WO2005059013A1 - A process for preparing polymeric films useful for blocking the transmission of near infra red light - Google Patents
A process for preparing polymeric films useful for blocking the transmission of near infra red light Download PDFInfo
- Publication number
- WO2005059013A1 WO2005059013A1 PCT/US2004/042477 US2004042477W WO2005059013A1 WO 2005059013 A1 WO2005059013 A1 WO 2005059013A1 US 2004042477 W US2004042477 W US 2004042477W WO 2005059013 A1 WO2005059013 A1 WO 2005059013A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- blocking
- infra red
- polymer
- tin oxide
- sheet
- Prior art date
Abstract
Description
Claims