WO2005077996A1 - Tackifier dispersion - Google Patents
Tackifier dispersion Download PDFInfo
- Publication number
- WO2005077996A1 WO2005077996A1 PCT/SE2005/000057 SE2005000057W WO2005077996A1 WO 2005077996 A1 WO2005077996 A1 WO 2005077996A1 SE 2005000057 W SE2005000057 W SE 2005000057W WO 2005077996 A1 WO2005077996 A1 WO 2005077996A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- emulsifier
- ester
- tackifier
- weight
- fatty acids
- Prior art date
Abstract
Description
Claims