WO2003020597A1 - Card sheet construction - Google Patents
Card sheet construction Download PDFInfo
- Publication number
- WO2003020597A1 WO2003020597A1 PCT/US2002/027518 US0227518W WO03020597A1 WO 2003020597 A1 WO2003020597 A1 WO 2003020597A1 US 0227518 W US0227518 W US 0227518W WO 03020597 A1 WO03020597 A1 WO 03020597A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- sheet
- polymer
- card
- top material
- carrier
- Prior art date
Abstract
Description
Claims