WO2004057688A1 - Improvements in and relating to organic semiconducting materials - Google Patents
Improvements in and relating to organic semiconducting materials Download PDFInfo
- Publication number
- WO2004057688A1 WO2004057688A1 PCT/GB2003/005521 GB0305521W WO2004057688A1 WO 2004057688 A1 WO2004057688 A1 WO 2004057688A1 GB 0305521 W GB0305521 W GB 0305521W WO 2004057688 A1 WO2004057688 A1 WO 2004057688A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- composition
- molecular weight
- semiconducting
- lower molecular
- layer
- Prior art date
Abstract
Description
Claims