WO2000044032A9 - Wear-resistant electromechanical contacts - Google Patents
Wear-resistant electromechanical contactsInfo
- Publication number
- WO2000044032A9 WO2000044032A9 PCT/US2000/001295 US0001295W WO0044032A9 WO 2000044032 A9 WO2000044032 A9 WO 2000044032A9 US 0001295 W US0001295 W US 0001295W WO 0044032 A9 WO0044032 A9 WO 0044032A9
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- coating
- contact according
- carbon
- substrate
- silicon
- Prior art date
Abstract
Description
Claims