WO2002051904A1 - Isocyanic compositions and use thereof in the preparation of expanded polyurethanes with improved fire behaviour - Google Patents
Isocyanic compositions and use thereof in the preparation of expanded polyurethanes with improved fire behaviour Download PDFInfo
- Publication number
- WO2002051904A1 WO2002051904A1 PCT/EP2001/015276 EP0115276W WO02051904A1 WO 2002051904 A1 WO2002051904 A1 WO 2002051904A1 EP 0115276 W EP0115276 W EP 0115276W WO 02051904 A1 WO02051904 A1 WO 02051904A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- weight
- isocyanic
- polyol
- toluene diisocyanate
- functionality
- Prior art date
Abstract
Description
Claims