WO2004016341A2 - Fluoropolymer membrane - Google Patents
Fluoropolymer membrane Download PDFInfo
- Publication number
- WO2004016341A2 WO2004016341A2 PCT/US2003/022907 US0322907W WO2004016341A2 WO 2004016341 A2 WO2004016341 A2 WO 2004016341A2 US 0322907 W US0322907 W US 0322907W WO 2004016341 A2 WO2004016341 A2 WO 2004016341A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- membrane
- fluoropolymer membrane
- fibrils
- porous fluoropolymer
- free
- Prior art date
Abstract
Description
Claims