WO2001070630A2 - Procede de fabrication de zeolites d'aluminosilicate a teneur en aluminium elevee, de zeolites microcristallines et agregats macroscopiques de celles-ci - Google Patents

Procede de fabrication de zeolites d'aluminosilicate a teneur en aluminium elevee, de zeolites microcristallines et agregats macroscopiques de celles-ci Download PDF

Info

Publication number
WO2001070630A2
WO2001070630A2 PCT/US2001/009070 US0109070W WO0170630A2 WO 2001070630 A2 WO2001070630 A2 WO 2001070630A2 US 0109070 W US0109070 W US 0109070W WO 0170630 A2 WO0170630 A2 WO 0170630A2
Authority
WO
WIPO (PCT)
Prior art keywords
zeolite
source
aluminum
composition
silicate
Prior art date
Application number
PCT/US2001/009070
Other languages
English (en)
Other versions
WO2001070630A3 (fr
Inventor
Steven M. Kuznicki
Tadeusz W. Langner
Jacqueline S. Curran
Valerie A. Bell
Original Assignee
Engelhard Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US09/533,771 external-priority patent/US6451283B1/en
Priority claimed from US09/533,606 external-priority patent/US6413492B1/en
Priority claimed from US09/533,707 external-priority patent/US6416732B1/en
Application filed by Engelhard Corporation filed Critical Engelhard Corporation
Priority to AU2001249319A priority Critical patent/AU2001249319A1/en
Publication of WO2001070630A2 publication Critical patent/WO2001070630A2/fr
Publication of WO2001070630A3 publication Critical patent/WO2001070630A3/fr

Abstract

L'invention concerne des zéolites d'aluminosilicate fabriquées dans un nouveau milieu de réaction contenant une source de silicate et une source d'aluminium dans une solution aqueuse alcaline. Le rapport Si/Al du mélange de réaction étant d'au moins 1,0 et le milieu de réaction comprenant également un sel électrolytique supplémentaire. L'adjonction du sel électrolytique forme des sites de nucléation qui sont destinés à la zéolite de manière à former des cristaux de très petite taille. Dans des environnements à teneur en silicate élevée, il est possible de créer des zéolites à teneur en aluminium élevée contenant du silicate occlus, et dans lesquels la morphologie des zéolites comprend des agrégats macroscopiques de zéolites microcristallines. L'adjonction de sel électrolyte peut également permettre de réduire le temps de réaction ou la température nécessaire à la cristallisation. Les compositions zéolitiques décrites dans cette invention présentent une capacité exceptionnelle à complexer des cations polyvalents, en particulier le calcium, en raison de la cinétique d'échange élevée du composant de zéolite microcristalline. Toutefois, ces compositions sont d'utilisation facile en raison de l'assemblage d'agrégats macroscopiques.
PCT/US2001/009070 2000-03-23 2001-03-22 Procede de fabrication de zeolites d'aluminosilicate a teneur en aluminium elevee, de zeolites microcristallines et agregats macroscopiques de celles-ci WO2001070630A2 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU2001249319A AU2001249319A1 (en) 2000-03-23 2001-03-22 A method of forming high aluminum aluminosilicate zeolites, microcrystalline zeolites and macroscopic aggregates thereof

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
US09/533,606 2000-03-23
US09/533,771 2000-03-23
US09/533,771 US6451283B1 (en) 2000-03-23 2000-03-23 Macroscopic aggregates of microcrystalline zeolites
US09/533,707 2000-03-23
US09/533,606 US6413492B1 (en) 2000-03-23 2000-03-23 Method of forming high aluminum aluminosilicate zeolites
US09/533,707 US6416732B1 (en) 2000-03-23 2000-03-23 Method of forming aluminosilicate zeolites

Publications (2)

Publication Number Publication Date
WO2001070630A2 true WO2001070630A2 (fr) 2001-09-27
WO2001070630A3 WO2001070630A3 (fr) 2002-01-24

Family

ID=27415133

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2001/009070 WO2001070630A2 (fr) 2000-03-23 2001-03-22 Procede de fabrication de zeolites d'aluminosilicate a teneur en aluminium elevee, de zeolites microcristallines et agregats macroscopiques de celles-ci

Country Status (2)

Country Link
AU (1) AU2001249319A1 (fr)
WO (1) WO2001070630A2 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2002026627A1 (fr) * 2000-09-25 2002-04-04 Engelhard Corporation Nouvelles compositions zeolithes de faujasite hexagonale a forte teneur en aluminium
WO2002048043A2 (fr) * 2000-12-14 2002-06-20 Engelhard Corporation Adoucisseur poreux d'eau statique contenant une composition hybride de zeolite-silicate
WO2002048040A2 (fr) * 2000-12-14 2002-06-20 Engelhard Corporation Agregats macroscopiques de zeolites microcristallines a utiliser pour l'adoucissement de l'eau statique
WO2002066381A2 (fr) * 2000-12-14 2002-08-29 Engelhard Corporation Procede d'adoucissement de l'eau statique utilisant des zeolites d'une nouvelle morphologie
WO2019059594A1 (fr) * 2017-09-22 2019-03-28 주식회사 엘지화학 Méthode de fabrication de nanoparticules d'aluminosilicate ayant une excellente dispersibilité, élément de renfort de caoutchouc contenant les nanoparticules d'aluminosilicate, et composition de caoutchouc comprenant ledit élément pour pneumatique

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2376073A1 (fr) * 1976-12-30 1978-07-28 Rhone Poulenc Ind Nouveau silico-aluminate alcalin cristallin de type 4 a ainsi que son procede d'obtention et application
US4443422A (en) * 1978-12-20 1984-04-17 J. M. Huber Corporation Synthesis of zeolites of small and uniform size having a high magnesium exchange capacity
US5512266A (en) * 1988-11-03 1996-04-30 Unilever Patent Holdings Bv Aluminosilicates and detergent composition
US5525323A (en) * 1993-07-15 1996-06-11 Basf Aktiengesellschaft Pentasil zeolites agglomerated in the form of hollow spheres
US5948383A (en) * 1997-03-26 1999-09-07 Engelhard Corporation Hybrid zeolite-silica compositions

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2793375B2 (ja) * 1991-03-19 1998-09-03 株式会社神戸製鋼所 Ｐ型ゼオライトの製造方法
JP2793376B2 (ja) * 1991-03-19 1998-09-03 株式会社神戸製鋼所 Ａ型ゼオライトの製造方法

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2376073A1 (fr) * 1976-12-30 1978-07-28 Rhone Poulenc Ind Nouveau silico-aluminate alcalin cristallin de type 4 a ainsi que son procede d'obtention et application
US4443422A (en) * 1978-12-20 1984-04-17 J. M. Huber Corporation Synthesis of zeolites of small and uniform size having a high magnesium exchange capacity
US5512266A (en) * 1988-11-03 1996-04-30 Unilever Patent Holdings Bv Aluminosilicates and detergent composition
US5525323A (en) * 1993-07-15 1996-06-11 Basf Aktiengesellschaft Pentasil zeolites agglomerated in the form of hollow spheres
US5948383A (en) * 1997-03-26 1999-09-07 Engelhard Corporation Hybrid zeolite-silica compositions

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
PATENT ABSTRACTS OF JAPAN vol. 017, no. 685 (C-1142), 15 December 1993 (1993-12-15) & JP 05 229814 A (KOBE STEEL LTD), 7 September 1993 (1993-09-07) *
PATENT ABSTRACTS OF JAPAN vol. 017, no. 700 (C-1145), 21 December 1993 (1993-12-21) & JP 05 238724 A (KOBE STEEL LTD), 17 September 1993 (1993-09-17) *

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2002026627A1 (fr) * 2000-09-25 2002-04-04 Engelhard Corporation Nouvelles compositions zeolithes de faujasite hexagonale a forte teneur en aluminium
WO2002048043A2 (fr) * 2000-12-14 2002-06-20 Engelhard Corporation Adoucisseur poreux d'eau statique contenant une composition hybride de zeolite-silicate
WO2002048040A2 (fr) * 2000-12-14 2002-06-20 Engelhard Corporation Agregats macroscopiques de zeolites microcristallines a utiliser pour l'adoucissement de l'eau statique
WO2002066381A2 (fr) * 2000-12-14 2002-08-29 Engelhard Corporation Procede d'adoucissement de l'eau statique utilisant des zeolites d'une nouvelle morphologie
WO2002048040A3 (fr) * 2000-12-14 2003-01-23 Engelhard Corp Agregats macroscopiques de zeolites microcristallines a utiliser pour l'adoucissement de l'eau statique
WO2002066381A3 (fr) * 2000-12-14 2003-01-23 Engelhard Corp Procede d'adoucissement de l'eau statique utilisant des zeolites d'une nouvelle morphologie
WO2002048043A3 (fr) * 2000-12-14 2003-12-18 Engelhard Corp Adoucisseur poreux d'eau statique contenant une composition hybride de zeolite-silicate
WO2019059594A1 (fr) * 2017-09-22 2019-03-28 주식회사 엘지화학 Méthode de fabrication de nanoparticules d'aluminosilicate ayant une excellente dispersibilité, élément de renfort de caoutchouc contenant les nanoparticules d'aluminosilicate, et composition de caoutchouc comprenant ledit élément pour pneumatique

Also Published As

Publication number Publication date
AU2001249319A1 (en) 2001-10-03
WO2001070630A3 (fr) 2002-01-24

Similar Documents

Publication Publication Date Title
US6451283B1 (en) Macroscopic aggregates of microcrystalline zeolites
EP0970017B1 (fr) Nouvelles compositions hybrides a base de zeolithe-silice
CA1062984A (fr) Suspensions aqueuses stables d'aluminosilicates insolubles dans l'eau, retenant le calcium, et d'agents de suspension organiques
CA1083916A (fr) Produit granulaire
CA1230797A (fr) Composition detergente
NO802171L (no) Fremgangsmaate til fremstilling av et vaske- og rensemiddel
JPS6052192B2 (ja) 洗剤組成物
US4169075A (en) Process for the production of powdery washing agents by spray-drying
US4179393A (en) Stable aqueous suspension of water-insoluble, calcium-binding aluminosilicates and organic suspending agents
US6416732B1 (en) Method of forming aluminosilicate zeolites
CA1052658A (fr) Lavage des textiles; produit comprenant des silicates inorganiques, et des polycarboxylates ou des polyphosphonates
WO1995000622A1 (fr) Compositions detergentes granulaires contenant des adjuvants selectionnes dans des proportions optimales
WO2001070630A2 (fr) Procede de fabrication de zeolites d'aluminosilicate a teneur en aluminium elevee, de zeolites microcristallines et agregats macroscopiques de celles-ci
US6413492B1 (en) Method of forming high aluminum aluminosilicate zeolites
EP0713478B1 (fr) Matieres composites a base de silicate
CA1039607A (fr) Produits de lavage contenant des aluminosilicates et des agents tenseurs specifiques; methode de lavage des textiles
EP0315282B1 (fr) Zéolites dans des compositions détergentes liquides
EP0292193B1 (fr) Composition détergente
EP0717769A1 (fr) Silicate cristallin de sodium et de potassium
US20080261848A1 (en) Multifunctional Material Compositions and Methods
CA1314189C (fr) Compositions detergentes
US5145599A (en) Use of cationic non-silicate layer compounds in detergents
US20150329800A1 (en) Methods for prevention and reduction of scale formation
CA2005931A1 (fr) Compositions a base de zeolite
JPH0129839B2 (fr)

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A2

Designated state(s): AE AL AM AT AU AZ BA BB BG BR BY CA CH CN CR CU CZ DE DK DM EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A2

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
AK Designated states

Kind code of ref document: A3

Designated state(s): AE AL AM AT AU AZ BA BB BG BR BY CA CH CN CR CU CZ DE DK DM EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A3

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase in:

Ref country code: JP