WO2000049089A1 - Polyester molding composition - Google Patents
Polyester molding composition Download PDFInfo
- Publication number
- WO2000049089A1 WO2000049089A1 PCT/US2000/000462 US0000462W WO0049089A1 WO 2000049089 A1 WO2000049089 A1 WO 2000049089A1 US 0000462 W US0000462 W US 0000462W WO 0049089 A1 WO0049089 A1 WO 0049089A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- thermoplastic resin
- resin composition
- polyester
- metal
- sulfonate
- Prior art date
Abstract
Description
Claims