WO2006063233A2 - Photoconductive device - Google Patents
Photoconductive device Download PDFInfo
- Publication number
- WO2006063233A2 WO2006063233A2 PCT/US2005/044620 US2005044620W WO2006063233A2 WO 2006063233 A2 WO2006063233 A2 WO 2006063233A2 US 2005044620 W US2005044620 W US 2005044620W WO 2006063233 A2 WO2006063233 A2 WO 2006063233A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- semiconductor structure
- range
- grown
- gap
- gaas
- Prior art date
Abstract
Description
Claims