WO2005063895A2 - Thermally-reversible crosslinking of polymers - Google Patents
Thermally-reversible crosslinking of polymers Download PDFInfo
- Publication number
- WO2005063895A2 WO2005063895A2 PCT/US2004/043342 US2004043342W WO2005063895A2 WO 2005063895 A2 WO2005063895 A2 WO 2005063895A2 US 2004043342 W US2004043342 W US 2004043342W WO 2005063895 A2 WO2005063895 A2 WO 2005063895A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymer
- free
- radical
- thermally
- ethylene
- Prior art date
Abstract
Description
Claims