WO2002096475A1 - Modified oxide - Google Patents
Modified oxide Download PDFInfo
- Publication number
- WO2002096475A1 WO2002096475A1 PCT/SE2002/001024 SE0201024W WO02096475A1 WO 2002096475 A1 WO2002096475 A1 WO 2002096475A1 SE 0201024 W SE0201024 W SE 0201024W WO 02096475 A1 WO02096475 A1 WO 02096475A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- titanium
- implant
- calcium
- oxide
- anodic
- Prior art date
Abstract
Description
Claims