WO2000069963A1 - Elastic films including crystalline polymer and crystallizable polymers of propylene - Google Patents
Elastic films including crystalline polymer and crystallizable polymers of propylene Download PDFInfo
- Publication number
- WO2000069963A1 WO2000069963A1 PCT/US2000/013011 US0013011W WO0069963A1 WO 2000069963 A1 WO2000069963 A1 WO 2000069963A1 US 0013011 W US0013011 W US 0013011W WO 0069963 A1 WO0069963 A1 WO 0069963A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- film
- fpc
- propylene
- weight percent
- spc
- Prior art date
Abstract
Description
Claims