WO2003078715A1 - Procede de production d'une toile non tissee filee-liee a meilleure resistance a l'abrasion - Google Patents

Procede de production d'une toile non tissee filee-liee a meilleure resistance a l'abrasion Download PDF

Info

Publication number
WO2003078715A1
WO2003078715A1 PCT/US2003/007386 US0307386W WO03078715A1 WO 2003078715 A1 WO2003078715 A1 WO 2003078715A1 US 0307386 W US0307386 W US 0307386W WO 03078715 A1 WO03078715 A1 WO 03078715A1
Authority
WO
WIPO (PCT)
Prior art keywords
spun
bonded nonwoven
fiber
nonwoven fabric
low melt
Prior art date
Application number
PCT/US2003/007386
Other languages
English (en)
Inventor
Dave E. Wenstrup
Original Assignee
Milliken & Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US10/099,082 external-priority patent/US20030176135A1/en
Priority claimed from US10/099,398 external-priority patent/US6720278B2/en
Application filed by Milliken & Company filed Critical Milliken & Company
Priority to AU2003230625A priority Critical patent/AU2003230625A1/en
Publication of WO2003078715A1 publication Critical patent/WO2003078715A1/fr

Abstract

L'invention concerne un procédé permettant d'améliorer la résistance à l'abrasion d'un non-tissé filé-lié, sans nuire de manière sensible à son toucher ou à ses caractéristiques de drapage, par incorporation à la toile de fibres liantes à fusion basse pendant la phase de pose du processus de production de non-tissé filé-lié. Plus précisément, on obtient une meilleure résistance à l'abrasion en mélangeant intimement des fibres liantes continues avec les fibres extrudées primaires dans une toile non tissée filée-liée. L'invention concerne en outre un tissu non tissé filé-lié d'une meilleure résistance à l'abrasion, qui comprend des fibres extrudées primaires et des fibres liantes à fusion basse, les fibres liantes à fusion basse étant constituées de tissu non tissé filé-liée dans une proportion située entre environ 1 et environ 50 % en poids.
PCT/US2003/007386 2002-03-15 2003-03-10 Procede de production d'une toile non tissee filee-liee a meilleure resistance a l'abrasion WO2003078715A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU2003230625A AU2003230625A1 (en) 2002-03-15 2003-03-10 Method for producing a spun-bonded nonwoven web with improved abrasion resistance

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US10/099,398 2002-03-15
US10/099,082 2002-03-15
US10/099,082 US20030176135A1 (en) 2002-03-15 2002-03-15 Method for producing a spun-bonded nonwoven web with improved abrasion resistance
US10/099,398 US6720278B2 (en) 2002-03-15 2002-03-15 Method for producing a spun-bonded nonwoven web with improved abrasion resistance

Publications (1)

Publication Number Publication Date
WO2003078715A1 true WO2003078715A1 (fr) 2003-09-25

Family

ID=28044141

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2003/007386 WO2003078715A1 (fr) 2002-03-15 2003-03-10 Procede de production d'une toile non tissee filee-liee a meilleure resistance a l'abrasion

Country Status (2)

Country Link
AU (1) AU2003230625A1 (fr)
WO (1) WO2003078715A1 (fr)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3740797A (en) * 1971-01-21 1973-06-26 Johnson & Johnson Method of forming webs and apparatus therefor
US3768118A (en) * 1971-01-21 1973-10-30 Johnson & Johnson Web forming process
US5685757A (en) * 1989-06-20 1997-11-11 Corovin Gmbh Fibrous spun-bonded non-woven composite
US6355079B1 (en) * 1998-10-01 2002-03-12 Bki Holding Corporation Production method for multilayer filter material and multilayer filter material

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3740797A (en) * 1971-01-21 1973-06-26 Johnson & Johnson Method of forming webs and apparatus therefor
US3768118A (en) * 1971-01-21 1973-10-30 Johnson & Johnson Web forming process
US5685757A (en) * 1989-06-20 1997-11-11 Corovin Gmbh Fibrous spun-bonded non-woven composite
US6355079B1 (en) * 1998-10-01 2002-03-12 Bki Holding Corporation Production method for multilayer filter material and multilayer filter material

Also Published As

Publication number Publication date
AU2003230625A1 (en) 2003-09-29

Similar Documents

Publication Publication Date Title
KR101871814B1 (ko) 극세사 복합 부직포
US6735833B2 (en) Nonwoven fabrics having a durable three-dimensional image
US20060225228A1 (en) Nonwoven fabrics having intercalated three-dimensional images
US6629340B1 (en) Acoustic underlayment for pre-finished laminate floor system
JP2019501077A (ja) 中実多葉形繊維を用いた自動車用カーペット
US6720278B2 (en) Method for producing a spun-bonded nonwoven web with improved abrasion resistance
RU2233359C2 (ru) Синтетическая кожа и способ ее получения
EP1492914B1 (fr) Non-tisse double face comportant une image tridimensionnelle
US6832418B2 (en) Nonwoven secondary carpet backing
EP1492912B1 (fr) Non-tisses presentant des images tridimensionnelles composites
US20030176135A1 (en) Method for producing a spun-bonded nonwoven web with improved abrasion resistance
US6878648B2 (en) Regionally imprinted nonwoven fabric
JPS6316504B2 (fr)
WO2003078715A1 (fr) Procede de production d'une toile non tissee filee-liee a meilleure resistance a l'abrasion
JP7405310B1 (ja) 人工皮革およびその製造方法、ならびに、乗物用内装材、座席
WO2024029215A1 (fr) Cuir artificiel, son procédé de production, matériau d'intérieur de véhicule et siège
KR20220046350A (ko) 중량이 낮은 내마모성 중실 다엽형 섬유를 갖는 자동차용 카펫
KR20070028318A (ko) 흡음성 이차 부직 카펫 기포
MXPA06008834A (es) Respaldo secundario de alfombra, no tejido, que absorbe el sonido

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NI NO NZ OM PH PL PT RO RU SC SD SE SG SK SL TJ TM TN TR TT TZ UA UG UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IT LU MC NL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: JP

WWW Wipo information: withdrawn in national office

Country of ref document: JP