WO2004072373A1 - Procede de fabrication d'une structure fibreuse comprenant des fibres de cellulose et synthetiques - Google Patents

Procede de fabrication d'une structure fibreuse comprenant des fibres de cellulose et synthetiques Download PDF

Info

Publication number
WO2004072373A1
WO2004072373A1 PCT/US2004/003337 US2004003337W WO2004072373A1 WO 2004072373 A1 WO2004072373 A1 WO 2004072373A1 US 2004003337 W US2004003337 W US 2004003337W WO 2004072373 A1 WO2004072373 A1 WO 2004072373A1
Authority
WO
WIPO (PCT)
Prior art keywords
fibers
fibrous structure
web
synthetic fibers
molding member
Prior art date
Application number
PCT/US2004/003337
Other languages
English (en)
Inventor
Timothy Jude Lorenz
Osman Polat
Paul Dennis Trokhan
Dean Van Phan
Original Assignee
The Procter & Gamble Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US10/360,038 external-priority patent/US7052580B2/en
Priority claimed from US10/360,021 external-priority patent/US7067038B2/en
Priority claimed from US10/740,060 external-priority patent/US7041196B2/en
Application filed by The Procter & Gamble Company filed Critical The Procter & Gamble Company
Priority to AU2004211619A priority Critical patent/AU2004211619B2/en
Priority to JP2005518379A priority patent/JP2006514176A/ja
Priority to CN2004800033692A priority patent/CN1745215B/zh
Priority to EP04708251A priority patent/EP1590533A1/fr
Priority to CA002514606A priority patent/CA2514606C/fr
Priority to MXPA05007932A priority patent/MXPA05007932A/es
Publication of WO2004072373A1 publication Critical patent/WO2004072373A1/fr

Abstract

l'invention concerne une structure fibreuse (10) et un procédé de fabrication de ladite structure fibreuse (10), consistant à apporter une pluralité de fibres (101) sur un élément de formation (13) ayant un motif de passages, la première pluralité de fibres (101) étant telle qu'au moins une partie des fibres est disposée dans les passages et à apporter une seconde pluralité de fibres (102) sur la première partie de fibres (101) de manière que la seconde pluralité de fibres (102) soit disposée adjacente à la première pluralité de fibres (101) ; et à former une structure fibreuse unitaire contenant la première pluralité et la seconde pluralité de fibres, dont au moins la première pluralité (101) ou la seconde pluralité (102) comporte des fibres synthétiques.
PCT/US2004/003337 2003-02-06 2004-02-04 Procede de fabrication d'une structure fibreuse comprenant des fibres de cellulose et synthetiques WO2004072373A1 (fr)

Priority Applications (6)

Application Number Priority Date Filing Date Title
AU2004211619A AU2004211619B2 (en) 2003-02-06 2004-02-04 Process for making a fibrous structure comprising cellulosic and synthetic fibers
JP2005518379A JP2006514176A (ja) 2003-02-06 2004-02-04 セルロース繊維及び合成繊維を含む繊維構造体を作製する方法
CN2004800033692A CN1745215B (zh) 2003-02-06 2004-02-04 用于制造包括纤维素和合成纤维的纤维结构的方法
EP04708251A EP1590533A1 (fr) 2003-02-06 2004-02-04 Procede de fabrication d'une structure fibreuse comprenant des fibres de cellulose et synthetiques
CA002514606A CA2514606C (fr) 2003-02-06 2004-02-04 Procede de fabrication d'une structure fibreuse comprenant des fibres de cellulose et synthetiques
MXPA05007932A MXPA05007932A (es) 2003-02-06 2004-02-04 Proceso para elaborar una estructura fibrosa que comprende fibras celulosicas y sinteticas.

Applications Claiming Priority (8)

Application Number Priority Date Filing Date Title
US10/360,038 US7052580B2 (en) 2003-02-06 2003-02-06 Unitary fibrous structure comprising cellulosic and synthetic fibers
US10/360,038 2003-02-06
US10/360,021 US7067038B2 (en) 2003-02-06 2003-02-06 Process for making unitary fibrous structure comprising randomly distributed cellulosic fibers and non-randomly distributed synthetic fibers
US10/360,021 2003-02-06
US10/740,060 US7041196B2 (en) 2003-02-06 2003-12-18 Process for making a fibrous structure comprising cellulosic and synthetic fibers
US10/740,059 US7045026B2 (en) 2003-02-06 2003-12-18 Process for making a fibrous structure comprising cellulosic and synthetic fibers
US10/740,060 2003-12-18
US10/740,059 2003-12-18

Publications (1)

Publication Number Publication Date
WO2004072373A1 true WO2004072373A1 (fr) 2004-08-26

Family

ID=32872958

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2004/003337 WO2004072373A1 (fr) 2003-02-06 2004-02-04 Procede de fabrication d'une structure fibreuse comprenant des fibres de cellulose et synthetiques

Country Status (6)

Country Link
EP (1) EP1590533A1 (fr)
JP (1) JP2006514176A (fr)
AU (1) AU2004211619B2 (fr)
CA (1) CA2514606C (fr)
MX (1) MXPA05007932A (fr)
WO (1) WO2004072373A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7041196B2 (en) * 2003-02-06 2006-05-09 The Procter & Gamble Company Process for making a fibrous structure comprising cellulosic and synthetic fibers
WO2007061635A1 (fr) * 2005-11-22 2007-05-31 Albany International Corp. Courroie de formation de fendage de nappe destinee a des produits non tisses
US7396436B2 (en) * 2003-02-06 2008-07-08 The Procter & Gamble Company Unitary fibrous structure comprising randomly distributed cellulosic and non-randomly distributed synthetic fibers

Citations (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3414459A (en) 1965-02-01 1968-12-03 Procter & Gamble Compressible laminated paper structure
US3556907A (en) 1969-01-23 1971-01-19 Paper Converting Machine Co Machine for producing laminated embossed webs
US3879257A (en) 1973-04-30 1975-04-22 Scott Paper Co Absorbent unitary laminate-like fibrous webs and method for producing them
US5178729A (en) 1991-01-15 1993-01-12 James River Corporation Of Virginia High purity stratified tissue and method of making same
WO1993014267A1 (fr) * 1992-01-21 1993-07-22 James River Corporation Of Virginia Papier absorbant renforce
US5245025A (en) * 1991-06-28 1993-09-14 The Procter & Gamble Company Method and apparatus for making cellulosic fibrous structures by selectively obturated drainage and cellulosic fibrous structures produced thereby
US5294475A (en) 1992-06-12 1994-03-15 The Procter & Gamble Company Dual ply cellulosic fibrous structure laminate
US5972813A (en) 1997-12-17 1999-10-26 The Procter & Gamble Company Textured impermeable papermaking belt, process of making, and process of making paper therewith
US6030690A (en) 1997-04-23 2000-02-29 The Procter & Gamble Company High pressure embossing and paper produced thereby
WO2000039394A1 (fr) * 1998-12-30 2000-07-06 Kimberly-Clark Worldwide, Inc. Tissu multicouche comportant une couche de fibres longues a distribution de masse donnant un motif
EP1236827A1 (fr) * 1997-03-21 2002-09-04 Kimberly-Clark Worldwide, Inc. Nappes absorbantes à zone double

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4741941A (en) * 1985-11-04 1988-05-03 Kimberly-Clark Corporation Nonwoven web with projections

Patent Citations (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3414459A (en) 1965-02-01 1968-12-03 Procter & Gamble Compressible laminated paper structure
US3556907A (en) 1969-01-23 1971-01-19 Paper Converting Machine Co Machine for producing laminated embossed webs
US3879257A (en) 1973-04-30 1975-04-22 Scott Paper Co Absorbent unitary laminate-like fibrous webs and method for producing them
US5178729A (en) 1991-01-15 1993-01-12 James River Corporation Of Virginia High purity stratified tissue and method of making same
US5245025A (en) * 1991-06-28 1993-09-14 The Procter & Gamble Company Method and apparatus for making cellulosic fibrous structures by selectively obturated drainage and cellulosic fibrous structures produced thereby
WO1993014267A1 (fr) * 1992-01-21 1993-07-22 James River Corporation Of Virginia Papier absorbant renforce
US5294475A (en) 1992-06-12 1994-03-15 The Procter & Gamble Company Dual ply cellulosic fibrous structure laminate
EP1236827A1 (fr) * 1997-03-21 2002-09-04 Kimberly-Clark Worldwide, Inc. Nappes absorbantes à zone double
US6030690A (en) 1997-04-23 2000-02-29 The Procter & Gamble Company High pressure embossing and paper produced thereby
US5972813A (en) 1997-12-17 1999-10-26 The Procter & Gamble Company Textured impermeable papermaking belt, process of making, and process of making paper therewith
WO2000039394A1 (fr) * 1998-12-30 2000-07-06 Kimberly-Clark Worldwide, Inc. Tissu multicouche comportant une couche de fibres longues a distribution de masse donnant un motif

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7041196B2 (en) * 2003-02-06 2006-05-09 The Procter & Gamble Company Process for making a fibrous structure comprising cellulosic and synthetic fibers
US7396436B2 (en) * 2003-02-06 2008-07-08 The Procter & Gamble Company Unitary fibrous structure comprising randomly distributed cellulosic and non-randomly distributed synthetic fibers
US7645359B2 (en) * 2003-02-06 2010-01-12 The Procter & Gamble Company Process for making a fibrous structure comprising cellulosic and synthetic fibers
WO2007061635A1 (fr) * 2005-11-22 2007-05-31 Albany International Corp. Courroie de formation de fendage de nappe destinee a des produits non tisses

Also Published As

Publication number Publication date
CA2514606A1 (fr) 2004-08-26
EP1590533A1 (fr) 2005-11-02
AU2004211619B2 (en) 2007-05-24
JP2006514176A (ja) 2006-04-27
MXPA05007932A (es) 2005-09-30
CA2514606C (fr) 2008-09-02
AU2004211619A1 (en) 2004-08-26

Similar Documents

Publication Publication Date Title
US7045026B2 (en) Process for making a fibrous structure comprising cellulosic and synthetic fibers
EP1590530B1 (fr) Structure fibreuse unitaire contenant des fibres de cellulose et synthetiques et son procede de fabrication
CA2514599C (fr) Procede permettant de fabriquer une structure fibreuse unitaire comprenant des fibres cellulosiques a repartition aleatoire et des fibres synthetiques a repartition non aleatoire et structure fibreuse unitaire obtenue au moyen dudit procede
AU701610B2 (en) Wet pressed paper web and method of making the same
WO1995017548A9 (fr) Bande de papier pressee au mouille et procede de production de cette derniere
AU2004211619B2 (en) Process for making a fibrous structure comprising cellulosic and synthetic fibers
EP1590532B1 (fr) Structure fibreuse comprenant des fibres de cellulose et synthetiques et son procede de fabrication

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): BW GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IT LU MC NL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 2004708251

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: PA/a/2005/007932

Country of ref document: MX

WWE Wipo information: entry into national phase

Ref document number: 2514606

Country of ref document: CA

WWE Wipo information: entry into national phase

Ref document number: 2005518379

Country of ref document: JP

WWE Wipo information: entry into national phase

Ref document number: 20048033692

Country of ref document: CN

WWE Wipo information: entry into national phase

Ref document number: 2004211619

Country of ref document: AU

ENP Entry into the national phase

Ref document number: 2004211619

Country of ref document: AU

Date of ref document: 20040204

Kind code of ref document: A

WWP Wipo information: published in national office

Ref document number: 2004211619

Country of ref document: AU

WWP Wipo information: published in national office

Ref document number: 2004708251

Country of ref document: EP

WWG Wipo information: grant in national office

Ref document number: 2004211619

Country of ref document: AU