WO2005053065A1 - Battery including aluminum components - Google Patents
Battery including aluminum components Download PDFInfo
- Publication number
- WO2005053065A1 WO2005053065A1 PCT/US2004/038840 US2004038840W WO2005053065A1 WO 2005053065 A1 WO2005053065 A1 WO 2005053065A1 US 2004038840 W US2004038840 W US 2004038840W WO 2005053065 A1 WO2005053065 A1 WO 2005053065A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- current collector
- battery
- aluminum alloy
- weight
- cathode
- Prior art date
Abstract
Description
Claims