WO2005068393A1 - Fusion-cast refractory with high electrical resistivity - Google Patents
Fusion-cast refractory with high electrical resistivity Download PDFInfo
- Publication number
- WO2005068393A1 WO2005068393A1 PCT/US2004/044042 US2004044042W WO2005068393A1 WO 2005068393 A1 WO2005068393 A1 WO 2005068393A1 US 2004044042 W US2004044042 W US 2004044042W WO 2005068393 A1 WO2005068393 A1 WO 2005068393A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- refractory
- cao
- fusion
- electrical resistivity
- content
- Prior art date
Abstract
Description
Claims