WO2002016972A2 - Transparent plastic or polymer based mirror apparatus and method for making the same - Google Patents
Transparent plastic or polymer based mirror apparatus and method for making the same Download PDFInfo
- Publication number
- WO2002016972A2 WO2002016972A2 PCT/US2001/026408 US0126408W WO0216972A2 WO 2002016972 A2 WO2002016972 A2 WO 2002016972A2 US 0126408 W US0126408 W US 0126408W WO 0216972 A2 WO0216972 A2 WO 0216972A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- polymer
- coating
- minor
- sio
- Prior art date
Abstract
Description
Claims