WO2006043019A1 - Fibre reinforced assembly - Google Patents
Fibre reinforced assembly Download PDFInfo
- Publication number
- WO2006043019A1 WO2006043019A1 PCT/GB2005/003450 GB2005003450W WO2006043019A1 WO 2006043019 A1 WO2006043019 A1 WO 2006043019A1 GB 2005003450 W GB2005003450 W GB 2005003450W WO 2006043019 A1 WO2006043019 A1 WO 2006043019A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- epoxy resin
- assembly
- epoxy
- terminated
- amine
- Prior art date
Abstract
Description
Claims