WO2005061846A1 - Compositions de ciment aux proprietes mecaniques ameliorees et procede de cimentation dans une formation sous-terraine - Google Patents
Compositions de ciment aux proprietes mecaniques ameliorees et procede de cimentation dans une formation sous-terraine Download PDFInfo
- Publication number
- WO2005061846A1 WO2005061846A1 PCT/GB2004/004925 GB2004004925W WO2005061846A1 WO 2005061846 A1 WO2005061846 A1 WO 2005061846A1 GB 2004004925 W GB2004004925 W GB 2004004925W WO 2005061846 A1 WO2005061846 A1 WO 2005061846A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- elastic particles
- cement composition
- cement
- fluid
- present
- Prior art date
Abstract
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US10/745,470 US20040171499A1 (en) | 2003-01-24 | 2003-12-22 | Cement compositions with improved mechanical properties and methods of cementing in a subterranean formation |
US10/745,470 | 2003-12-22 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2005061846A1 true WO2005061846A1 (fr) | 2005-07-07 |
Family
ID=34710603
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/GB2004/004925 WO2005061846A1 (fr) | 2003-12-22 | 2004-11-23 | Compositions de ciment aux proprietes mecaniques ameliorees et procede de cimentation dans une formation sous-terraine |
Country Status (2)
Country | Link |
---|---|
US (1) | US20040171499A1 (fr) |
WO (1) | WO2005061846A1 (fr) |
Cited By (28)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2006095124A1 (fr) * | 2005-03-11 | 2006-09-14 | Halliburton, Energy Services, Inc. | Compositions pour une cimentation legere a temperature elevee |
WO2008092078A1 (fr) * | 2007-01-26 | 2008-07-31 | Bj Services Company | Procédé d'acidification et fracturation mettant en oeuvre des fluides réactifs et des matières particulaires déformables |
WO2010125327A1 (fr) * | 2009-04-30 | 2010-11-04 | Halliburton Energy Services, Inc. | Procédé de sélection d'un ciment de trou de forage ayant des caractéristiques souhaitables |
US8603952B2 (en) | 2007-05-10 | 2013-12-10 | Halliburton Energy Services, Inc. | Cement compositions and methods utilizing nano-clay |
US8672029B2 (en) | 2009-12-30 | 2014-03-18 | Schlumberger Technology Corporation | System for reducing foam in mixing operations |
US8691737B2 (en) | 2005-09-09 | 2014-04-08 | Halliburton Energy Services, Inc. | Consolidating spacer fluids and methods of use |
US8741818B2 (en) | 2007-05-10 | 2014-06-03 | Halliburton Energy Services, Inc. | Lost circulation compositions and associated methods |
US8895486B2 (en) | 2005-09-09 | 2014-11-25 | Halliburton Energy Services, Inc. | Methods and compositions comprising cement kiln dust having an altered particle size |
US8921284B2 (en) | 2005-09-09 | 2014-12-30 | Halliburton Energy Services, Inc. | Spacer fluids containing cement kiln dust and methods of use |
US8940670B2 (en) | 2007-05-10 | 2015-01-27 | Halliburton Energy Services, Inc. | Cement compositions comprising sub-micron alumina and associated methods |
US8950486B2 (en) | 2005-09-09 | 2015-02-10 | Halliburton Energy Services, Inc. | Acid-soluble cement compositions comprising cement kiln dust and methods of use |
US9006154B2 (en) | 2005-09-09 | 2015-04-14 | Halliburton Energy Services, Inc. | Methods for determining reactive index for cement kiln dust, associated compositions and methods of use |
US9006155B2 (en) | 2005-09-09 | 2015-04-14 | Halliburton Energy Services, Inc. | Placing a fluid comprising kiln dust in a wellbore through a bottom hole assembly |
US9023150B2 (en) | 2005-09-09 | 2015-05-05 | Halliburton Energy Services, Inc. | Acid-soluble cement compositions comprising cement kiln dust and/or a natural pozzolan and methods of use |
US9051505B2 (en) | 2005-09-09 | 2015-06-09 | Halliburton Energy Services, Inc. | Placing a fluid comprising kiln dust in a wellbore through a bottom hole assembly |
US9150773B2 (en) | 2005-09-09 | 2015-10-06 | Halliburton Energy Services, Inc. | Compositions comprising kiln dust and wollastonite and methods of use in subterranean formations |
US9199879B2 (en) | 2007-05-10 | 2015-12-01 | Halliburton Energy Serives, Inc. | Well treatment compositions and methods utilizing nano-particles |
US9206344B2 (en) | 2007-05-10 | 2015-12-08 | Halliburton Energy Services, Inc. | Sealant compositions and methods utilizing nano-particles |
US9376609B2 (en) | 2010-12-21 | 2016-06-28 | Halliburton Energy Services, Inc. | Settable compositions comprising interground perlite and hydraulic cement |
US9409821B2 (en) | 2010-12-08 | 2016-08-09 | Schlumberger Technology Corporation | Compositions and methods for well completions |
US9512352B2 (en) | 2007-05-10 | 2016-12-06 | Halliburton Energy Services, Inc. | Well treatment fluids and methods utilizing nano-particles |
US9512346B2 (en) | 2004-02-10 | 2016-12-06 | Halliburton Energy Services, Inc. | Cement compositions and methods utilizing nano-hydraulic cement |
US9676989B2 (en) | 2005-09-09 | 2017-06-13 | Halliburton Energy Services, Inc. | Sealant compositions comprising cement kiln dust and tire-rubber particles and method of use |
EP3228609A1 (fr) * | 2016-04-08 | 2017-10-11 | Services Pétroliers Schlumberger | Agent d'expansion encapsulé dans un polysiloxan calciné pour la cimentation de puits |
WO2017174208A1 (fr) * | 2016-04-08 | 2017-10-12 | Schlumberger Technology Corporation | Boue comprenant un agent d'expansion encapsulé pour la cimentation de puits |
US9809737B2 (en) | 2005-09-09 | 2017-11-07 | Halliburton Energy Services, Inc. | Compositions containing kiln dust and/or biowaste ash and methods of use |
US10526523B2 (en) | 2016-02-11 | 2020-01-07 | Schlumberger Technology Corporation | Release of expansion agents for well cementing |
US11130899B2 (en) | 2014-06-18 | 2021-09-28 | Schlumberger Technology Corporation | Compositions and methods for well cementing |
Families Citing this family (65)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US7482309B2 (en) * | 2003-11-24 | 2009-01-27 | Halliburton Energy Services, Inc. | Methods of drilling wellbores using variable density fluids comprising coated elastic particles |
US7749942B2 (en) * | 2003-01-24 | 2010-07-06 | Halliburton Energy Services, Inc | Variable density fluids and methods of use in subterranean formations |
US7866394B2 (en) | 2003-02-27 | 2011-01-11 | Halliburton Energy Services Inc. | Compositions and methods of cementing in subterranean formations using a swelling agent to inhibit the influx of water into a cement slurry |
US7055603B2 (en) * | 2003-09-24 | 2006-06-06 | Halliburton Energy Services, Inc. | Cement compositions comprising strength-enhancing lost circulation materials and methods of cementing in subterranean formations |
US7376148B1 (en) * | 2004-01-26 | 2008-05-20 | Cisco Technology, Inc. | Method and apparatus for improving voice quality in a packet based network |
US7607482B2 (en) | 2005-09-09 | 2009-10-27 | Halliburton Energy Services, Inc. | Settable compositions comprising cement kiln dust and swellable particles |
US7607483B2 (en) * | 2004-04-19 | 2009-10-27 | Halliburton Energy Services, Inc. | Sealant compositions comprising colloidally stabilized latex and methods of using the same |
US20050241538A1 (en) * | 2004-04-28 | 2005-11-03 | Vargo Richard F Jr | Methods of making cement compositions using liquid additives containing lightweight beads |
US8088716B2 (en) | 2004-06-17 | 2012-01-03 | Exxonmobil Upstream Research Company | Compressible objects having a predetermined internal pressure combined with a drilling fluid to form a variable density drilling mud |
WO2007145735A2 (fr) | 2006-06-07 | 2007-12-21 | Exxonmobil Upstream Research Company | Procédé de fabrication d'objets compressibles pour boue de forage à densité variable |
US20050284641A1 (en) * | 2004-06-24 | 2005-12-29 | Baker Hughes Incorporated | Controlled variable density fluid for wellbore operations |
US7259130B2 (en) * | 2004-08-03 | 2007-08-21 | Halliburton Energy Services, Inc. | Set-on demand, ester-based wellbore fluids and methods of using the same |
US9512345B2 (en) | 2004-10-20 | 2016-12-06 | Halliburton Energy Services, Inc. | Settable spacer fluids comprising pumicite and methods of using such fluids in subterranean formations |
US7293609B2 (en) * | 2004-10-20 | 2007-11-13 | Halliburton Energy Services, Inc. | Treatment fluids comprising vitrified shale and methods of using such fluids in subterranean formations |
US20100044057A1 (en) * | 2004-10-20 | 2010-02-25 | Dealy Sears T | Treatment Fluids Comprising Pumicite and Methods of Using Such Fluids in Subterranean Formations |
US7690429B2 (en) * | 2004-10-21 | 2010-04-06 | Halliburton Energy Services, Inc. | Methods of using a swelling agent in a wellbore |
US7284611B2 (en) * | 2004-11-05 | 2007-10-23 | Halliburton Energy Services, Inc. | Methods and compositions for controlling lost circulation in subterranean operations |
US7219732B2 (en) * | 2004-12-02 | 2007-05-22 | Halliburton Energy Services, Inc. | Methods of sequentially injecting different sealant compositions into a wellbore to improve zonal isolation |
US7488705B2 (en) | 2004-12-08 | 2009-02-10 | Halliburton Energy Services, Inc. | Oilwell sealant compositions comprising alkali swellable latex |
US20070111900A1 (en) * | 2005-11-11 | 2007-05-17 | Reddy B R | Sealant compositions comprising solid latex |
US20070111901A1 (en) | 2005-11-11 | 2007-05-17 | Reddy B R | Method of servicing a wellbore with a sealant composition comprising solid latex |
US7373981B2 (en) * | 2005-02-14 | 2008-05-20 | Halliburton Energy Services, Inc. | Methods of cementing with lightweight cement compositions |
US7398827B2 (en) * | 2005-03-11 | 2008-07-15 | Halliburton Energy Services, Inc. | Methods for high temperature lightweight cementing |
US7264053B2 (en) * | 2005-03-24 | 2007-09-04 | Halliburton Energy Services, Inc. | Methods of using wellbore servicing fluids comprising resilient material |
US20060217270A1 (en) * | 2005-03-24 | 2006-09-28 | Halliburton Energy Services, Inc. | Wellbore servicing fluids comprising resilient material |
US7891424B2 (en) | 2005-03-25 | 2011-02-22 | Halliburton Energy Services Inc. | Methods of delivering material downhole |
US7473313B2 (en) * | 2005-06-15 | 2009-01-06 | Halliburton Energy Services, Inc. | Gas-generating additives having improved shelf lives for use in cement compositions |
US7334638B2 (en) * | 2005-06-15 | 2008-02-26 | Halliburton Energy Services, Inc. | Methods of improving the shelf life of a cement composition comprising a coated gas-generating material |
US7870903B2 (en) | 2005-07-13 | 2011-01-18 | Halliburton Energy Services Inc. | Inverse emulsion polymers as lost circulation material |
US7341106B2 (en) * | 2005-07-21 | 2008-03-11 | Halliburton Energy Services, Inc. | Methods for wellbore strengthening and controlling fluid circulation loss |
US7617870B1 (en) | 2008-05-14 | 2009-11-17 | Halliburton Energy Services, Inc. | Extended cement compositions comprising oil-swellable particles and associated methods |
US7607484B2 (en) | 2005-09-09 | 2009-10-27 | Halliburton Energy Services, Inc. | Foamed cement compositions comprising oil-swellable particles and methods of use |
US7913757B2 (en) * | 2005-09-16 | 2011-03-29 | Halliburton Energy Services. Inc. | Methods of formulating a cement composition |
US7650940B2 (en) * | 2005-12-29 | 2010-01-26 | Halliburton Energy Services Inc. | Cement compositions comprising particulate carboxylated elastomers and associated methods |
US7645817B2 (en) * | 2005-12-29 | 2010-01-12 | Halliburton Energy Services, Inc. | Cement compositions comprising particulate carboxylated elastomers and associated methods |
EP2038364A2 (fr) | 2006-06-07 | 2009-03-25 | ExxonMobil Upstream Research Company | Objets compressibles à garniture partielle en mousse combinés à un fluide de forage pour former une boue de forage à densité variable |
EP2041235B1 (fr) | 2006-06-07 | 2013-02-13 | ExxonMobil Upstream Research Company | Objets compressibles destinés à être combinés à un fluide de forage pour former une boue de forage à densité variable |
US7575055B2 (en) * | 2006-07-05 | 2009-08-18 | Halliburton Energy Services, Inc. | Storable nonaqueous cement slurries and methods of using same |
CN103898996A (zh) | 2007-03-21 | 2014-07-02 | 阿什工业技术有限责任公司 | 结合微粒基质的实用材料 |
US20090239429A1 (en) | 2007-03-21 | 2009-09-24 | Kipp Michael D | Sound Attenuation Building Material And System |
US8445101B2 (en) | 2007-03-21 | 2013-05-21 | Ashtech Industries, Llc | Sound attenuation building material and system |
US7530396B1 (en) | 2008-01-24 | 2009-05-12 | Halliburton Energy Services, Inc. | Self repairing cement compositions and methods of using same |
US7740066B2 (en) | 2008-01-25 | 2010-06-22 | Halliburton Energy Services, Inc. | Additives for high alumina cements and associated methods |
US8591677B2 (en) | 2008-11-04 | 2013-11-26 | Ashtech Industries, Llc | Utility materials incorporating a microparticle matrix formed with a setting agent |
US7934554B2 (en) * | 2009-02-03 | 2011-05-03 | Halliburton Energy Services, Inc. | Methods and compositions comprising a dual oil/water-swellable particle |
US20100212892A1 (en) * | 2009-02-26 | 2010-08-26 | Halliburton Energy Services, Inc. | Methods of formulating a cement composition |
US8623936B2 (en) | 2009-07-29 | 2014-01-07 | Halliburton Energy Services, Inc. | Weighted elastomers, cement compositions comprising weighted elastomers, and methods of use |
US8450391B2 (en) * | 2009-07-29 | 2013-05-28 | Halliburton Energy Services, Inc. | Weighted elastomers, cement compositions comprising weighted elastomers, and methods of use |
US8689871B2 (en) | 2010-11-08 | 2014-04-08 | Schlumberger Technology Corporation | Compositions and methods for well completions |
US9738822B2 (en) | 2013-10-02 | 2017-08-22 | Schlumberger Technology Corporation | Compositions and methods for cementing wells |
EP3077344A1 (fr) * | 2013-12-06 | 2016-10-12 | Construction Research & Technology GmbH | Procédé de fabrication de compositions cimentaires |
US10947438B2 (en) | 2016-09-20 | 2021-03-16 | Saudi Arabian Oil Company | Method for monitoring cement using polymer-based capsules |
US10377940B2 (en) | 2016-09-20 | 2019-08-13 | Saudi Arabian Oil Company | Cement having cross-linked polymers |
US10947437B2 (en) | 2016-09-20 | 2021-03-16 | Saudi Arabian Oil Company | Chemical composition of superabsorbent vesicles, method for mortar cement admixture, and applications of the same |
US10513905B2 (en) | 2017-03-07 | 2019-12-24 | Saudi Arabian Oil Company | Wellbore cement having spent polymer capsule shells |
WO2018165256A1 (fr) | 2017-03-07 | 2018-09-13 | Saudi Arabian Oil Company | Procédé d'encapsulation d'agents de signalisation destinés à être utilisés en fond de trou |
CN107572975B (zh) * | 2017-07-19 | 2020-06-09 | 中国石油天然气股份有限公司 | 一种堵漏剂、制备方法及其应用 |
US10683724B2 (en) * | 2017-09-11 | 2020-06-16 | Saudi Arabian Oil Company | Curing a lost circulation zone in a wellbore |
US10787600B2 (en) | 2018-01-02 | 2020-09-29 | Saudi Arabian Oil Company | Composition of encapsulated chemical additives and methods for preparation of the same |
CA3087375A1 (fr) | 2018-01-02 | 2019-07-11 | Saudi Arabian Oil Company | Conception de materiau pour l'encapsulation d'additifs et liberation |
WO2019135938A1 (fr) | 2018-01-02 | 2019-07-11 | Saudi Arabian Oil Company | Conception de capsule pour la capture de réactifs |
WO2020013867A1 (fr) * | 2018-07-13 | 2020-01-16 | Halliburton Energy Services, Inc. | Fluides de traitement expansés pour contrôle de perte de circulation |
CN109293262B (zh) * | 2018-10-23 | 2021-05-18 | 常州盘石水泥有限公司 | 一种高强度抗渗水泥及其制备方法 |
CN110407495B (zh) * | 2019-08-30 | 2021-12-14 | 陕西龙宾立德新材料科技有限公司 | 一种抗裂水泥发泡保温板材料及其制备方法 |
US11939520B2 (en) * | 2020-08-12 | 2024-03-26 | Saudi Arabian Oil Company | Methods and cement compositions for reducing corrosion of wellbore casings |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5569324A (en) * | 1994-09-28 | 1996-10-29 | Halliburton Company | Cementitious compositions |
WO2000020350A1 (fr) * | 1998-10-06 | 2000-04-13 | Sofitech N.V. | Compositions de cimentation et leur utilisation pour cimenter des puits de petrole ou similaires |
US6508305B1 (en) * | 1999-09-16 | 2003-01-21 | Bj Services Company | Compositions and methods for cementing using elastic particles |
US6645288B1 (en) * | 1998-12-21 | 2003-11-11 | Schlumberger Technology Corporation | Cementing compositions and application of such compositions for cementing oil wells or the like |
Family Cites Families (69)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3044548A (en) * | 1957-02-27 | 1962-07-17 | Sinclair Oil & Gas Company | Method for selectively plugging a subterranean location in a well with liquid organic resin-forming material |
US3021291A (en) * | 1958-12-15 | 1962-02-13 | Koppers Co Inc | Preparation of concrete containing expanded polymeric particles |
US3214393A (en) * | 1963-02-20 | 1965-10-26 | Koppers Co Inc | Concrete mixture containing expanded polystyrene and a homogenizing agent |
DE1253131C2 (de) * | 1963-08-17 | 1973-05-03 | Basf Ag | Verfahren zum Verbinden von organischen Kunststoffen mit mineralischen Stoffen oder anorganischen hydraulischen Bindemitteln |
US3306356A (en) * | 1964-03-23 | 1967-02-28 | Continental Oil Co | Catalytic polymerization method |
US3363689A (en) * | 1965-03-11 | 1968-01-16 | Halliburton Co | Well cementing |
US3766984A (en) * | 1968-05-20 | 1973-10-23 | Dow Chemical Co | Method for temporarily sealing a permeable formation |
US3764357A (en) * | 1970-03-30 | 1973-10-09 | A Bowles | Method of preparing lightweight concrete and plaster and the lightweight concrete and plaster thus prepared |
US3869295A (en) * | 1970-03-30 | 1975-03-04 | Andrew D Bowles | Uniform lightweight concrete and plaster |
US4010108A (en) * | 1972-01-24 | 1977-03-01 | Nuclear Engineering Company, Inc. | Radioactive waste disposal of water containing waste using urea-formaldehyde resin |
US3804958A (en) * | 1972-01-27 | 1974-04-16 | Goodmark Inc | Process for making pork sausage |
US4221697A (en) * | 1974-05-29 | 1980-09-09 | Imperial Chemical Industries Limited | Composite materials |
US4063608A (en) * | 1974-11-25 | 1977-12-20 | Sullivan Patrick D | Hydrostatic drive vehicle |
DE2710548C2 (de) * | 1977-03-10 | 1982-02-11 | Rudolf 8019 Moosach Hinterwaldner | Lagerstabile härtbare Masse und Verfahren zu deren Härtung |
CH602511A5 (fr) * | 1977-05-23 | 1978-07-31 | Fresse Sa | |
US4306395A (en) * | 1978-06-01 | 1981-12-22 | Carpenter Orval R | Lightweight cementitious product and method for making same |
US4340427A (en) * | 1979-05-10 | 1982-07-20 | Halliburton Company | Well cementing process and gasified cements useful therein |
US4304298A (en) * | 1979-05-10 | 1981-12-08 | Halliburton Company | Well cementing process and gasified cements useful therein |
US4234344A (en) * | 1979-05-18 | 1980-11-18 | Halliburton Company | Lightweight cement and method of cementing therewith |
US4303729A (en) * | 1979-07-20 | 1981-12-01 | Torobin Leonard B | Hollow plastic microspheres |
US4306736A (en) * | 1980-01-17 | 1981-12-22 | Wright Line Inc. | Document holder |
US4370166A (en) * | 1980-09-04 | 1983-01-25 | Standard Oil Company (Indiana) | Low density cement slurry and its use |
US4328038A (en) * | 1980-11-13 | 1982-05-04 | Bj-Hughes Inc. | Resin coated aluminum |
GB2095227B (en) * | 1981-03-24 | 1985-05-01 | Cempol Sales | Making lightweight concrete |
US4367093A (en) * | 1981-07-10 | 1983-01-04 | Halliburton Company | Well cementing process and gasified cements useful therein |
US4460052A (en) * | 1981-08-10 | 1984-07-17 | Judith Gockel | Prevention of lost circulation of drilling muds |
US4498995A (en) * | 1981-08-10 | 1985-02-12 | Judith Gockel | Lost circulation drilling fluid |
US4768593A (en) * | 1983-02-02 | 1988-09-06 | Exxon Production Research Company | Method for primary cementing a well using a drilling mud composition which may be converted to cement upon irradiation |
US4760882A (en) * | 1983-02-02 | 1988-08-02 | Exxon Production Research Company | Method for primary cementing a well with a drilling mud which may be converted to cement using chemical initiators with or without additional irradiation |
US4450010A (en) * | 1983-04-29 | 1984-05-22 | Halliburton Company | Well cementing process and gasified cements useful therein |
US4450009A (en) * | 1983-04-29 | 1984-05-22 | Halliburton Company | Method of preparing a light weight cement composition from sea water |
US4565578A (en) * | 1985-02-26 | 1986-01-21 | Halliburton Company | Gas generation retarded aluminum powder for oil field cements |
US4676317A (en) * | 1986-05-13 | 1987-06-30 | Halliburton Company | Method of reducing fluid loss in cement compositions which may contain substantial salt concentrations |
US4703801A (en) * | 1986-05-13 | 1987-11-03 | Halliburton Company | Method of reducing fluid loss in cement compositions which may contain substantial salt concentrations |
US4816503A (en) * | 1986-06-04 | 1989-03-28 | The Dow Chemical Company | Polymer concrete having high bond strength and long working time |
US4700780A (en) * | 1987-03-27 | 1987-10-20 | Halliburton Services | Method of reducing fluid loss in cement compositions which may contain substantial salt concentrations |
US4806164A (en) * | 1987-03-27 | 1989-02-21 | Halliburton Company | Method of reducing fluid loss in cement compositions |
US4828761A (en) * | 1988-05-04 | 1989-05-09 | The United States Of America As Represented By The United States Department Of Energy | Process for impregnating a concrete or cement body with a polymeric material |
US5124186A (en) * | 1990-02-05 | 1992-06-23 | Mpa Diversified Products Co. | Composite tubular door beam reinforced with a reacted core localized at the mid-span of the tube |
US5456751A (en) * | 1993-09-03 | 1995-10-10 | Trustees Of The University Of Pennsylvania | Particulate rubber included concrete compositions |
US5447984A (en) * | 1994-03-28 | 1995-09-05 | Takemoto Yushi Kabushiki Kaisha | Curable polymer mortar or concrete compositions |
US5837739A (en) * | 1995-06-07 | 1998-11-17 | Mcdonnell Douglas Corporation | Loaded syntactic foam-core material |
EG21132A (en) * | 1995-12-15 | 2000-11-29 | Super Graphite Co | Drilling fluid loss prevention and lubrication additive |
US5736594A (en) * | 1996-03-28 | 1998-04-07 | B J Services Company | Cementing compositions and methods using recycled expanded polystyrene |
US5839520A (en) * | 1996-10-03 | 1998-11-24 | Maillet; Bonnie Blue | Method of drilling well bores |
WO1998020389A1 (fr) * | 1996-11-08 | 1998-05-14 | Optical Coating Laboratory, Inc. | Films de verre souple pour couverture de terminaux a ecran de visualisation |
US5900053A (en) * | 1997-08-15 | 1999-05-04 | Halliburton Energy Services, Inc. | Light weight high temperature well cement compositions and methods |
US5779787A (en) * | 1997-08-15 | 1998-07-14 | Halliburton Energy Services, Inc. | Well cement compositions containing rubber particles and methods of cementing subterranean zones |
US6279652B1 (en) * | 1998-09-23 | 2001-08-28 | Halliburton Energy Services, Inc. | Heat insulation compositions and methods |
GB2362881B (en) * | 1998-11-13 | 2002-08-14 | Sofitech | A cementing composition and application to cementing oil wells or the like |
US6197418B1 (en) * | 1998-12-21 | 2001-03-06 | Agfa-Gevaert, N.V. | Electroconductive glass laminate |
EP1024120B1 (fr) * | 1999-01-29 | 2012-03-07 | Sika Technology AG | Procédé de reduction du retrait des liants hydrauliques |
FR2796935B1 (fr) * | 1999-07-29 | 2001-09-21 | Dowell Schlumberger Services | Coulis de cimentation des puits petroliers ou analogues a basse densite et basse porosite |
FR2799458B1 (fr) * | 1999-10-07 | 2001-12-21 | Dowell Schlumberger Services | Compositions de cimentation et application de ces compositions pour la cimentation des puits petroliers ou analogues |
WO2001053429A1 (fr) * | 2000-01-24 | 2001-07-26 | Wood Robert R | Liquides de forage ameliores |
US6444316B1 (en) * | 2000-05-05 | 2002-09-03 | Halliburton Energy Services, Inc. | Encapsulated chemicals for use in controlled time release applications and methods |
US6530437B2 (en) * | 2000-06-08 | 2003-03-11 | Maurer Technology Incorporated | Multi-gradient drilling method and system |
GB2365859B (en) * | 2000-08-18 | 2002-09-04 | Earth Link Technology Entpr Lt | Cementitious construction materials containing rubber |
US6457524B1 (en) * | 2000-09-15 | 2002-10-01 | Halliburton Energy Services, Inc. | Well cementing compositions and methods |
US6739408B2 (en) * | 2000-10-30 | 2004-05-25 | Baker Hughes Incorporated | Apparatus and method for preparing variable density drilling muds |
US6536540B2 (en) * | 2001-02-15 | 2003-03-25 | De Boer Luc | Method and apparatus for varying the density of drilling fluids in deep water oil drilling applications |
US6367549B1 (en) * | 2001-09-21 | 2002-04-09 | Halliburton Energy Services, Inc. | Methods and ultra-low density sealing compositions for sealing pipe in well bores |
US6732800B2 (en) * | 2002-06-12 | 2004-05-11 | Schlumberger Technology Corporation | Method of completing a well in an unconsolidated formation |
US6516883B1 (en) * | 2002-07-25 | 2003-02-11 | Halliburton Energy Services, Inc. | Methods of cementing pipe in well bores and low density cement compositions therefor |
US6962201B2 (en) * | 2003-02-25 | 2005-11-08 | Halliburton Energy Services, Inc. | Cement compositions with improved mechanical properties and methods of cementing in subterranean formations |
US7147055B2 (en) * | 2003-04-24 | 2006-12-12 | Halliburton Energy Services, Inc. | Cement compositions with improved corrosion resistance and methods of cementing in subterranean formations |
US6904971B2 (en) * | 2003-04-24 | 2005-06-14 | Halliburton Energy Services, Inc. | Cement compositions with improved corrosion resistance and methods of cementing in subterranean formations |
WO2004109053A2 (fr) * | 2003-06-04 | 2004-12-16 | Sun Drilling Products Corporation | Melange colmatant permettant d'obtenir un filtrat pauvre en solides |
US6902001B2 (en) * | 2003-06-10 | 2005-06-07 | Schlumberger Technology Corporation | Cementing compositions and application of such compositions for cementing oil wells or the like |
-
2003
- 2003-12-22 US US10/745,470 patent/US20040171499A1/en not_active Abandoned
-
2004
- 2004-11-23 WO PCT/GB2004/004925 patent/WO2005061846A1/fr active Application Filing
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5569324A (en) * | 1994-09-28 | 1996-10-29 | Halliburton Company | Cementitious compositions |
WO2000020350A1 (fr) * | 1998-10-06 | 2000-04-13 | Sofitech N.V. | Compositions de cimentation et leur utilisation pour cimenter des puits de petrole ou similaires |
US6645288B1 (en) * | 1998-12-21 | 2003-11-11 | Schlumberger Technology Corporation | Cementing compositions and application of such compositions for cementing oil wells or the like |
US6508305B1 (en) * | 1999-09-16 | 2003-01-21 | Bj Services Company | Compositions and methods for cementing using elastic particles |
Cited By (35)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US10005949B2 (en) | 2004-02-10 | 2018-06-26 | Halliburton Energy Services, Inc. | Cement compositions and methods utilizing nano-hydraulic cement |
US9512346B2 (en) | 2004-02-10 | 2016-12-06 | Halliburton Energy Services, Inc. | Cement compositions and methods utilizing nano-hydraulic cement |
WO2006095124A1 (fr) * | 2005-03-11 | 2006-09-14 | Halliburton, Energy Services, Inc. | Compositions pour une cimentation legere a temperature elevee |
US9150773B2 (en) | 2005-09-09 | 2015-10-06 | Halliburton Energy Services, Inc. | Compositions comprising kiln dust and wollastonite and methods of use in subterranean formations |
US9644132B2 (en) | 2005-09-09 | 2017-05-09 | Halliburton Energy Services, Inc. | Methods for determining reactive index for cement kiln dust, associated compositions and methods of use |
US8691737B2 (en) | 2005-09-09 | 2014-04-08 | Halliburton Energy Services, Inc. | Consolidating spacer fluids and methods of use |
US9157020B2 (en) | 2005-09-09 | 2015-10-13 | Halliburton Energy Services, Inc. | Compositions comprising kiln dust and wollastonite and methods of use in subterranean formations |
US8895486B2 (en) | 2005-09-09 | 2014-11-25 | Halliburton Energy Services, Inc. | Methods and compositions comprising cement kiln dust having an altered particle size |
US8895485B2 (en) | 2005-09-09 | 2014-11-25 | Halliburton Energy Services, Inc. | Methods and compositions comprising cement kiln dust having an altered particle size |
US9903184B2 (en) | 2005-09-09 | 2018-02-27 | Halliburton Energy Services, Inc. | Consolidating spacer fluids and methods of use |
US9809737B2 (en) | 2005-09-09 | 2017-11-07 | Halliburton Energy Services, Inc. | Compositions containing kiln dust and/or biowaste ash and methods of use |
US8950486B2 (en) | 2005-09-09 | 2015-02-10 | Halliburton Energy Services, Inc. | Acid-soluble cement compositions comprising cement kiln dust and methods of use |
US9006154B2 (en) | 2005-09-09 | 2015-04-14 | Halliburton Energy Services, Inc. | Methods for determining reactive index for cement kiln dust, associated compositions and methods of use |
US9006155B2 (en) | 2005-09-09 | 2015-04-14 | Halliburton Energy Services, Inc. | Placing a fluid comprising kiln dust in a wellbore through a bottom hole assembly |
US9023150B2 (en) | 2005-09-09 | 2015-05-05 | Halliburton Energy Services, Inc. | Acid-soluble cement compositions comprising cement kiln dust and/or a natural pozzolan and methods of use |
US9051505B2 (en) | 2005-09-09 | 2015-06-09 | Halliburton Energy Services, Inc. | Placing a fluid comprising kiln dust in a wellbore through a bottom hole assembly |
US9676989B2 (en) | 2005-09-09 | 2017-06-13 | Halliburton Energy Services, Inc. | Sealant compositions comprising cement kiln dust and tire-rubber particles and method of use |
US8921284B2 (en) | 2005-09-09 | 2014-12-30 | Halliburton Energy Services, Inc. | Spacer fluids containing cement kiln dust and methods of use |
WO2008092078A1 (fr) * | 2007-01-26 | 2008-07-31 | Bj Services Company | Procédé d'acidification et fracturation mettant en oeuvre des fluides réactifs et des matières particulaires déformables |
US9206344B2 (en) | 2007-05-10 | 2015-12-08 | Halliburton Energy Services, Inc. | Sealant compositions and methods utilizing nano-particles |
US8940670B2 (en) | 2007-05-10 | 2015-01-27 | Halliburton Energy Services, Inc. | Cement compositions comprising sub-micron alumina and associated methods |
US9199879B2 (en) | 2007-05-10 | 2015-12-01 | Halliburton Energy Serives, Inc. | Well treatment compositions and methods utilizing nano-particles |
US9512352B2 (en) | 2007-05-10 | 2016-12-06 | Halliburton Energy Services, Inc. | Well treatment fluids and methods utilizing nano-particles |
US8603952B2 (en) | 2007-05-10 | 2013-12-10 | Halliburton Energy Services, Inc. | Cement compositions and methods utilizing nano-clay |
US9512351B2 (en) | 2007-05-10 | 2016-12-06 | Halliburton Energy Services, Inc. | Well treatment fluids and methods utilizing nano-particles |
US8741818B2 (en) | 2007-05-10 | 2014-06-03 | Halliburton Energy Services, Inc. | Lost circulation compositions and associated methods |
WO2010125327A1 (fr) * | 2009-04-30 | 2010-11-04 | Halliburton Energy Services, Inc. | Procédé de sélection d'un ciment de trou de forage ayant des caractéristiques souhaitables |
US8672029B2 (en) | 2009-12-30 | 2014-03-18 | Schlumberger Technology Corporation | System for reducing foam in mixing operations |
US9409821B2 (en) | 2010-12-08 | 2016-08-09 | Schlumberger Technology Corporation | Compositions and methods for well completions |
US9376609B2 (en) | 2010-12-21 | 2016-06-28 | Halliburton Energy Services, Inc. | Settable compositions comprising interground perlite and hydraulic cement |
US11130899B2 (en) | 2014-06-18 | 2021-09-28 | Schlumberger Technology Corporation | Compositions and methods for well cementing |
US10526523B2 (en) | 2016-02-11 | 2020-01-07 | Schlumberger Technology Corporation | Release of expansion agents for well cementing |
EP3228609A1 (fr) * | 2016-04-08 | 2017-10-11 | Services Pétroliers Schlumberger | Agent d'expansion encapsulé dans un polysiloxan calciné pour la cimentation de puits |
WO2017174208A1 (fr) * | 2016-04-08 | 2017-10-12 | Schlumberger Technology Corporation | Boue comprenant un agent d'expansion encapsulé pour la cimentation de puits |
US10941329B2 (en) | 2016-04-08 | 2021-03-09 | Schlumberger Technology Corporation | Slurry comprising an encapsulated expansion agent for well cementing |
Also Published As
Publication number | Publication date |
---|---|
US20040171499A1 (en) | 2004-09-02 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20040171499A1 (en) | Cement compositions with improved mechanical properties and methods of cementing in a subterranean formation | |
US7543642B2 (en) | Cement compositions containing flexible, compressible beads and methods of cementing in subterranean formations | |
US7282093B2 (en) | Cement compositions with improved mechanical properties and methods of cementing in subterranean formations | |
US7934554B2 (en) | Methods and compositions comprising a dual oil/water-swellable particle | |
US6220354B1 (en) | High strength foamed well cement compositions and methods | |
US7806183B2 (en) | Well treatment compositions and methods utilizing nano-particles | |
US7892352B2 (en) | Well treatment compositions and methods utilizing nano-particles | |
US7172022B2 (en) | Cement compositions containing degradable materials and methods of cementing in subterranean formations | |
EP1769132B1 (fr) | Compositions de ciment comprenant des materiaux a grand allongement, et procedes d'utilisation dans des formations souterraines | |
US6957702B2 (en) | Cement compositions with improved mechanical properties and methods of cementing in a subterranean formation | |
EP1608841A1 (fr) | Compositions de ciment a proprietes mecaniques ameliorees, et procedes de cimentage dans des formations souterraines | |
CA2772374A1 (fr) | Compositions de ciment et procedes associes comprenant du carbonate de calcium submicronique et du latex | |
US20110160096A1 (en) | Methods and Compositions Comprising a Dual Oil/Water-Swellable Particle | |
WO2024020569A1 (fr) | Compositions de géopolymères et procédés |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IS IT LU MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
NENP | Non-entry into the national phase |
Ref country code: DE |
|
WWW | Wipo information: withdrawn in national office |
Country of ref document: DE |
|
122 | Ep: pct application non-entry in european phase |