WO2000069009A2 - Platinum-ruthenium-palladium-osmium alloy for use as a fuel cell catalyst - Google Patents
Platinum-ruthenium-palladium-osmium alloy for use as a fuel cell catalyst Download PDFInfo
- Publication number
- WO2000069009A2 WO2000069009A2 PCT/US2000/011327 US0011327W WO0069009A2 WO 2000069009 A2 WO2000069009 A2 WO 2000069009A2 US 0011327 W US0011327 W US 0011327W WO 0069009 A2 WO0069009 A2 WO 0069009A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- concentration
- platinum
- osmium
- atomic percent
- ruthenium
- Prior art date
Abstract
Description
Claims