WO2000069587A2 - Low pressure injection molding of flat tableware from metal feedstocks - Google Patents
Low pressure injection molding of flat tableware from metal feedstocks Download PDFInfo
- Publication number
- WO2000069587A2 WO2000069587A2 PCT/US2000/013830 US0013830W WO0069587A2 WO 2000069587 A2 WO2000069587 A2 WO 2000069587A2 US 0013830 W US0013830 W US 0013830W WO 0069587 A2 WO0069587 A2 WO 0069587A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- mixture
- gel
- forming material
- article
- molding
- Prior art date
Abstract
Description
Claims