WO2006138224A1 - Beton a armature textile - Google Patents

Beton a armature textile Download PDF

Info

Publication number
WO2006138224A1
WO2006138224A1 PCT/US2006/022836 US2006022836W WO2006138224A1 WO 2006138224 A1 WO2006138224 A1 WO 2006138224A1 US 2006022836 W US2006022836 W US 2006022836W WO 2006138224 A1 WO2006138224 A1 WO 2006138224A1
Authority
WO
WIPO (PCT)
Prior art keywords
reinforcing
concrete
fabric
steel
rebar
Prior art date
Application number
PCT/US2006/022836
Other languages
English (en)
Inventor
Lancelot Coar
Original Assignee
Lancelot Coar
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lancelot Coar filed Critical Lancelot Coar
Publication of WO2006138224A1 publication Critical patent/WO2006138224A1/fr

Abstract

L'invention concerne une structure de béton armé qui fait appel à un textile structurel tissé comme principal composant de renforcement à la traction. Le textile d'armature est noyé dans la structure du béton afin de suivre les motifs de contrainte anticipés généraux ou spécifiques et offrir un support de traction efficace. Fabriqué dans un matériau léger, le textile d'armature faciliter l'installation, offre une efficacité de renforcement améliorée et une performance améliorée dans les conditions environnementales par rapport aux constructions à renfort en acier habituelles.
PCT/US2006/022836 2005-06-14 2006-06-13 Beton a armature textile WO2006138224A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US69055705P 2005-06-14 2005-06-14
US60/690,557 2005-06-14

Publications (1)

Publication Number Publication Date
WO2006138224A1 true WO2006138224A1 (fr) 2006-12-28

Family

ID=37570764

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2006/022836 WO2006138224A1 (fr) 2005-06-14 2006-06-13 Beton a armature textile

Country Status (1)

Country Link
WO (1) WO2006138224A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2008085526A1 (fr) * 2007-01-12 2008-07-17 Arizona Board Of Regents On Behalf Of The University Of Arizona Masse de matériau renforcée et procédé de formage
CN101979789B (zh) * 2009-07-15 2015-09-30 默罕默德·奥马尔·贾扎尔 钢筋混凝土建筑结构及其方法
EP3705657A1 (fr) * 2019-03-05 2020-09-09 CarboCon GmbH Structure de renfort textile pour un composant, procédé de fabrication pour une structure de renfort, composant et pièce semi-finie
EP2894272B1 (fr) * 2014-01-13 2023-04-19 GOLDBECK GmbH Béton armé haute performance

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4298413A (en) * 1980-03-03 1981-11-03 Teare John W Method and apparatus for producing concrete panels
US4446083A (en) * 1981-08-03 1984-05-01 Nicholls Robert L Air-inflated fabric-reinforced concrete shells
US20040219845A1 (en) * 2003-04-29 2004-11-04 Graham Samuel E. Fabric reinforced cement

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4298413A (en) * 1980-03-03 1981-11-03 Teare John W Method and apparatus for producing concrete panels
US4446083A (en) * 1981-08-03 1984-05-01 Nicholls Robert L Air-inflated fabric-reinforced concrete shells
US20040219845A1 (en) * 2003-04-29 2004-11-04 Graham Samuel E. Fabric reinforced cement

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2008085526A1 (fr) * 2007-01-12 2008-07-17 Arizona Board Of Regents On Behalf Of The University Of Arizona Masse de matériau renforcée et procédé de formage
CN101979789B (zh) * 2009-07-15 2015-09-30 默罕默德·奥马尔·贾扎尔 钢筋混凝土建筑结构及其方法
EP2894272B1 (fr) * 2014-01-13 2023-04-19 GOLDBECK GmbH Béton armé haute performance
EP3705657A1 (fr) * 2019-03-05 2020-09-09 CarboCon GmbH Structure de renfort textile pour un composant, procédé de fabrication pour une structure de renfort, composant et pièce semi-finie

Similar Documents

Publication Publication Date Title
US6263629B1 (en) Structural reinforcement member and method of utilizing the same to reinforce a product
AU2007206065B2 (en) Hybrid composite beam system
US7895799B2 (en) Hybrid composite beam and beam system
US20200224448A1 (en) Building structure and method
US8826626B2 (en) Light-weight load-bearing structures
WO2006020261A2 (fr) Armature de frettage pour structures en maçonnerie ou en beton
JP2019126991A (ja) 超高強度繊維補強コンクリート複合プレキャストｐｃ床版
EA018421B1 (ru) Легкие несущие конструкции, армированные элементами сердечника, выполненными из сегментов, и способ бетонирования таких конструкций
WO2006138224A1 (fr) Beton a armature textile
CN111677187A (zh) 一种复材纵筋-缠绕网格箍筋增强混凝土梁及其制备方法
Paramasivam et al. Ferrocement structures and structural elements
Sweidan The application of fiber reinforced plastics to the strengthening of masonry structures
Daniel et al. The Specifics of Use of Composite Materials in Consolidation of Historical Monuments
US20230332405A1 (en) Reinforcement mesh and method for producing thereof
Wu et al. State of the Art Review of Reinforcement Strategies and Technologies for 3D Printing of Concrete. Energies 2022, 15, 360
KR101103299B1 (ko) 하이브리드 보강재
Gowri et al. A review on structural properties of concrete with ferro cement
Arduini et al. Strengthening of casilina bridge with carbon fibre reinforced polymer sheets
AU2022354113A1 (en) Post-tensioned expanding concrete with fibers for slabs
Iskhakov et al. Using steel fibred high strength concrete for repairing normal strength concrete beams and slabs
D'Ayala et al. Advance composites applications on historical structures in Italy: Case studies and future developments
Doddamaini et al. Generation of Strength Statistics for Concrete Beam with Alternative of Permanent Ferrocement form
Sheikh et al. ``Fibre reinforced polymers FRP) as an economical alternative for construction and rehabilitation''
Scott Non-Ferrous Reinforcement
Papadrakakis et al. Composite Materials Technologies in Constructions Structural Retrofitting: New Developments and Applications in Historical Buildings and Applications in Seismic Zone

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application
NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 06772940

Country of ref document: EP

Kind code of ref document: A1