WO2001008824A1 - Methods of treating waste - Google Patents
Methods of treating waste Download PDFInfo
- Publication number
- WO2001008824A1 WO2001008824A1 PCT/US2000/020562 US0020562W WO0108824A1 WO 2001008824 A1 WO2001008824 A1 WO 2001008824A1 US 0020562 W US0020562 W US 0020562W WO 0108824 A1 WO0108824 A1 WO 0108824A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- waste
- article
- waste solids
- disposal
- solids
- Prior art date
Abstract
Description
Claims