WO2001048264A1 - Composition and process for treating metal surface and resulting article - Google Patents
Composition and process for treating metal surface and resulting article Download PDFInfo
- Publication number
- WO2001048264A1 WO2001048264A1 PCT/US2000/035039 US0035039W WO0148264A1 WO 2001048264 A1 WO2001048264 A1 WO 2001048264A1 US 0035039 W US0035039 W US 0035039W WO 0148264 A1 WO0148264 A1 WO 0148264A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- component
- moieties
- mass
- parts
- group
- Prior art date
Abstract
Description
Claims