WO2001046597A1 - Releasable fasteners - Google Patents
Releasable fasteners Download PDFInfo
- Publication number
- WO2001046597A1 WO2001046597A1 PCT/GB2000/004954 GB0004954W WO0146597A1 WO 2001046597 A1 WO2001046597 A1 WO 2001046597A1 GB 0004954 W GB0004954 W GB 0004954W WO 0146597 A1 WO0146597 A1 WO 0146597A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- shape memory
- fastener
- region
- blank
- engagement region
- Prior art date
Abstract
Description
Claims