WO2003033250A1 - Silver ink for forming electrodes - Google Patents
Silver ink for forming electrodes Download PDFInfo
- Publication number
- WO2003033250A1 WO2003033250A1 PCT/US2002/033163 US0233163W WO03033250A1 WO 2003033250 A1 WO2003033250 A1 WO 2003033250A1 US 0233163 W US0233163 W US 0233163W WO 03033250 A1 WO03033250 A1 WO 03033250A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- set forth
- metal oxide
- conductive ink
- ink composition
- layers
- Prior art date
Abstract
Description
Claims