 in well bore 100 in a particular application. In some embodiments, the self-degrading cement composition 2 may be placed in well bore 100 just below the point at which a directional hole or well bore will be initiated.

After the placement of the self-degrading cement composition 2 within the subterranean formation, the water source within the self-degrading cement composition 2 may combine with the dry materials in the self-degrading cement composition 2 to form what may be referred to as a "hydrate," e.g., a solid compound comprising water molecules that may combine in a definite ratio. Furthermore, the water molecules within the hydrate may provide a hydrolysis source for the degradable material.

The amount of time required for the self-degrading cement composition 2 to set to form a hardened kickoff plug 150 may depend upon a variety of factors, including, but not limited to, the temperature in well bore 100, the desired size and/or strength of the kickoff plug 150, the formulation of the self-degrading cement composition 2, and/or the presence of a set retarder. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the amount of time required for the self-degrading cement composition 2 to set. In some embodiments of the present invention, permitting the self-degrading cement composition 2 to set to form a hardened kickoff plug 150 may require waiting an amount of time in the range of from about 15 minutes to about 72 hours.

Referring now to Figure 6, the self-degrading cement composition placed within well bore 100 has set to form kickoff plug 150.

In some embodiments, the methods of the present invention further may comprise contacting the hardened kickoff plug 150 with a drill string such that the path of the drill string deviates away from well bore 100 to a desired degree and allows the drill string to continue drilling a directional hole at a desired deviation from well bore 100. Referring now to Figure 7, a directional hole 250 is shown, which permits fluid flow from lower reservoir 35 to well bore 100, and subsequently to the surface. In certain embodiments, the directional hole 250 may deviate away from well bore 100 by an amount in the range of from about 1 degree to about 20 degrees. The desired degree of deviation will depend upon a variety of factors, including, but not limited to, the location of recoverable fluids in the subterranean formation or an adjacent formation, the stability of the subterranean formation (e.g., the mechanical properties of the formation), the location of an obstruction around which the directional hole is constructed, and the like. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the desired degree of deviation from well bore 100 for directional hole 250, and will be able to adapt the methods of the present invention to drill directional hole 250 at that desired deviation.

Referring now to Figure 8, hydrocarbon production has commenced from the lower reservoir 35. In some embodiments of the present invention, including those illustrated in Figure 8, the hardened kickoff plug 150 may be allowed to degrade such that fluid communication through the portion of well bore 100 wherein kickoff plug 150 resides is at least partially restored; in preferred embodiments, kickoff plug 150 may degrade to such extent that fluid communication is completely restored. In some embodiments of the present invention, it may be desirable to allow the degradable material to degrade slowly over time, rather than instantaneously. In certain embodiments, allowing kickoff plug 150 to degrade such that fluid communication through the portion of well bore 100 wherein kickoff plug 150 resides is at least partially restored may require waiting an amount of time in the range of from about 4 hours to about 21 days. In certain embodiments, allowing kickoff plug 150 to degrade such that fluid communication through the portion of well bore 100 wherein kickoff plug 150 resides is at least partially restored may require waiting an amount of time in the range of from about 4 hours to about 36 hours. As illustrated in Figure 8, enhanced hydrocarbon production is depicted, facilitated by the degradation of kickoff plug 150 and the drilling of directional hole 250.

Certain embodiments of the methods of the present invention may be used in well bores comprising casing. Referring now to Figure 9, a cross-section of a subterranean formation is illustrated therein. In the formation illustrated in Figure 9, a reservoir 1 (comprising hydrocarbons, e.g., oil and/or gas) is depicted, bounded above and below by shale zones. Reservoir 1 has an upper portion 30 and a lower portion 35. Well bore 100 has been drilled within the formation. Casing 120 is disposed within well bore 100. A conventional cement composition 109 has been placed in an annulus between the outer surface of casing 120 and the inner walls of well bore 100.

Referring now to Figure 10, a self-degrading cement composition 2 is placed in well bore 100, via any suitable manner (e.g., by pumping through a drillstring, or, as shown in Figure 10, by pumping through open-ended coiled tubing 160, or the like), as previously has been described herein.

Referring now to Figure 11, the self-degrading cement composition 2 has set to form kickoff plug 150.

Referring now to Figure 12, illustrated therein is a directional hole 250 that permits fluid flow from lower reservoir 35 to well bore 100, and subsequently to the surface. Directional hole 250 may be provided, for example, by contacting the hardened kickoff plug 150 with a drill string (not shown in Figure 12) such that the path of the drill string deviates away from well bore 100 to a desired degree, thereby permitting the drill string to continue drilling directional hole 250 at a desired deviation from well bore 100. The degree to which directional hole 250 may deviate away from well bore 100 previously has been described herein. In certain embodiments, once directional hole 250 has been drilled to a desired extent, a casing string 320 (not shown in Figure 12) may be placed within directional hole 250, and perforations 330 (not shown in Figure 12) may be created within casing string 320 (e.g., by use of a perforating tool, and the like). Subsequently, hydrocarbons (e.g., in the lower reservoir 35) may flow through perforations 330 (not shown in Figure 12), into directional hole 250, and flow therefrom to the surface.

Referring now to Figure 13, enhanced hydrocarbon production is depicted, facilitated by the drilling of directional hole 250 and the degradation of kickoff plug 150. In some embodiments of the present invention, including those illustrated in Figure 13, the hardened kickoff plug 150 may be allowed to degrade such that fluid communication through the portion of well bore 100 wherein kickoff plug 150 resides is at least partially restored; in preferred embodiments, kickoff plug 150 may degrade to such extent that fluid communication is completely restored. As illustrated in Figure 13, the degradation of kickoff plug 150 facilitates entry of hydrocarbons into well bore 100 through perforations 290. In some embodiments of the present invention, it may be desirable to allow the degradable material to degrade slowly over time, rather than instantaneously.

To facilitate a better understanding of the present invention, the following examples of certain aspects of some embodiments are given. In no way should the following examples be read to limit, or to define, the scope of the invention. EXAMPLE 1

Sample compositions were formed as follows. First, 7.58 grams of magnesium oxide were dry blended with 25.75 grams of potassium phosphate monobasic crystals (KH₂PO₄), and mixed with 16.67 grams of tap water. The mixture was stirred for some time, and poly(lactic acid) ("6250D") was added, generally in an amount in the range of from about 35% by weight to about 40% by weight. Certain of the sample compositions further comprised an acid-base cement referred to as Newberyite, and having the chemical formula MgH(PO₄)¹SH₂O. Among other things, Newberyite is thought to impart strength-enhancing properties to the sample composition, and the additional water that Newberyite may supply may facilitate hydrolysis of the degradable material (6250D₃ in this example). Table 2 sets forth the respective amounts of 6250D and Newberyite included in a particular sample composition.

TABLE 2

Each sample composition was placed in a 2OmL plastic cylinder, and was allowed to set therein into a hard rod. Each rod then was left for a designated cure time at room temperature. Next, the set rod was taken out of the cylinder and either tested for compressibility or directly placed in a bomb supplied by PARR Instrument Company, Moline, Illinois. Among other things, the bomb prevented the escape of water that may have been present in the set rod. The bomb was heated in a stove at 25O⁰F. After a time (listed as "PARR Time" in Table 3 below), the bomb was removed from the stove, and its contents were observed to see whether or not degradation occurred.

Certain sample compositions were tested for compressibility using an apparatus supplied by Tinius Olsen Company of Willow Grove, Pennsylvania. The procedure was performed as follows. After the sample composition had cured and set into a hard rod, the rod was cut down to a 1 inch diameter and a 3 inch length. Two faces of the rod were smoothed. The rod then was placed under the Tinius Olsen compressibility load cell and subjected to a displacement load at a rate of 0.07 inches per minute. The maximum loading that each rod could withstand until failure was recorded.

The results of the testing are set forth in Table 3 below.

TABLE 3

Example 1 demonstrates, inter alia, that the combination of a degradable material and an acid-base cement may be suitable for use in the methods of the present invention.

Therefore, the present invention is well adapted to attain the ends and advantages mentioned as well as those that are inherent therein. While numerous changes may be made by those skilled in the art, such changes are encompassed within the spirit of this invention as defined by the appended claims. The terms in the claims have their plain, ordinary meaning unless otherwise explicitly and clearly defined by the patentee.

Claims

Claims:

1. A method comprising: providing a self-degrading cement composition that comprises a degradable material, an acid source, a base source, and a water source; placing the self-degrading cement composition in a desired location in a well bore that penetrates a subterranean formation; and allowing the self-degrading cement composition to set to form a hardened kickoffplug.

2. The method of claim 1 wherein the degradable material comprises at least one of the following group: an aliphatic polyester; a polysaccharide; a poly(lactide); a poly(glycolide); a poly(y-caprolactone); a protein; a poly(hydroxybutyrate); a poly(anhydride); an aliphatic polycarbonate; an ortho ester; a poly(orthoester); a poly(vinylacetate); a poly(hydroxy ester ether); a poly(amino acid); a poly(ethylene oxide); chitin; chitosan; a polyphosphazene; a poly ether ester; a polyester amide; a polyamide; and a derivative thereof.

3. The method of claim 1 wherein the degradable material comprises poly(lactic) acid.

4. The method of claim 1 wherein the degradable material comprises a self- degrading fiber that comprises an outer shell and a core liquid, wherein the outer shell comprises a degradable polymer and substantially retains the core liquid.

5. The method of claim 4 wherein the self-degrading fiber comprises a coating on the outer shell.

6. The method of claim 4 wherein the self-degrading fiber comprises an additional additive within the core liquid.

7. The method of claim 1 wherein the self-degrading cement composition further comprises a buffer compound.

8. The method of claim 1 wherein the acid source comprises at least one of the following group: magnesium chloride; potassium phosphate monobasic; phosphoric acid; magnesium sulfate; ammonium phosphate monobasic; and a derivative thereof.

9. The method of claim 1 wherein the base source comprises at least one of the following group: magnesium oxide; ammonia; and a derivative thereof.

10. The method of claim 1 wherein the self-degrading cement composition further comprises a strength-enhancing additive.

11. The method of claim 1 wherein the self-degrading cement composition further comprises a set retarder.

12. The method of claim 1 further comprising contacting the hardened kickoff plug with a drill string so as to cause the path of the drill string to deviate away from the well bore.

13. The method of claim 12 further comprising allowing the drill string to continue drilling a directional hole that deviates from the well bore.

14. The method of claim 1 further comprising allowing the hardened kickoff plug to degrade such that fluid communication through the portion of well bore where the kickoff plug was disposed is at least partially restored.

15. The method of claim 13 further comprising allowing the hardened kickoff plug to degrade such that fluid communication through the portion of well bore where the kickoff plug was disposed is at least partially restored.

16. A method of placing a degradable kickoff plug at a desired location in a well bore penetrating a subterranean formation, the method comprising: providing a self-degrading cement composition that comprises a degradable material, an acid source, a base source, and a water source; placing the self-degrading cement composition in the desired location in the well bore; and allowing the self-degrading cement composition to set to form the degradable kickoff plug.

17. The method of claim 16 wherein the desired location in the well bore is located just below the point in the well bore at which a directional hole through the side of the well bore is to be drilled.

18. A method of drilling a directional hole through the side of a well bore penetrating a subterranean formation, the method comprising: providing a self-degrading cement composition that comprises a degradable material, an acid source, a base source, and a water source; placing the self-degrading cement composition in a desired location in the well bore; allowing the self-degrading cement composition to set to form a hardened kickoffplug; contacting the hardened kickoffplug with a drill string such that the path of the drill string deviates away from the well bore; and allowing the drill string to continue drilling a directional hole that deviates from the well bore.

19. The method of claim 18 wherein allowing the drill string to continue drilling a directional hole comprises drilling through at least a portion of a casing string in the well bore.

20. The method of claim 18 further comprising allowing the hardened kickoff plug to degrade such that fluid communication through the portion of well bore where the kickoffplug resides is at least partially restored.

21. A degradable kickoff plug, comprising: a degradable material; and an acid-base cement.

22. The degradable kickoff plug of claim 21 , wherein the degradable material comprises at least one of the following group: an aliphatic polyester; a polysaccharide; a poly(lactide); a poly(glycolide); a poly(y-caprolactone); a protein; a poly(hydroxybutyrate); a poly(anhydride); an aliphatic polycarbonate; an ortho ester; a poly(orthoester); a poly(vinylacetate); a poly(hydroxy ester ether); a poly(amino acid); a poly(ethylene oxide); chitin; chitosan; a polyphosphazene; a poly ether ester; a polyester amide; a polyamide; and a derivative thereof.

23. The degradable kickoff plug of claim 21 , wherein the degradable material comprises poly(lactic) acid.

24. The degradable kickoffplug of claim 21, wherein the acid-base cement comprises a compound corresponding to the chemical formula MgKPO₄-OH₂O or a derivative thereof.

25. The degradable kickoff plug of claim 21 , wherein the acid-base cement comprises a compound corresponding to the chemical formula 5 Mg(OH)₂MgCl₂-8H₂O or a derivative thereof.

26. The degradable kickoff plug of claim 21 , wherein the acid-base cement comprises a compound corresponding to the chemical formula MgHPO₄-SH₂O or a derivative thereof.

27. The degradable kickoff plug of claim 21 , wherein the acid-base cement comprises a compound corresponding to the chemical formula 3Mg(OH)₂MgSO₄- 8H₂O or a derivative thereof.

28. The degradable kickoff plug of claim 21 , wherein the acid-base cement comprises a compound corresponding to the chemical formula Mg(NH₄)PO₄-OH₂O or a derivative thereof.

29. The degradable kickoff plug of claim 21 , wherein the degradable material comprises poly(lactic acid) and wherein the acid-base cement comprises at least one of the following: a compound corresponding to the chemical formula MgKPO₄-OH₂O or a derivative thereof; a compound corresponding to the chemical formula 5Mg(OH)₂MgCl₂- 8H₂O or a derivative thereof; a compound corresponding to the chemical formula MgHPO₄-3H₂O or a derivative thereof; a compound corresponding to the chemical formula 3Mg(OH)₂MgSO₄- 8H₂O or a derivative thereof; and a compound corresponding to the chemical formula Mg(NH₄)PO₄-OH₂O or a derivative thereof.

30. A degradable kickoff plug formed by a method comprising: providing a self-degrading cement composition that comprises a degradable material, an acid source, a base source, and a water source; placing the self-degrading cement composition in a desired location in a well bore that penetrates a subterranean formation; and allowing the self-degrading cement composition to set to form a hardened kickoff plug.

31. The degradable kickoff plug of claim 30 wherein the degradable material comprises at least one of the following group: an aliphatic polyester; a polysaccharide; a poly(lactide); a poly(glycolide); a poly(y-caprolactone); a protein; a poly(hydroxybutyrate); a poly(anhydride); an aliphatic polycarbonate; an ortho ester; a poly(orthoester); a poly(vinylacetate); a poly(hydroxy ester ether); a poly(amino acid); a poly(ethylene oxide); chitin; chitosan; a polyphosphazene; a poly ether ester; a polyester amide; a polyamide; and a derivative thereof.

32. The degradable kickoff plug of claim 30 wherein the degradable material comprises poly(lactic) acid.

33. The degradable kickoff plug of claim 30 wherein the degradable material comprises a self-degrading fiber that comprises an outer shell and a core liquid, wherein the outer shell comprises a degradable polymer and substantially retains the core liquid.

34. The degradable kickoff plug of claim 30 wherein the self-degrading cement composition further comprises a buffer compound.

35. The degradable kickoff plug of claim 3030 wherein the acid source comprises at least one of the following group: magnesium chloride; potassium phosphate monobasic; phosphoric acid; magnesium sulfate; ammonium phosphate monobasic; and a derivative thereof.

36. The degradable kickoff plug of claim 30 wherein the base source comprises at least one of the following: magnesium oxide; ammonia; or a derivative thereof.

37. The degradable kickoff plug of claim 30 wherein the self-degrading cement composition further comprises a strength-enhancing additive.

38. The degradable kickoff plug of claim 30 wherein the self-degrading cement composition further comprises a set retarder.

39. The degradable kickoff plug of claim 30 wherein the base source comprises magnesium oxide, and the acid source comprises at least one of the following group: magnesium chloride; potassium phosphate monobasic; phosphoric acid; magnesium sulfate; ammonium phosphate monobasic; and a derivative thereof.

40. The degradable kickoff plug of claim 30 wherein the degradable material comprises poly(lactic acid), wherein the base source comprises magnesium oxide, and wherein the acid source comprises at least one of the following group: magnesium chloride; potassium phosphate monobasic; phosphoric acid; magnesium sulfate; ammonium phosphate monobasic; and a derivative thereof.