WO2006079715A1 - Methode de coloration d'une lentille optique comprenant un primaire d'impression, et lentille optique teintee comprenant un tel primaire d'impression - Google Patents
Methode de coloration d'une lentille optique comprenant un primaire d'impression, et lentille optique teintee comprenant un tel primaire d'impression Download PDFInfo
- Publication number
- WO2006079715A1 WO2006079715A1 PCT/FR2006/000167 FR2006000167W WO2006079715A1 WO 2006079715 A1 WO2006079715 A1 WO 2006079715A1 FR 2006000167 W FR2006000167 W FR 2006000167W WO 2006079715 A1 WO2006079715 A1 WO 2006079715A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- staining method
- primer
- colloid
- optical lens
- anionic
- Prior art date
Abstract
Description
Claims