WO2003028945A1 - Liquid phase sintered braze forms - Google Patents
Liquid phase sintered braze forms Download PDFInfo
- Publication number
- WO2003028945A1 WO2003028945A1 PCT/US2002/027686 US0227686W WO03028945A1 WO 2003028945 A1 WO2003028945 A1 WO 2003028945A1 US 0227686 W US0227686 W US 0227686W WO 03028945 A1 WO03028945 A1 WO 03028945A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- filler metal
- braze preform
- powder
- liquid phase
- preform
- Prior art date
Abstract
Description
Claims