WO2004076548A2 - Moisture-crosslinkable polymeric composition - Google Patents

Moisture-crosslinkable polymeric composition Download PDF

Info

Publication number
WO2004076548A2
WO2004076548A2 PCT/US2004/004463 US2004004463W WO2004076548A2 WO 2004076548 A2 WO2004076548 A2 WO 2004076548A2 US 2004004463 W US2004004463 W US 2004004463W WO 2004076548 A2 WO2004076548 A2 WO 2004076548A2
Authority
WO
WIPO (PCT)
Prior art keywords
polymeric composition
crosslinkable polymeric
carbon black
moisture crosslinkable
moisture
Prior art date
Application number
PCT/US2004/004463
Other languages
French (fr)
Other versions
WO2004076548A3 (en
Inventor
Suh Joon Han
David P. Wright
Laurence H. Gross
Michael B. Biscoglio
Thorne M. Bartlett
James M. Leech
Original Assignee
Dow Global Technologies Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dow Global Technologies Inc filed Critical Dow Global Technologies Inc
Priority to DE602004000981T priority Critical patent/DE602004000981T2/en
Priority to US10/546,177 priority patent/US20060269772A1/en
Priority to EP04712291A priority patent/EP1597288B1/en
Priority to JP2006503606A priority patent/JP2006518797A/en
Priority to MXPA05008795A priority patent/MXPA05008795A/en
Priority to CA2516415A priority patent/CA2516415C/en
Publication of WO2004076548A2 publication Critical patent/WO2004076548A2/en
Publication of WO2004076548A3 publication Critical patent/WO2004076548A3/en

Abstract

The present invention is a moisture crosslinkable polymeric composition comprising a siloxane-functional polyolefin polymer and a thermally-treated carbon black. The invention also includes a coating prepared from the moisture crosslinkable polymeric composition as well as a wire-and-cable construction made by applying the coating over a wire or a cable.

Description

MOISTURE-CROSSLINKABLE POLYMERIC COMPOSITION
This invention relates to a moisture-crosslinkable polymeric composition that is useful for wire-and-cable applications, particularly low voltage outdoor applications and medium and high voltage semiconductive shield applications.
Moisture crosslinking has many benefits over peroxide or irradiation-induced crosslinking. However, one drawback to using presently available moisture crosslinkable polymeric compositions is premature crosslinking (or scorching) in the extrusion process. This premature crosslinking prevents uniform product smoothness and quality. Accordingly, there is a need for a moisture crosslinkable polymeric composition, which avoids premature crosslinking. A moisture crosslinkable composition may be prepared from (a) the grafting of vinyl alkoxysilane to an ethylene homopolymer or (b) polymerizing vinyl alkoxysilane with ethylene. It is believed that, when applied to this moisture crosslinkable composition, the silane crosslinking chemistry relies on the participation of water to hydrolyze the pendant alkoxysilane and then condensation to a stable, crosslinking, siloxane structure. Presently available moisture crosslinkable polymeric compositions do not adequately prevent premature crosslinking.
If a suitable moisture crosslinkable polymeric composition is available, it will permit the use of conventional thermoplastic processing equipment, result in low capital investment, require less manufacturing space, and permit greater flexibility in the types of applications. Significantly, if premature crosslinking is avoided, it will prevent adhesion of polymer gel to the surface of the conventional extrusion equipment and facilitate continuous operation of the equipment.
The present invention is a moisture crosslinkable polymeric composition comprising a siloxane-functional polyolefin polymer and a thermally-treated carbon black. The invention also includes a coating prepared from the moisture crosslinkable polymeric composition as well as a wire-and-cable construction made by applying the coating over a wire or a cable.
Using information disclosed herein, a person of ordinary skill in the art could readily identify suitable wire-and-cable constructions, which may be made from the moisture-crosslinkable polymeric composition of the present invention. The invented moisture crosslinkable polymeric composition comprises a siloxane-functional polyolefin polymer and a thermally-treated carbon black.
Suitable siloxane-functional polyolefϊn polymers include (a) ethylene homopolymers having a silane compound grafted thereto and (b) polymerization products of a silane compound and ethylene. Vinyl alkoxysilane is a suitable silane compound for grafting to an ethylene homopolymer. The polymerization products include copolymers and terpolymers. An example of a copolymer is the copolymer of ethylene and vinyl alkoxysilane. An example of a terpolymer is the terpolymer of ethylene, an unsaturated ester, and vinyl alkoxysilane. Preferred unsaturated esters have 4 to 20 carbon atoms.
Preferably, the thermally-treated carbon black is a carbon black, having been post reactor thermally treated at a temperature of at least 400 degrees Celsius. The carbon black may be a furnace black, thermal black, Ketjen black, acetylene black, or any grade of carbon black described in ASTM N110, N351, N472, or N550. In addition, preferably, the thermally-treated carbon black has a loss of volatiles of less than 1.0% by weight at 900 degrees Celsius in nitrogen atmosphere. More preferably, the thermally-treated carbon black has a loss of volatiles of less than 0.1% by weight at 900 degrees Celsius in nitrogen atmosphere.
In addition, the composition may contain other additives such as antioxidants, lubricants, anti-blocking agents, catalysts, fillers, and processing aids.
In another embodiment, the invention is a coating prepared from the moisture crosslinkable polymeric composition of a siloxane-functional polyolefin polymer and a thermally-treated carbon black. In a yet another embodiment, the present invention is a wire or cable construction prepared by applying the coating over a wire or cable. EXAMPLES
The following non-limiting examples illustrate the invention.
Examples 1-12: Carbon Black Masterbatch Comparatives
A carbon black masterbatch was prepared using six commercially-available carbon black materials. The commercially-available carbon black materials included: (1) CC1150 U;
(2) CSX362; (3) M8; (4) M5; (5) M2; and (6) BP3700. While CC1150 U is available from Columbian Chemicals Company, the other carbon black materials are available from Cabot Corporation. For each carbon black, the supplier provided specifications indicating the materials iodine adsorption (mg/g) as measured according to ASTM D1510 and DBP adsorption (cc/lOOg) as measured according to ASTM D2414. The moisture content of each carbon black was measured by Karl Fischer titration.
Table I
Figure imgf000004_0001
It is expected that the moisture content of the thermally-treated carbon black will be less than 200 parts per million (ppm).
Each carbon black masterbatch was prepared using (1) an ethylene ethyl- acrylate copolymer ("EEA") having ethyl-acrylate present at 18 weight % and a melt index of 20 g / 10 min, (2) the carbon black, (3) an ambient cure (fast cure speed) condensation catalyst, and (4) an antioxidant mixture. The masterbatch was prepared using the following weight percents: (1) 47% EAA; (2) 45% carbon black; (3) 4% condensation catalyst; and (4) 4% antioxidant mixture. Table II
Figure imgf000004_0002
It is expected that the moisture content of a carbon black masterbatch made from or containing a thermally-treated carbon black will be less than 200 parts per million (ppm). Examples 13-19: The Extruded Cables Each of the carbon black masterbatches was dry blended with a commercially- available silane-reactor copolymer at a ratio of 5.8 masterbatch to 94.2 silane-ethylene copolymer. The blended composition was extruded using a Brabender extruder over 14AWG copper wire to achieve a wall thickness of 30 mil. The surface of each extruded cable (Examples 13-18) was rough, indicating scorch due to premature crosslinking.
A control cable was extruded using a non-ambient cure (slower cure speed), three-component, silane-crosslinking system (Example 19), commercially available from The Dow Chemical Company as SI-LINK™ PE moisture cure. The control cable showed a smooth surface after extrusion, validating that the extrusion conditions can produce a smooth surface in the absence of pre-cure.
It is expected that a cable extruded from an ambient cure (fast cure speed) moisture crosslinkable polymeric composition made from or containing the thermally- treated carbon black will show a smooth surface after extrusion.

Claims

What is claimed is: 1. A moisture crosslinkable polymeric composition comprising: a. a siloxane-functional polyolefin polymer and b. a thermally-treated carbon black.
2. The moisture crosslinkable polymeric composition of Claim 1 wherein the siloxane-functional polyolefin polymer is an ethylene homopolymer having a silane compound grafted thereto.
3. The moisture crosslinkable polymeric composition of Claim 2 wherein the silane compound is vinyl alkoxysilane.
4. The moisture crosslinkable polymeric composition of Claim 1 wherein the siloxane-functional polyolefin polymer is a polymerization product of a silane compound and ethylene.
5. The moisture crosslinkable polymeric composition of Claim 4 wherein the siloxane-functional polyolefϊn polymer is a copolymer of ethylene and vinyl alkoxysilane.
6. The moisture crosslinkable polymeric composition of Claim 4 wherein the siloxane-functional polyolefin polymer is a terpolymer of ethylene, an unsaturated ester, and vinyl alkoxysilane.
7. The moisture crosslinkable polymeric composition of Claim 4 wherein the silane compound is vinyl alkoxysilane.
8. The moisture crosslinkable polymeric composition of Claim 1 wherein the thermally-treated carbon black is a carbon black, having been post reactor thermally treated at a temperature of at least 400 degrees Celsius.
9. The moisture crosslinkable polymeric composition of Claim 8 wherein the carbon black is selected from the group consisting of furnace black, thermal black, Ketjen black, and acetylene black.
10. The moisture crosslinkable polymeric composition of Claim 1 wherein the thermally-treated carbon black has a loss of volatiles of less than 1.0% by weight at 900 degrees Celsius in nitrogen atmosphere.
11. The moisture crosslinkable polymeric composition of Claim 1 wherein the thermally-treated carbon black has a loss of volatiles of less than 0.1 % by weight at 900 degrees Celsius in nitrogen atmosphere.
12. A coating prepared from the moisture crosslinkable polymeric composition of Claim 1.
13. A wire or cable construction prepared by applying the coating of Claim 12 over a wire or cable.
PCT/US2004/004463 2003-02-21 2004-02-18 Moisture-crosslinkable polymeric composition WO2004076548A2 (en)