WO2001014641A1 - Produits en ouate de cellulose, presentant des proprietes d'absorbance ameliorees - Google Patents

Produits en ouate de cellulose, presentant des proprietes d'absorbance ameliorees Download PDF

Info

Publication number
WO2001014641A1
WO2001014641A1 PCT/US2000/022978 US0022978W WO0114641A1 WO 2001014641 A1 WO2001014641 A1 WO 2001014641A1 US 0022978 W US0022978 W US 0022978W WO 0114641 A1 WO0114641 A1 WO 0114641A1
Authority
WO
WIPO (PCT)
Prior art keywords
superabsorbent material
tissue product
weight
web
grams
Prior art date
Application number
PCT/US2000/022978
Other languages
English (en)
Inventor
Dale Burghardt
Palani Raj Wallajapet
Sheng-Hsin Hu
Original Assignee
Kimberly-Clark Worldwide, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kimberly-Clark Worldwide, Inc. filed Critical Kimberly-Clark Worldwide, Inc.
Priority to AU70643/00A priority Critical patent/AU7064300A/en
Priority to MXPA02001684A priority patent/MXPA02001684A/es
Publication of WO2001014641A1 publication Critical patent/WO2001014641A1/fr

Abstract

L'invention concerne un produit en ouate de cellulose, contenant un matériau fibreux cellulosique et moins d'environ 10 % en poids d'un matériau superabsorbant (entre autres, fibres, particules). Dans certains cas, le matériau superabsorbant peut absorber entre environ 100 à environ 350 grammes d'une solution aqueuse par gramme de matériau superabsorbant. Dans certains modes de réalisation, le matériau superabsorbant peut être appliqué dans l'étape de préparation de la pâte, d'un procédé de fabrication de papier, et peut être fourni à l'état sec ou pré-gonflé.
PCT/US2000/022978 1999-08-23 2000-08-22 Produits en ouate de cellulose, presentant des proprietes d'absorbance ameliorees WO2001014641A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
AU70643/00A AU7064300A (en) 1999-08-23 2000-08-22 Tissue products having increased absorbency
MXPA02001684A MXPA02001684A (es) 1999-08-23 2000-08-22 Productos de tisu que tienen una absorbencia incrementada.

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US15032599P 1999-08-23 1999-08-23
US60/150,325 1999-08-23

Publications (1)

Publication Number Publication Date
WO2001014641A1 true WO2001014641A1 (fr) 2001-03-01

Family

ID=22534045

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2000/022978 WO2001014641A1 (fr) 1999-08-23 2000-08-22 Produits en ouate de cellulose, presentant des proprietes d'absorbance ameliorees

Country Status (4)

Country Link
AR (1) AR025360A1 (fr)
AU (1) AU7064300A (fr)
MX (1) MXPA02001684A (fr)
WO (1) WO2001014641A1 (fr)

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1325981A1 (fr) * 2002-01-05 2003-07-09 The Procter & Gamble Company Serviettes multicouches avec des fibres superabsorbantes
EP1327716A1 (fr) * 2002-01-05 2003-07-16 The Procter & Gamble Company Papier tissu multi couches
WO2004044325A1 (fr) * 2002-11-08 2004-05-27 Kimberly-Clark Worldwide, Inc. Procede permettant d'ameliorer la douceur de produits a base de papier
WO2006077613A1 (fr) * 2005-01-21 2006-07-27 Fabio Perini S.P.A. Procede et systeme permettant de produire un article en papier de soie ou analogue comprenant un materiau superabsorbant
US7211171B2 (en) 2002-01-05 2007-05-01 The Procter & Gamble Company Multiply tissue product
US7449085B2 (en) * 2003-09-02 2008-11-11 Kimberly-Clark Worldwide, Inc. Paper sheet having high absorbent capacity and delayed wet-out
US7678228B2 (en) 2004-07-15 2010-03-16 Kimberly-Clark Worldwide, Inc. Binders curable at room temperature with low blocking
US8021518B2 (en) 2006-11-30 2011-09-20 Nalco Company Method of applying a super-absorbent composition to tissue or towel substrates
EP2880218A4 (fr) * 2012-07-31 2016-05-25 Kimberly Clark Co Tissu très gonflant comprenant des microsphères expansibles

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1997017397A1 (fr) * 1995-11-03 1997-05-15 Basf Aktiengesellschaft Polymeres hydrogels absorbant l'eau, en mousse, reticules
WO1997036047A1 (fr) * 1996-03-25 1997-10-02 Eka Chemicals Ab Materiau absorbant et son procede de production
WO1999034057A1 (fr) * 1997-12-24 1999-07-08 Kimberly-Clark Worldwide, Inc. Produits de papier et procedes pour l'application d'additifs chimiques sur des fibres cellulosiques
US5997690A (en) * 1998-02-18 1999-12-07 Basf Corporation Smooth textured wet-laid absorbent structure

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1997017397A1 (fr) * 1995-11-03 1997-05-15 Basf Aktiengesellschaft Polymeres hydrogels absorbant l'eau, en mousse, reticules
WO1997036047A1 (fr) * 1996-03-25 1997-10-02 Eka Chemicals Ab Materiau absorbant et son procede de production
WO1999034057A1 (fr) * 1997-12-24 1999-07-08 Kimberly-Clark Worldwide, Inc. Produits de papier et procedes pour l'application d'additifs chimiques sur des fibres cellulosiques
US5997690A (en) * 1998-02-18 1999-12-07 Basf Corporation Smooth textured wet-laid absorbent structure

Cited By (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7211171B2 (en) 2002-01-05 2007-05-01 The Procter & Gamble Company Multiply tissue product
EP1327716A1 (fr) * 2002-01-05 2003-07-16 The Procter & Gamble Company Papier tissu multi couches
WO2003057990A1 (fr) * 2002-01-05 2003-07-17 The Procter & Gamble Company Produit de papier menager multicouche
EP1325981A1 (fr) * 2002-01-05 2003-07-09 The Procter & Gamble Company Serviettes multicouches avec des fibres superabsorbantes
WO2004044325A1 (fr) * 2002-11-08 2004-05-27 Kimberly-Clark Worldwide, Inc. Procede permettant d'ameliorer la douceur de produits a base de papier
US6808600B2 (en) 2002-11-08 2004-10-26 Kimberly-Clark Worldwide, Inc. Method for enhancing the softness of paper-based products
US7449085B2 (en) * 2003-09-02 2008-11-11 Kimberly-Clark Worldwide, Inc. Paper sheet having high absorbent capacity and delayed wet-out
US7678228B2 (en) 2004-07-15 2010-03-16 Kimberly-Clark Worldwide, Inc. Binders curable at room temperature with low blocking
US7678856B2 (en) 2004-07-15 2010-03-16 Kimberly-Clark Worldwide Inc. Binders curable at room temperature with low blocking
WO2006077613A1 (fr) * 2005-01-21 2006-07-27 Fabio Perini S.P.A. Procede et systeme permettant de produire un article en papier de soie ou analogue comprenant un materiau superabsorbant
US8007639B2 (en) 2005-01-21 2011-08-30 Fabio Perini S.P.A. System for producing an article made of tissue paper or the like comprising a superabsorbent material
US8021518B2 (en) 2006-11-30 2011-09-20 Nalco Company Method of applying a super-absorbent composition to tissue or towel substrates
EP2880218A4 (fr) * 2012-07-31 2016-05-25 Kimberly Clark Co Tissu très gonflant comprenant des microsphères expansibles

Also Published As

Publication number Publication date
AR025360A1 (es) 2002-11-20
AU7064300A (en) 2001-03-19
MXPA02001684A (es) 2002-09-23

Similar Documents

Publication Publication Date Title
US6096152A (en) Creped tissue product having a low friction surface and improved wet strength
US6322665B1 (en) Reactive compounds to fibrous webs
US6911114B2 (en) Tissue with semi-synthetic cationic polymer
EP1102896B1 (fr) Papier resistant a la penetration de fluides
CA2291733C (fr) Serviette/chiffon absorbant avec surface renforcee et procede de production associe
US6379498B1 (en) Method for adding an adsorbable chemical additive to pulp during the pulp processing and products made by said method
US6264791B1 (en) Flash curing of fibrous webs treated with polymeric reactive compounds
US6979386B1 (en) Tissue products having increased absorbency
AU2001239938A1 (en) Method for adding an adsorbable chemical additive to pulp during the pulp processing and products made by said method
SE1251427A1 (sv) Våtlagt arkmaterial av en mikrofibrillerad materialkomposition
WO1999025924A1 (fr) Tissu de base absorbant les liquides
WO2007100667A2 (fr) Procédé de traitement d'un substrat
WO2006038977A1 (fr) Objets absorbants comprenant des fibres de résine thermoplastique prétraitées
US20020112830A1 (en) Process for increasing the softness of base webs and products made therefrom
US6808600B2 (en) Method for enhancing the softness of paper-based products
WO2001014641A1 (fr) Produits en ouate de cellulose, presentant des proprietes d'absorbance ameliorees
WO2001031122A1 (fr) Papier a hautes performances a l'etat humide, utilisant des composes anioniques polymeres, et son procede de production
US20030145964A1 (en) Reactive compositions and their use in paper products
WO2001090479A1 (fr) Sechage par impulsions de papier-linge

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CR CU CZ DE DK DM DZ EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
WWE Wipo information: entry into national phase

Ref document number: PA/a/2002/001684

Country of ref document: MX

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: JP